PA6 8253 HS BK-102 PA6 、_产品资讯

PA6 8253 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Physical Properties	Metric	English	Comments

Water Absorption	1.5 %	1.5 %	24 hour; ISO Test
Linear Mold Shrinkage	0.012 cm/cm	0.012 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	82	82	ASTM Test
Tensile Strength, Yield	65.0 MPa	9430 psi	2 in/min; ASTM Test
Elongation at Break	>= 100 %	>= 100 %	2 in/min; ASTM Test
Elongation at Yield	4.0 %	4.0 %	2 in/min; ASTM Test
Flexural Strength	65.0 MPa	9430 psi	ISO Data
	85.0 MPa	12300 psi	ASTM Test
Flexural Modulus	1.90 GPa	276 ksi	ISO Data
	2.27 GPa	329 ksi	ASTM Test
Izod Impact, Notched	1.50 J/cm @Thickness 3.17 mm	2.81 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	14.0 kJ/m²	6.66 ft-lb/in²	ISO Test

Thermal Properties	Metric	English	Comments
CTE, linear	99.0 µm/m-°C @Temperature -30.0 - 30.0 °C	55.0 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
Melting Point	220 °C	428 °F	ASTM Test
Deflection Temperature at 1.8 MPa (264 psi)	60.0 °C	140 °F	ASTM Test

Descriptive Properties
Color	BK-102
Commercial Status	Active America
Impact Modified	Yes
Primary Processing Technique	Injection Molding
UL.UL-C	Yes

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。

欢迎各位客户前来咨询：