POM-KCL34 沙伯基础创新塑料LNP lubricomp kcl34缩醛共聚物 类别:聚合物;热塑性;聚甲醛(POM);共聚甲醛,碳纤维填充 材料说明:LNP * lubricomp * kcl34是基于缩醛共聚物树脂化合物含有聚四氟乙烯,碳纤维。这种材料的附加功能包括:内部润滑,导电性。 联系人: 夏先生 手 机: 13501802636 QQ :205730283 邮 箱 :205730283@qq.com
 POM-KCL34 的物性表:
 
Physical Properties Metric English Comments
Density  1.48 g/cc 0.0535 lb/in³ ASTM D 792
  1.48 g/cc 0.0535 lb/in³ ISO 1183
Moisture Absorption at Equilibrium  0.10 %
@Time 86400 sec
0.10 %
@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow    0.0075 cm/cm
@Time 86400 sec
0.0075 in/in
@Time 24.0 hour
ISO 294
  0.0070 - 0.0090 cm/cm
@Time 86400 sec
0.0070 - 0.0090 in/in
@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse     0.013 - 0.015 cm/cm
@Time 86400 sec
0.013 - 0.015 in/in
@Time 24.0 hour
ASTM D 955
  0.014 cm/cm
@Time 86400 sec
0.014 in/in
@Time 24.0 hour
ISO 294
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  121 MPa 17500 psi ISO 527
  127 MPa 18400 psi ASTM D 638
Tensile Strength, Yield  122 MPa 17700 psi ISO 527
  127 MPa 18400 psi ASTM D 638
Elongation at Break  1.8 % 1.8 % ISO 527
  1.9 % 1.9 % ASTM D 638
Elongation at Yield  1.8 % 1.8 % ISO 527
  1.9 % 1.9 % ASTM D 638
Tensile Modulus  14.3 GPa 2070 ksi 1 mm/min; ISO 527
  15.85 GPa 2299 ksi 50 mm/min; ASTM D 638
Flexural Strength  180 MPa 26100 psi ISO 178
  186 MPa 27000 psi ASTM D 790
Flexural Modulus  12.9 GPa 1870 ksi ISO 178
  13.1 GPa 1900 ksi ASTM D 790
Izod Impact, Notched  0.480 J/cm
@Temperature 23.0 °C
0.899 ft-lb/in
@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched  5.12 J/cm
@Temperature 23.0 °C
9.59 ft-lb/in
@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO)  5.00 kJ/m²
@Temperature 23.0 °C
2.38 ft-lb/in²
@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO)  31.0 kJ/m²
@Temperature 23.0 °C
14.8 ft-lb/in²
@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test  2.00 J 1.48 ft-lb Multiaxial Impact; ISO 6603
   11.0 J
@Temperature 23.0 °C
8.11 ft-lb
@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Coefficient of Friction, Dynamic  0.36 0.36 ASTM D 3702 Modified
K (wear) Factor  127 x 10-8 mm³/N-M 63.0 x 10-10 in³-min/ft-lb-hr Washer; ASTM D 3702 Modified
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow    70.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F
@Temperature -40.0 - 104 °F
ISO 11359-2
  70.2 µm/m-°C
@Temperature -40.0 - 40.0 °C
39.0 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow    34.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
18.9 µin/in-°F
@Temperature -40.0 - 104 °F
ISO 11359-2
  34.2 µm/m-°C
@Temperature -40.0 - 40.0 °C
19.0 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi)  163 °C 325 °F Flatw 80*10*4 sp=64mm; ISO 75/Bf
  162 °C
@Thickness 3.20 mm
324 °F
@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)  159 °C 318 °F Flatw 80*10*4 sp=64mm; ISO 75/Af
  160 °C
@Thickness 3.20 mm
320 °F
@Thickness 0.126 in
unannealed; ASTM D 648
 

上海松翰塑化科技有限公司,供应原料,品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询:
联系人: 夏先生  
手  机:13501802636  021 51131842
QQ    :205730283  
邮 箱 :205730283@qq.com 

POM-KCL34 图:

waibao basf

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-38728.html

免责声明: 本文 LNP美国 POM-KCL34,碳纤维填充 内部润滑,导电性 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4