| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 5.0 % @Thickness 2.00 mm |
5.0 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Moisture Absorption | 1.60 % @Thickness 2.00 mm |
1.60 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 95 | 95 | DAM; ISO 2039-2 | ||
| Hardness, Rockwell R | 121 | 121 | DAM; ISO 2039-2 | ||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50%RH; ISO 527-1/-2 | ||
| 85.0 MPa | 12300 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 4.0 % | 4.0 % | DAM; ISO 527-1/-2 | ||
| 9.0 % | 9.0 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 3.80 GPa | 551 ksi | 50%RH; ISO 527-1/-2 | ||
| 6.60 GPa | 957 ksi | DAM; ISO 527-1/-2 | |||
| Shear Modulus | 0.427 GPa @Temperature 150 °C |
61.9 ksi @Temperature 302 °F |
DAM; Dynamic; ISO 11403-1 -2 | ||
| 0.544 GPa @Temperature 110 °C |
78.9 ksi @Temperature 230 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 1.226 GPa @Temperature 62.0 °C |
177.8 ksi @Temperature 144 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 2.393 GPa @Temperature 10.0 °C |
347.1 ksi @Temperature 50.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 2.504 GPa @Temperature -20.0 °C |
363.2 ksi @Temperature -4.00 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 2.692 GPa @Temperature -50.0 °C |
390.4 ksi @Temperature -58.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | DAM; ISO 179/1eU | ||
| 5.50 J/cm² | 26.2 ft-lb/in² | 50%RH; ISO 179/1eU | |||
| 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eU | |||
| 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | DAM; ISO 179/1eA | ||
| 0.400 J/cm² | 1.90 ft-lb/in² | 50%RH; ISO 179/1eA | |||
| 0.200 J/cm² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |||
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 3500 MPa @Time 3600 sec |
508000 psi @Time 1.00 hour |
50%RH; ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 2100 MPa @Time 3.60e+6 sec |
305000 psi @Time 1000 hour |
50%RH; ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | 50%RH; IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | 50%RH; IEC 60093 | ||
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz |
3.9 @Frequency 1.00e+6 Hz |
DAM; IEC 60250 | ||
| 4.5 @Frequency 1.00e+6 Hz |
4.5 @Frequency 1.00e+6 Hz |
50%RH; IEC 60250 | |||
| 4.5 @Frequency 100 Hz |
4.5 @Frequency 100 Hz |
DAM; IEC 60250 | |||
| 9.4 @Frequency 100 Hz |
9.4 @Frequency 100 Hz |
50%RH; IEC 60250 | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | DAM; IEC 60243-1 | ||
| Dissipation Factor | 0.011 @Frequency 100 Hz |
0.011 @Frequency 100 Hz |
DAM; IEC 60250 | ||
| 0.023 @Frequency 1.00e+6 Hz |
0.023 @Frequency 1.00e+6 Hz |
DAM; IEC 60250 | |||
| 0.055 @Frequency 1.00e+6 Hz |
0.055 @Frequency 1.00e+6 Hz |
50%RH; IEC 60250 | |||
| 0.21 @Frequency 100 Hz |
0.21 @Frequency 100 Hz |
50%RH; IEC 60250 | |||
| Comparative Tracking Index | 575 V | 575 V | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C | 36.1 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| Melting Point | 263 °C | 505 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | DAM; ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 0.700 mm |
HB @Thickness 0.0276 in |
DAM; IEC 60695-11-10 | ||
| De |
|||||
| Part Marking Code | >PA66-MD40< | ISO 11469 | |||
| Regional Availability | Europe | ||||
| Near East/Africa | |||||
| Resin Identification | PA66-MD40 | ||||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。