| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Water Absorption | 0.90 % @Temperature 23.0 °C, Time 86400 sec |
0.90 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 0.70 % @Temperature 20.0 °C |
0.70 % @Temperature 68.0 °F |
50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 2.00 mm, Time 86400 sec |
0.0080 in/in @Thickness 0.0787 in, Time 24.0 hour |
|
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm, Time 86400 sec |
0.0080 in/in @Thickness 0.0787 in, Time 24.0 hour |
|
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 72 | 72 | After 15 sec, Conditioned 15 days at 23°C - 50% RH; ISO 868 |
| Tensile Strength at Break | 64.0 MPa | 9280 psi | Conditioned 15 days at 23°C - 50% RH; ISO 527 |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | Conditioned 15 days at 23°C - 50% RH; ISO 527 |
| Elongation at Break | <= 250 % | <= 250 % | Conditioned 15 days at 23°C - 50% RH; ISO 527 |
| Elongation at Yield | 7.0 % | 7.0 % | Conditioned 15 days at 23°C - 50% RH; ISO 527 |
| Tensile Modulus | 1.17 GPa | 170 ksi | Conditioned 15 days at 23°C - 50% RH; ISO 527 |
| Flexural Modulus | 1.20 GPa | 174 ksi | Conditioned 15 days at 23°C - 50% RH; ISO 178 |
Charpy Impact Unnotched  |
NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched |
0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 180 °C | 356 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 250 °C | 482 °F | Recommended |
| 230 - 280 °C | 446 - 536 °F | ||
| Mold Temperature | 40.0 °C | 104 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com