| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | 10x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 80x80x1mm, at 23°C and 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.65 % | 0.65 % | 80x80x1mm, 23°C; ISO 62 | ||
| Melt Flow | 11.28 g/10 min @Load 2.16 kg, Temperature 190 °C |
11.28 g/10 min @Load 4.76 lb, Temperature 374 °F |
Calculated from Volume flow Rate: 8 cm3/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 144 MPa | 20900 psi | 30 sec value, 20x20x4 mm; ISO 2039, part 1; applied load 358 N | ||
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min | ||
| Elongation at Break | 30 % | 30 % | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min | ||
| Elongation at Yield | 9.0 % | 9.0 % | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min | ||
| Tensile Modulus | 2.85 GPa | 413 ksi | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 1 mm/min | ||
| Flexural Modulus | 2.70 GPa | 392 ksi | 80x10x4mm from multi-purpose test specimen (ISO 3167); ISO 178 | ||
| Charpy Impact Unnotched | 16.0 J/cm² @Temperature -30.0 °C |
76.1 ft-lb/in² @Temperature -22.0 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eU | ||
| 18.0 J/cm² @Thickness 4.00 mm, Temperature 23.0 °C |
85.7 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA | ||
| 0.650 J/cm² @Thickness 4.00 mm, Temperature 23.0 °C |
3.09 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA | |||
| Tensile Creep Modulus, 1 hour | 2500 MPa | 363000 psi | multi-purpose test specimen (ISO 3167); ISO 899, part 1 | ||
| Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | multi-purpose test specimen (ISO 3167); ISO 899, part 1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
80x80x1 mm; IEC 60250 | ||
| 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
80x80x1 mm; IEC 60250 | |||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | 80x80x1 mm; IEC 60243, part 1 | ||
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
80x80x1 mm; IEC 60250 | ||
| 0.0050 @Frequency 1e+6 Hz |
0.0050 @Frequency 1e+6 Hz |
80x80x1 mm; IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
Longitudinal, 30x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 11359, part 1/2 | ||
| Melting Point | 166 °C | 331 °F | DSC, 10 K/min, Molding compound; ISO 3146, method C1b | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | 80x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 75, part 1/2 | ||
| Vicat Softening Point | 150 °C | 302 °F | VST/B/50, 10x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 306 | ||
| De |
|||||
| Emission | Max 10 mg/kg | ||||