| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D 792 |
| 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.23 % @Time 86400 sec |
0.23 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0125 - 0.0129 cm/cm @Time 86400 sec |
0.0125 - 0.0129 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0125 - 0.0129 cm/cm @Time 86400 sec |
0.0125 - 0.0129 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0157 - 0.0165 cm/cm @Time 86400 sec |
0.0157 - 0.0165 in/in @Time 24.0 hour |
ISO 294 |
| 0.0157 - 0.017 cm/cm @Time 86400 sec |
0.0157 - 0.017 in/in @Time 24.0 hour |
ASTM D 955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 78.0 MPa | 11300 psi | ASTM D 638 |
| 78.0 MPa | 11300 psi | ISO 527 | |
| Elongation at Break | 2.7 % | 2.7 % | ISO 527 |
| 3.2 % | 3.2 % | ASTM D 638 | |
| Tensile Modulus | 5.10 GPa | 740 ksi | 50 mm/min; ASTM D 638 |
| 5.28 GPa | 766 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 126 MPa | 18300 psi | ASTM D 790 |
| 127 MPa | 18400 psi | ISO 178 | |
| Flexural Modulus | 4.96 GPa | 719 ksi | ASTM D 790 |
| 5.04 GPa | 731 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C |
0.899 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.27 J/cm @Temperature 23.0 °C |
8.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 85.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 85.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 92.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
51.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 92.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
51.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 331 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 172 °C @Thickness 3.20 mm |
342 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM-KFI12A 图：