  4. 挤出级增强PA66/美国杜邦/11C40 NC010本色

挤出级增强PA66/美国杜邦/11C40 NC010本色

挤出级增强PA66/美国杜邦/11C40 NC010本色
 参考图片：

颗粒图片：

包装图片：

成品图片：
images (7)

 

 

 
Physical Properties Metric English Comments
Density  1.47 g/cc 0.0531 lb/in³ DAM; ISO 1183
Water Absorption  6.0 %
@Thickness 2.00 mm		 6.0 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  1.60 %
@Thickness 2.00 mm		 1.60 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Water Absorption at Saturation  1.1 % 1.1 % DAM; Immersion 24h; ASTM D570
Linear Mold Shrinkage, Flow  0.0090 cm/cm 0.0090 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0090 cm/cm 0.0090 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  63.0 MPa 9140 psi 50%RH; ISO 527-1/-2
  90.0 MPa 13100 psi DAM; ISO 527-1/-2
Tensile Stress   3.93 MPa
@Strain 0.500 %,
Temperature 150 °C		 570 psi
@Strain 0.500 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  6.20 MPa
@Strain 0.700 %,
Temperature 150 °C		 899 psi
@Strain 0.700 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  10.38 MPa
@Strain 1.70 %,
Temperature 150 °C		 1505 psi
@Strain 1.70 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  11.76 MPa
@Strain 0.500 %,
Temperature 23.0 °C		 1706 psi
@Strain 0.500 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  16.06 MPa
@Strain 3.50 %,
Temperature 150 °C		 2329 psi
@Strain 3.50 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  17.0 MPa
@Strain 2.70 %,
Temperature 150 °C		 2470 psi
@Strain 2.70 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  19.0 MPa
@Strain 5.00 %,
Temperature 150 °C		 2760 psi
@Strain 5.00 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  19.43 MPa
@Strain 0.300 %,
Temperature -40.0 °C		 2818 psi
@Strain 0.300 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  20.27 MPa
@Strain 1.00 %,
Temperature 23.0 °C		 2940 psi
@Strain 1.00 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  24.6 MPa
@Strain 6.00 %,
Temperature 150 °C		 3570 psi
@Strain 6.00 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  27.27 MPa
@Strain 0.500 %,
Temperature 0.000 °C		 3955 psi
@Strain 0.500 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  29.7 MPa
@Strain 13.0 %,
Temperature 150 °C		 4310 psi
@Strain 13.0 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  30.03 MPa
@Strain 1.90 %,
Temperature 23.0 °C		 4355 psi
@Strain 1.90 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  30.3 MPa
@Strain 0.500 %,
Temperature 0.000 °C		 4390 psi
@Strain 0.500 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  33.3 MPa
@Strain 0.600 %,
Temperature 23.0 °C		 4830 psi
@Strain 0.600 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  36.3 MPa
@Strain 0.500 %,
Temperature -40.0 °C		 5260 psi
@Strain 0.500 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  42.11 MPa
@Strain 3.90 %,
Temperature 23.0 °C		 6108 psi
@Strain 3.90 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  56.33 MPa
@Strain 0.900 %,
Temperature -40.0 °C		 8170 psi
@Strain 0.900 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  58.6 MPa
@Strain 1.10 %,
Temperature 23.0 °C		 8500 psi
@Strain 1.10 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  61.78 MPa
@Strain 1.20 %,
Temperature 0.000 °C		 8960 psi
@Strain 1.20 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  63.9 MPa
@Strain 1.10 %,
Temperature 0.000 °C		 9270 psi
@Strain 1.10 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  64.161 MPa
@Strain 35.0 %,
Temperature 23.0 °C		 9305.8 psi
@Strain 35.0 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  66.1 MPa
@Strain 1.00 %,
Temperature -40.0 °C		 9590 psi
@Strain 1.00 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  70.7 MPa
@Strain 1.40 %,
Temperature 23.0 °C		 10300 psi
@Strain 1.40 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  76.3 MPa
@Strain 1.60 %,
Temperature 0.000 °C		 11100 psi
@Strain 1.60 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  78.05 MPa
@Strain 1.30 %,
Temperature -40.0 °C		 11320 psi
@Strain 1.30 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  79.8 MPa
@Strain 1.30 %,
Temperature -40.0 °C		 11600 psi
@Strain 1.30 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  80.8 MPa
@Strain 1.80 %,
Temperature 23.0 °C		 11700 psi
@Strain 1.80 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  81.1 MPa
@Strain 1.50 %,
Temperature 0.000 °C		 11800 psi
@Strain 1.50 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  84.38 MPa
@Strain 1.90 %,
Temperature 0.000 °C		 12240 psi
@Strain 1.90 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  90.91 MPa
@Strain 3.70 %,
Temperature 23.0 °C		 13190 psi
@Strain 3.70 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  93.5 MPa
@Strain 1.70 %,
Temperature -40.0 °C		 13600 psi
@Strain 1.70 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  93.7 MPa
@Strain 1.90 %,
Temperature 0.000 °C		 13600 psi
@Strain 1.90 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  96.12 MPa
@Strain 1.70 %,
Temperature -40.0 °C		 13940 psi
@Strain 1.70 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  99.88 MPa
@Strain 4.40 %,
Temperature 0.000 °C		 14490 psi
@Strain 4.40 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  112.7 MPa
@Strain 4.30 %,
Temperature 0.000 °C		 16350 psi
@Strain 4.30 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  119.4 MPa
@Strain 4.90 %,
Temperature -40.0 °C		 17320 psi
@Strain 4.90 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  128.4 MPa
@Strain 3.10 %,
Temperature -40.0 °C		 18620 psi
@Strain 3.10 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
Elongation at Break  10 % 10 % DAM; ISO 527-1/-2
  35 % 35 % 50%RH; ISO 527-1/-2
Tensile Modulus  2.60 GPa 377 ksi 50%RH; ISO 527-1/-2
  5.90 GPa 856 ksi DAM; ISO 527-1/-2
Flexural Modulus  2.00 GPa 290 ksi 50%RH; ISO 178
  5.40 GPa 783 ksi DAM; ISO 178
Secant Modulus  0.25895 GPa
@Strain 20.0 %,
Temperature 80.0 °C		 37.558 ksi
@Strain 20.0 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  0.261 GPa
@Strain 14.0 %,
Temperature 100 °C		 37.9 ksi
@Strain 14.0 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  0.331 GPa
@Strain 12.0 %,
Temperature 80.0 °C		 48.0 ksi
@Strain 12.0 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  0.3315 GPa
@Strain 12.0 %,
Temperature 100 °C		 48.08 ksi
@Strain 12.0 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.454 GPa
@Strain 13.0 %,
Temperature 23.0 °C		 65.8 ksi
@Strain 13.0 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  0.510 GPa
@Strain 6.50 %,
Temperature 100 °C		 73.9 ksi
@Strain 6.50 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.516 GPa
@Strain 8.00 %,
Temperature 80.0 °C		 74.9 ksi
@Strain 8.00 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  0.533 GPa
@Strain 5.50 %,
Temperature 100 °C		 77.3 ksi
@Strain 5.50 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  0.548 GPa
@Strain 6.00 %,
Temperature 80.0 °C		 79.5 ksi
@Strain 6.00 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  0.601 GPa
@Strain 4.60 %,
Temperature 100 °C		 87.1 ksi
@Strain 4.60 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.707 GPa
@Strain 3.10 %,
Temperature 100 °C		 103 ksi
@Strain 3.10 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  0.758 GPa
@Strain 3.30 %,
Temperature 80.0 °C		 110 ksi
@Strain 3.30 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  0.792 GPa
@Strain 3.70 %,
Temperature 80.0 °C		 115 ksi
@Strain 3.70 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  0.800 GPa
@Strain 2.20 %,
Temperature 100 °C		 116 ksi
@Strain 2.20 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.922 GPa
@Strain 5.00 %,
Temperature 23.0 °C		 134 ksi
@Strain 5.00 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  0.973 GPa
@Strain 1.20 %,
Temperature 100 °C		 141 ksi
@Strain 1.20 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  1.02 GPa
@Strain 1.40 %,
Temperature 80.0 °C		 149 ksi
@Strain 1.40 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  1.07 GPa
@Strain 1.80 %,
Temperature 80.0 °C		 155 ksi
@Strain 1.80 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.15 GPa
@Strain 0.400 %,
Temperature 100 °C		 167 ksi
@Strain 0.400 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  1.226 GPa
@Strain 0.500 %,
Temperature 100 °C		 177.8 ksi
@Strain 0.500 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  1.27 GPa
@Strain 0.500 %,
Temperature 80.0 °C		 184 ksi
@Strain 0.500 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  1.405 GPa
@Strain 0.600 %,
Temperature 80.0 °C		 203.8 ksi
@Strain 0.600 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.44 GPa
@Strain 2.30 %,
Temperature 23.0 °C		 209 ksi
@Strain 2.30 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2.027 GPa
@Strain 1.00 %,
Temperature 23.0 °C		 294.0 ksi
@Strain 1.00 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2.352 GPa
@Strain 0.500 %,
Temperature 23.0 °C		 341.1 ksi
@Strain 0.500 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.12 GPa
@Strain 2.90 %,
Temperature 23.0 °C		 453 ksi
@Strain 2.90 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  3.36 GPa
@Strain 2.90 %,
Temperature 0.000 °C		 487 ksi
@Strain 2.90 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  3.4625 GPa
@Strain 3.20 %,
Temperature 0.000 °C		 502.20 ksi
@Strain 3.20 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  3.89 GPa
@Strain 2.90 %,
Temperature -40.0 °C		 564 ksi
@Strain 2.90 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  4.10 GPa
@Strain 2.20 %,
Temperature 0.000 °C		 594 ksi
@Strain 2.20 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  4.22 GPa
@Strain 2.00 %,
Temperature 23.0 °C		 612 ksi
@Strain 2.00 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  4.57 GPa
@Strain 2.20 %,
Temperature 0.000 °C		 663 ksi
@Strain 2.20 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  4.66 GPa
@Strain 1.70 %,
Temperature 0.000 °C		 676 ksi
@Strain 1.70 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  4.78 GPa
@Strain 1.60 %,
Temperature 23.0 °C		 693 ksi
@Strain 1.60 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  4.88 GPa
@Strain 2.40 %,
Temperature -40.0 °C		 707 ksi
@Strain 2.40 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  5.015 GPa
@Strain 2.00 %,
Temperature -40.0 °C		 727.4 ksi
@Strain 2.00 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  5.15 GPa
@Strain 1.20 %,
Temperature 0.000 °C		 747 ksi
@Strain 1.20 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.17 GPa
@Strain 1.70 %,
Temperature 0.000 °C		 750 ksi
@Strain 1.70 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.33 GPa
@Strain 1.10 %,
Temperature 23.0 °C		 773 ksi
@Strain 1.10 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.44 GPa
@Strain 1.90 %,
Temperature -40.0 °C		 789 ksi
@Strain 1.90 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  5.454 GPa
@Strain 0.500 %,
Temperature 0.000 °C		 791.0 ksi
@Strain 0.500 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.55 GPa
@Strain 0.600 %,
Temperature 23.0 °C		 805 ksi
@Strain 0.600 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.81 GPa
@Strain 1.10 %,
Temperature 0.000 °C		 843 ksi
@Strain 1.10 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.82 GPa
@Strain 1.50 %,
Temperature -40.0 °C		 844 ksi
@Strain 1.50 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  5.84 GPa
@Strain 1.50 %,
Temperature -40.0 °C		 846 ksi
@Strain 1.50 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  6.06 GPa
@Strain 0.500 %,
Temperature 0.000 °C		 879 ksi
@Strain 0.500 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  6.26 GPa
@Strain 0.900 %,
Temperature -40.0 °C		 908 ksi
@Strain 0.900 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  6.48 GPa
@Strain 0.300 %,
Temperature -40.0 °C		 939 ksi
@Strain 0.300 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  6.61 GPa
@Strain 1.00 %,
Temperature -40.0 °C		 959 ksi
@Strain 1.00 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  7.26 GPa
@Strain 0.500 %,
Temperature -40.0 °C		 1050 ksi
@Strain 0.500 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  7.00 kJ/m² 3.33 ft-lb/in² DAM; ISO 180/1A
  11.0 kJ/m² 5.23 ft-lb/in² 50%RH; ISO 180/1A
  5.00 kJ/m²
@Temperature -30.0 °C		 2.38 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
  5.00 kJ/m²
@Temperature -40.0 °C		 2.38 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1A
  5.00 kJ/m²
@Temperature -40.0 °C		 2.38 ft-lb/in²
@Temperature -40.0 °F		 50%RH; ISO 180/1A
  6.00 kJ/m²
@Temperature -30.0 °C		 2.86 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  150 kJ/m² 71.4 ft-lb/in² DAM; ISO 180/1U
  100 kJ/m²
@Temperature -30.0 °C		 47.6 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1U
  100 kJ/m²
@Temperature -30.0 °C		 47.6 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1U
Charpy Impact Unnotched  20.0 J/cm² 95.2 ft-lb/in² DAM; ISO 179/1eU
  NB NB 50%RH; ISO 179/1eU
  8.50 J/cm²
@Temperature -30.0 °C		 40.4 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
  10.0 J/cm²
@Temperature -30.0 °C		 47.6 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
Charpy Impact, Notched  0.700 J/cm² 3.33 ft-lb/in² DAM; ISO 179/1eA
  1.20 J/cm² 5.71 ft-lb/in² 50%RH; ISO 179/1eA
  0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+13 ohm-cm 1.00e+13 ohm-cm DAM; IEC 60093
Dielectric Constant   3.9
@Frequency 1.00e+6 Hz		 3.9
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
  4.2
@Frequency 100 Hz		 4.2
@Frequency 100 Hz		 DAM; IEC 60250
Dielectric Strength  24.0 kV/mm 610 kV/in DAM; IEC 60243-1
Dissipation Factor   0.010
@Frequency 100 Hz		 0.010
@Frequency 100 Hz		 DAM; IEC 60250
  0.010
@Frequency 1.00e+6 Hz		 0.010
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  64.0 µm/m-°C 35.6 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  65.0 µm/m-°C 36.1 µin/in-°F DAM; ISO 11359-1/-2
Melting Point  256 °C 493 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  215 °C 419 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  100 °C 212 °F DAM; ISO 75-1/-2
Flammability, UL94  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 DAM; IEC 60695-11-10
Oxygen Index  26 % 26 % DAM; ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PA66-IMD40< ISO 11469
Processing Injection Moulding  
Regional Availability North America  
  South and Central America  
Resin Identification PA66-IMD40  
Special characteristics Heat stabilised or stable to heat  

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39750.html

免责声明: 本文 挤出级增强PA66/美国杜邦/11C40 NC010本色 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4