| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D 792 |
| 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0099 cm/cm @Time 86400 sec |
0.0099 in/in @Time 24.0 hour |
ISO 294 |
| 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Time 86400 sec |
0.015 in/in @Time 24.0 hour |
ISO 294 |
| 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D 955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 102 MPa | 14800 psi | ISO 527 |
| 104 MPa | 15100 psi | ASTM D 638 | |
| Tensile Strength, Yield | 103 MPa | 14900 psi | ISO 527 |
| 104 MPa | 15100 psi | ASTM D 638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.1 % | 2.1 % | ASTM D 638 | |
| Elongation at Yield | 2.0 % | 2.0 % | ISO 527 |
| 2.1 % | 2.1 % | ASTM D 638 | |
| Tensile Modulus | 8.91 GPa | 1290 ksi | 1 mm/min; ISO 527 |
| 8.96 GPa | 1300 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 146 MPa | 21200 psi | ISO 178 |
| 151 MPa | 21900 psi | ASTM D 790 | |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D 790 |
| 7.60 GPa | 1100 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm @Temperature 23.0 °C |
0.787 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.48 J/cm @Temperature 23.0 °C |
8.39 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.36 | 0.36 | ASTM D 3702 Modified |
| K (wear) Factor | 179 x 10-8 mm³/N-M | 89.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 79.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 66.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 67.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM-KCL22 图：