| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Asahi Kasei Method |
| Melt Flow | 20 g/10 min | 20 g/10 min | ISO 1133 D |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 61.0 MPa | 8850 psi | ISO 527 - 1 & - 2 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 - 1 & - 2 |
| Tensile Modulus | 4.90 GPa | 711 ksi | ISO 527 - 1 & - 2 |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 / 1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C | 322 °F | ISO 75 -1 & -2 flat |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 268 °F | ISO 75 -1 & -2 flat |
| Flammability, UL94 | HB | HB | |