颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.40 % @Temperature 23.0 °C |
1.40 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 6.8 % @Temperature 23.0 °C |
6.8 % @Temperature 73.4 °F |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | on Tensile Bar; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 123 | 123 | ISO 2039-2 |
| Tensile Strength at Break | 145 MPa | 21000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.8 % | 3.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.50 GPa | 943 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 200 MPa | 29000 psi | break, 2 mm/min; ISO 178 |
| Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -40.0 °C |
2.86 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -20.0 °C |
3.33 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A | |
| 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1U |
| 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1U | |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU |
| 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 20 @Load 1.00 kg |
20 @Load 2.20 lb |
CS-17; E2P Method |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.6 @Frequency 50.0 - 60.0 Hz |
3.6 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.20 mm |
508 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0061 @Frequency 50.0 - 60.0 Hz |
0.0061 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 400 V | 400 V | M; IEC 60112 |
| 500 V | 500 V | IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
19.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 95.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
52.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af |
| Vicat Softening Point | 206 °C | 403 °F | B/120; ISO 306 |
| 208 °C | 406 °F | B/50; ISO 306 | |
| UL RTI, Electrical | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
IEC 60695-11-10 | |
| Oxygen Index | 24 % | 24 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | Zone 1 |
| Middle Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Zone 2 |
| Front Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Zone 3 |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。