颗粒图：
用途：
、
、广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座。
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | on Tensile Bar; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 69.0 MPa | 10000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.1 % | 3.1 % | 5 mm/min; ISO 527 |
| Flexural Strength | 102 MPa | 14800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.40 GPa | 493 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| UL RTI, Electrical | 65.0 °C @Thickness 1.60 mm |
149 °F @Thickness 0.0630 in |
|
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 1.60 mm |
149 °F @Thickness 0.0630 in |
|
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.60 mm |
149 °F @Thickness 0.0630 in |
|
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Zone 1 |
| Middle Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Zone 2 |
| Front Barrel Temperature | 250 - 270 °C | 482 - 518 °F | Zone 3 |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4.00 hour | 4.00 hour | |
| Moisture Content | 0.20 % | 0.20 % | |