| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | weight gain after 24 hr. immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 3.3 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.3 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 38 | 38 | ASTM D785 |
| Tensile Strength, Ultimate | 37.9 MPa | 5500 psi | ASTM D638 |
| Tensile Modulus | 1.86 GPa | 270 ksi | ASTM D638 |
| Flexural Strength | <= 71.0 MPa | <= 10300 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.216 W/m-K | 1.50 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.9 °C | 192 °F | annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.4 °C | 175 °F | annealed; ASTM D648 |
| Vicat Softening Point | 82.8 °C | 181 °F | 50°C/hr; 50N; ASTM D1525 |
| 93.9 °C | 201 °F | 50°C/hr; 10N; ASTM D1525 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 @Temperature 22.8 °C |
1.49 @Temperature 73.0 °F |
ND; ASTM D542 |
| Haze | <= 2.0 % @Thickness 3.17 mm |
<= 2.0 % @Thickness 0.125 in |
ASTM D1003 |
| Transmission, Visible | 90 % @Thickness 3.17 mm |
90 % @Thickness 0.125 in |
ASTM D1003 |
材料说明：有机玻璃®hfi10是影响改性热塑性丙烯酸树脂注塑成型配方。它具有较高的熔体流动，提高脱模性能和提供10倍标准压克力耐冲击的同时保持良好的光学特性。它提供了完美平衡的熔体流动性和增加抗破损，同时提供耐候性优于其他高冲击塑料提供。补充Moldflow模拟数据是可用的。
外观：透明/透明；可供选择；不透明；半透明
特点：高流动性；耐刮性；高清晰度；良好的颜色稳定性；良好的尺寸稳定性；低收缩；良好的热稳定性；良好的抗紫外线性能；良好的耐候性；良好的韧性；高耐冲击性
应用：电器；照明器