类别：聚合物；热塑性塑料；树脂聚合物；丙烯腈-丁二烯-苯乙烯（尼龙）/尼龙共混物，玻璃增强
材料说明：Terblend N ng-02 UV是8%玻璃纤维增强（UV固化）ABS／PA共混增强尺寸稳定性和刚度。
高尺寸稳定性
增强刚度
软化温度
玻璃纤维增强（8%）
物性表：| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.1 % @Temperature 23.0 °C |
1.1 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 |
| Melt Flow | 30 g/10 min @Load 10.0 kg, Temperature 240 °C |
30 g/10 min @Load 22.0 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 95.0 MPa | 13800 psi | ISO 2039-1 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 2.85 GPa | 413 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75 |
| Vicat Softening Point | 108 °C @Load 5.10 kg |
226 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 170 °C @Load 1.02 kg |
338 °F @Load 2.25 lb |
50°C/h; ISO 306 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | ISO 294 |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | ISO 294 |
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com