类别：聚合物；热塑性；聚甲醛（POM）；乙缩醛共聚物，影响改性
材料说明：tx86稍微增韧缩醛共聚物具有延性的弯曲和冲击载荷。延性而非脆性，故障模式为工程师提供更大的设计自由，在应用程序，如剪辑，紧固件，齿轮和滚筒。
物性表：| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | 50 mm/min; ISO 527-2/1A |
| Tensile Modulus | 2.45 GPa | 355 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Modulus | 2.16 GPa | 313 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | |
| Mold Temperature | 77.0 - 93.0 °C | 171 - 199 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 hour | 3 hour | |
| Injection Pressure | 75.8 - 110 MPa | 11000 - 16000 psi | |
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com