PA6 BG-15 HM PA6-GF15 抗冲击强度好、_产品资讯

PA6 BG-15 HM 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Physical Properties	Metric	English	Comments

Density	1.14 g/cc	0.0412 lb/in³	ISO 1183
Water Absorption	5.5 %	5.5 %	ISO 62
Moisture Absorption	2.00 %	2.00 %	ISO 62
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0050 cm/cm	0.0050 in/in	ISO 294-4, 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	90.0 MPa	13100 psi	conditioned; ISO 2039-1
	150 MPa	21800 psi	dry; ISO 2039-1
Tensile Strength at Break	70.0 MPa	10200 psi	conditioned; ISO 527-1/-2
	105 MPa	15200 psi	dry; ISO 527-1/-2
Elongation at Break	4.0 %	4.0 %	dry; ISO 527-1/-2
	10 %	10 %	conditioned; ISO 527-1/-2
Tensile Modulus	4.00 GPa	580 ksi	conditioned; ISO 527-1/-2
	5.50 GPa	798 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	5.50 J/cm²	26.2 ft-lb/in²	dry; ISO 179/1eU
	6.00 J/cm²	28.6 ft-lb/in²	conditioned; ISO 179/1eU
	6.00 J/cm² @Temperature 30.0 °C	28.6 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	6.00 J/cm² @Temperature 30.0 °C	28.6 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU
Charpy Impact, Notched	1.00 J/cm²	4.76 ft-lb/in²	dry; ISO 179/1eA
	1.20 J/cm²	5.71 ft-lb/in²	conditioned; ISO 179/1eA
	0.500 J/cm² @Temperature 30.0 °C	2.38 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	0.500 J/cm² @Temperature 30.0 °C	2.38 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	conditioned; IEC 60093
	1.00e+14 ohm-cm	1.00e+14 ohm-cm	dry; IEC 60093
Surface Resistance	1.00e+12 ohm	1.00e+12 ohm	IEC 60093
Dielectric Strength	32.0 kV/mm	813 kV/in	conditioned; IEC 60243-1
	38.0 kV/mm	965 kV/in	dry; IEC 60243-1
Comparative Tracking Index	600 V	600 V	conditioned; IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 µm/m-°C	11.1 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	130 µm/m-°C	72.2 µin/in-°F	ISO 11359-1/-2
Melting Point	222 °C	432 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	80.0 - 110 °C	176 - 230 °F	long term; EMS
	160 °C	320 °F	short term; EMS
Deflection Temperature at 1.8 MPa (264 psi)	160 °C	320 °F	ISO 75-1/-2
Deflection Temperature at 8.0 MPa	65.0 °C	149 °F	ISO 75-1/-2
Flammability, UL94	HB	HB	IEC 60695-11-10

Descriptive Properties
Automotive	Air intake sytems
	Interior
Electricals & Electronics	Electrical appliances
	Electrical equipment
Form	Granules
Processing	Injection Molding
Special Characteristics	High impact or impact modified

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。