| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D 792 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D 792 |
| 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.19 % | 0.19 % | 23°C / 50% RH; ISO 62 |
| 0.19 % @Time 86400 sec |
0.19 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.040 cm/cm @Time 86400 sec |
0.010 - 0.040 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.040 cm/cm @Time 86400 sec |
0.010 - 0.040 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 |
| 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 21 % | 21 % | Type I, 5 mm/min; ASTM D 638 |
| 22.5 % | 22.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.16 GPa | 603 ksi | 1 mm/min; ISO 527 |
| 4.21 GPa | 611 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 73.0 MPa | 10600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 3.46 GPa | 502 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 3.66 GPa | 531 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.78 J/cm @Temperature 23.0 °C |
10.8 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 93.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
51.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 88.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
49.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C | 405 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 196 °C @Thickness 3.20 mm |
385 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM-KB004 图：