类别：聚合物；热塑性塑料；丙烯酸（有机玻璃）；丙烯酸，挤出
材料说明：有机玻璃®XT挤压丙烯酸具有以下特性：，绝对无色透明，打破耐冲击抗（有机玻璃抗®），无与伦比的抗风化和老化，非常好的表面；辉煌，纹理或缎（德固赛磨砂板®），板材，管，圆棒，多皮片，波纹片，反射镜，1.5至25毫米厚的板材，多皮片16毫米和32毫米厚，标准尺寸为4050×2050毫米（+额外长度），25多个标准色
特性：耐稀酸，有机溶剂的限制性，良好的抗碱，易于工作，类似于硬木，容易成型的最佳常数条件下，易粘结也与溶剂粘合剂（如acrifix®116，117），烧得越来越少，像硬木，很少有烟的产生最高使用温度约70°C
该材料的具体。
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.572 % | 0.572 % | 24 hrs, 23°C from dry state; ISO 62, Method 1 | ||
| Water Absorption at Saturation | 2.1 % | 2.1 % | Max. Weight Gain During Immersion; ISO 62, Method 1 | ||
| Moisture Expansion | 0.80 % | 0.80 % | Possible Expansion due to heat and moisture | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 100 MPa | 14500 psi | H961/30; ISO 2039-1 | ||
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ISO 527-2/1B/5 | ||
| Elongation at Break | 25 % | 25 % | Nominal; ISO 527-2 1B/50 | ||
| Modulus of Elasticity | 1.80 GPa | 261 ksi | Short Time Value; ISO 527-2/1B/1 | ||
| Flexural Strength | 69.0 MPa | 10000 psi | 5 mm/min (80x10x4 mm); ISO 178 | ||
| Poissons Ratio | 0.43 @Temperature 23.0 °C |
0.43 @Temperature 73.4 °F |
dilation speed of 5% per min; up to 2% dilation; ISO 527-1 | ||
| Shear Modulus | 0.629 GPa | 91.2 ksi | Calculated | ||
| Izod Impact, Notched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1fU | ||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA | ||
| Impact | 6.0 | 6.0 | mm, Resistance to puck impact from thickness, Test Certificate No. From FMPA Stuttgart - 46/901 870/Sm/C; Similar to DIN 18032, part 3 | ||
| Abrasion | 30 - 40 | 30 - 40 | % Haze, Abrasion resistance in Taber abrader test (100 rev.;5.4 N; CS-10F); ISO 9352 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | DIN VDE 0303, Part 3 | ||
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | DIN VDE 0303, Part 3 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 110 µm/m-°C @Temperature 0.000 - 50.0 °C |
61.1 µin/in-°F @Temperature 32.0 - 122 °F |
DIN 53752A | ||
| Specific Heat Capacity | 1.47 J/g-°C | 0.351 BTU/lb-°F | |||
| Maximum Service Temperature, Air | 65.0 °C | 149 °F | Permanent | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75 | ||
| Vicat Softening Point | 97.0 °C | 207 °F | ISO 306, Method B 50 | ||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.491 @Thickness 3.00 mm |
1.491 @Thickness 0.118 in |
clear grade; ISO 489 | ||
| Transmission, Visible | 91 % @Thickness 3.00 mm |
91 % @Thickness 0.118 in |
clear grade; DIN 5036, Part 3 | ||
| UV Transmittance | 0.00 % @Thickness 3.00 mm |
0.00 % @Thickness 0.118 in |
clear grade | ||
| Reflection Coefficient, Visible (0-1) | 0.040 @Thickness 3.00 mm |
0.040 @Thickness 0.118 in |
clear grade, Reflection loss in the visible range (for each surface) | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | >= 70.0 °C | >= 158 °F | Reverse Forming Temperature | ||
| 140 - 150 °C | 284 - 302 °F | Forming Temperature | |||
| De |
|||||
| Adsorption in the Visible Range | Max 0.05% | clear grade, 3 mm | |||
| Fire Rating | B 2, Normally Flammable | DIN 4102 | |||
| Min Cold Bending Radius | 150 x thickness | ||||
| Total Energy Transmittance g | 85% | clear grade, 3 mm, DIN EN 410 | |||
| U Value for 10mm | 4.4 W/m2K | DIN 4701 | |||
| U Value for 1mm | 5.8 W/m2K | DIN 4701 | |||
| U Value for 3mm | 5.6 W/m2K | DIN 4701 | |||
| U Value for 5mm | 5.3 W/m2K | DIN 4701 |
|||
图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com