Physical Properties Metric English Comments
Density  1.41 g/cc 0.0509 lb/in³ DAM; ISO 1183
Water Absorption  6.2 %
@Thickness 2.00 mm		 6.2 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  1.70 %
@Thickness 2.00 mm		 1.70 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Water Absorption at Saturation  1.2 % 1.2 % DAM; Immersion 24h; ASTM D570
Linear Mold Shrinkage, Flow  0.0090 cm/cm 0.0090 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0090 cm/cm 0.0090 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  58.0 MPa 8410 psi 50%RH; ISO 527-1/-2
  80.0 MPa 11600 psi DAM; ISO 527-1/-2
Tensile Stress  2.20 MPa
@Strain 0.100 %,
Temperature 23.0 °C		 319 psi
@Strain 0.100 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.34 MPa
@Strain 0.400 %,
Temperature 150 °C		 484 psi
@Strain 0.400 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  6.31 MPa
@Strain 1.10 %,
Temperature 150 °C		 915 psi
@Strain 1.10 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  10.28 MPa
@Strain 1.70 %,
Temperature 150 °C		 1491 psi
@Strain 1.70 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  10.73 MPa
@Strain 0.200 %,
Temperature 0.000 °C		 1556 psi
@Strain 0.200 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  11.06 MPa
@Strain 2.30 %,
Temperature 150 °C		 1604 psi
@Strain 2.30 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  12.9 MPa
@Strain 0.700 %,
Temperature 23.0 °C		 1870 psi
@Strain 0.700 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  15.3 MPa
@Strain 0.300 %,
Temperature 0.000 °C		 2220 psi
@Strain 0.300 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  15.36 MPa
@Strain 3.20 %,
Temperature 150 °C		 2228 psi
@Strain 3.20 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  15.52 MPa
@Strain 4.00 %,
Temperature 150 °C		 2251 psi
@Strain 4.00 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  18.53 MPa
@Strain 6.00 %,
Temperature 150 °C		 2688 psi
@Strain 6.00 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  18.83 MPa
@Strain 4.90 %,
Temperature 150 °C		 2731 psi
@Strain 4.90 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  20.3 MPa
@Strain 0.300 %,
Temperature -40.0 °C		 2940 psi
@Strain 0.300 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  21.0 MPa
@Strain 0.400 %,
Temperature 23.0 °C		 3050 psi
@Strain 0.400 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  22.3 MPa
@Strain 1.60 %,
Temperature 23.0 °C		 3230 psi
@Strain 1.60 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  26.77 MPa
@Strain 40.0 %,
Temperature 150 °C		 3883 psi
@Strain 40.0 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  29.55 MPa
@Strain 0.500 %,
Temperature -40.0 °C		 4286 psi
@Strain 0.500 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  30.3 MPa
@Strain 2.90 %,
Temperature 23.0 °C		 4390 psi
@Strain 2.90 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  31.31 MPa
@Strain 0.600 %,
Temperature 0.000 °C		 4541 psi
@Strain 0.600 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  37.9 MPa
@Strain 0.800 %,
Temperature 0.000 °C		 5500 psi
@Strain 0.800 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  44.2 MPa
@Strain 0.900 %,
Temperature 23.0 °C		 6410 psi
@Strain 0.900 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  50.4 MPa
@Strain 0.800 %,
Temperature -40.0 °C		 7310 psi
@Strain 0.800 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  52.7 MPa
@Strain 1.40 %,
Temperature 0.000 °C		 7640 psi
@Strain 1.40 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  55.3 MPa
@Strain 1.20 %,
Temperature 23.0 °C		 8020 psi
@Strain 1.20 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  55.4 MPa
@Strain 40.0 %,
Temperature 23.0 °C		 8040 psi
@Strain 40.0 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  57.45 MPa
@Strain 1.20 %,
Temperature 0.000 °C		 8332 psi
@Strain 1.20 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  63.5 MPa
@Strain 2.50 %,
Temperature 0.000 °C		 9210 psi
@Strain 2.50 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  65.3 MPa
@Strain 1.10 %,
Temperature -40.0 °C		 9470 psi
@Strain 1.10 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  65.9 MPa
@Strain 1.60 %,
Temperature 23.0 °C		 9560 psi
@Strain 1.60 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  72.67 MPa
@Strain 1.40 %,
Temperature -40.0 °C		 10540 psi
@Strain 1.40 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  73.15 MPa
@Strain 1.70 %,
Temperature 0.000 °C		 10610 psi
@Strain 1.70 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  78.0 MPa
@Strain 4.00 %,
Temperature 23.0 °C		 11300 psi
@Strain 4.00 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  79.9 MPa
@Strain 24.0 %,
Temperature 0.000 °C		 11600 psi
@Strain 24.0 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  84.2 MPa
@Strain 1.60 %,
Temperature -40.0 °C		 12200 psi
@Strain 1.60 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  89.79 MPa
@Strain 1.90 %,
Temperature -40.0 °C		 13020 psi
@Strain 1.90 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  92.72 MPa
@Strain 4.20 %,
Temperature 0.000 °C		 13450 psi
@Strain 4.20 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  101.96 MPa
@Strain 2.40 %,
Temperature -40.0 °C		 14788 psi
@Strain 2.40 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  116.2 MPa
@Strain 8.00 %,
Temperature -40.0 °C		 16850 psi
@Strain 8.00 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Elongation at Break  18 % 18 % DAM; ISO 527-1/-2
  40 % 40 % 50%RH; ISO 527-1/-2
Tensile Modulus  2.00 GPa 290 ksi 50%RH; ISO 527-1/-2
  4.90 GPa 711 ksi DAM; ISO 527-1/-2
Flexural Modulus  1.80 GPa 261 ksi 50%RH; ISO 178
  4.50 GPa 653 ksi DAM; ISO 178
Secant Modulus   0.0997 GPa
@Strain 38.0 %,
Temperature 80.0 °C		 14.5 ksi
@Strain 38.0 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  0.127 GPa
@Strain 30.9 %,
Temperature 100 °C		 18.5 ksi
@Strain 30.9 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.154 GPa
@Strain 30.9 %,
Temperature 80.0 °C		 22.3 ksi
@Strain 30.9 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  0.172 GPa
@Strain 19.0 %,
Temperature 100 °C		 24.9 ksi
@Strain 19.0 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  0.233 GPa
@Strain 14.0 %,
Temperature 80.0 °C		 33.8 ksi
@Strain 14.0 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  0.306 GPa
@Strain 12.9 %,
Temperature 80.0 °C		 44.4 ksi
@Strain 12.9 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  0.31766 GPa
@Strain 9.40 %,
Temperature 100 °C		 46.073 ksi
@Strain 9.40 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.356 GPa
@Strain 7.50 %,
Temperature 100 °C		 51.6 ksi
@Strain 7.50 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  0.428 GPa
@Strain 6.00 %,
Temperature 80.0 °C		 62.1 ksi
@Strain 6.00 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  0.467 GPa
@Strain 10.0 %,
Temperature 23.0 °C		 67.7 ksi
@Strain 10.0 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  0.542 GPa
@Strain 3.60 %,
Temperature 100 °C		 78.6 ksi
@Strain 3.60 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  0.607 GPa
@Strain 3.00 %,
Temperature 100 °C		 88.0 ksi
@Strain 3.00 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.627 GPa
@Strain 4.50 %,
Temperature 80.0 °C		 90.9 ksi
@Strain 4.50 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  0.680 GPa
@Strain 2.50 %,
Temperature 80.0 °C		 98.6 ksi
@Strain 2.50 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  0.693 GPa
@Strain 11.0 %,
Temperature 0.000 °C		 100 ksi
@Strain 11.0 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  0.727 GPa
@Strain 1.50 %,
Temperature 100 °C		 105 ksi
@Strain 1.50 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  0.768 GPa
@Strain 5.00 %,
Temperature 23.0 °C		 111 ksi
@Strain 5.00 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  0.785 GPa
@Strain 1.30 %,
Temperature 100 °C		 114 ksi
@Strain 1.30 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.860 GPa
@Strain 0.500 %,
Temperature 100 °C		 125 ksi
@Strain 0.500 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  0.900 GPa
@Strain 0.600 %,
Temperature 100 °C		 131 ksi
@Strain 0.600 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.995 GPa
@Strain 1.60 %,
Temperature 80.0 °C		 144 ksi
@Strain 1.60 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.025 GPa
@Strain 0.400 %,
Temperature 80.0 °C		 148.7 ksi
@Strain 0.400 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  1.255 GPa
@Strain 2.00 %,
Temperature 23.0 °C		 182.0 ksi
@Strain 2.00 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  1.274 GPa
@Strain 0.500 %,
Temperature 80.0 °C		 184.8 ksi
@Strain 0.500 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.575 GPa
@Strain 4.40 %,
Temperature 0.000 °C		 228.4 ksi
@Strain 4.40 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  1.84 GPa
@Strain 0.700 %,
Temperature 23.0 °C		 267 ksi
@Strain 0.700 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2.20 GPa
@Strain 0.100 %,
Temperature 23.0 °C		 319 ksi
@Strain 0.100 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2.41 GPa
@Strain 4.90 %,
Temperature -40.0 °C		 350 ksi
@Strain 4.90 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  2.75 GPa
@Strain 2.80 %,
Temperature 23.0 °C		 399 ksi
@Strain 2.80 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  2.77 GPa
@Strain 3.30 %,
Temperature 0.000 °C		 402 ksi
@Strain 3.30 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  3.48 GPa
@Strain 1.60 %,
Temperature 0.000 °C		 505 ksi
@Strain 1.60 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  3.49 GPa
@Strain 3.10 %,
Temperature -40.0 °C		 507 ksi
@Strain 3.10 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  3.61 GPa
@Strain 2.00 %,
Temperature 23.0 °C		 524 ksi
@Strain 2.00 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  3.86 GPa
@Strain 2.80 %,
Temperature -40.0 °C		 561 ksi
@Strain 2.80 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  3.88 GPa
@Strain 2.10 %,
Temperature 0.000 °C		 563 ksi
@Strain 2.10 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  4.48 GPa
@Strain 1.30 %,
Temperature 23.0 °C		 650 ksi
@Strain 1.30 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  4.53 GPa
@Strain 2.10 %,
Temperature -40.0 °C		 657 ksi
@Strain 2.10 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  4.61 GPa
@Strain 1.40 %,
Temperature 0.000 °C		 668 ksi
@Strain 1.40 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  4.7375 GPa
@Strain 0.800 %,
Temperature 0.000 °C		 687.13 ksi
@Strain 0.800 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  4.91 GPa
@Strain 0.900 %,
Temperature 23.0 °C		 712 ksi
@Strain 0.900 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  4.99 GPa
@Strain 1.80 %,
Temperature -40.0 °C		 724 ksi
@Strain 1.80 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  5.10 GPa
@Strain 0.300 %,
Temperature 0.000 °C		 740 ksi
@Strain 0.300 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.19 GPa
@Strain 1.40 %,
Temperature -40.0 °C		 753 ksi
@Strain 1.40 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  5.22 GPa
@Strain 0.600 %,
Temperature 0.000 °C		 757 ksi
@Strain 0.600 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.25 GPa
@Strain 0.400 %,
Temperature 23.0 °C		 761 ksi
@Strain 0.400 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.365 GPa
@Strain 0.200 %,
Temperature 0.000 °C		 778.1 ksi
@Strain 0.200 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.67 GPa
@Strain 1.30 %,
Temperature -40.0 °C		 822 ksi
@Strain 1.30 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  5.91 GPa
@Strain 0.500 %,
Temperature -40.0 °C		 857 ksi
@Strain 0.500 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  6.30 GPa
@Strain 0.800 %,
Temperature -40.0 °C		 914 ksi
@Strain 0.800 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  6.77 GPa
@Strain 0.300 %,
Temperature -40.0 °C		 981 ksi
@Strain 0.300 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  9.00 kJ/m² 4.28 ft-lb/in² DAM; ISO 180/1A
  13.0 kJ/m² 6.19 ft-lb/in² 50%RH; ISO 180/1A
  5.00 kJ/m²
@Temperature -40.0 °C		 2.38 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1A
  5.00 kJ/m²
@Temperature -40.0 °C		 2.38 ft-lb/in²
@Temperature -40.0 °F		 50%RH; ISO 180/1A
  6.00 kJ/m²
@Temperature -30.0 °C		 2.86 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
  6.00 kJ/m²
@Temperature -30.0 °C		 2.86 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  190 kJ/m² 90.4 ft-lb/in² DAM; ISO 180/1U
  330 kJ/m² 157 ft-lb/in² 50%RH; ISO 180/1U
  90.0 kJ/m²
@Temperature -30.0 °C		 42.8 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1U
  100 kJ/m²
@Temperature -30.0 °C		 47.6 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1U
Charpy Impact Unnotched  21.0 J/cm² 99.9 ft-lb/in² DAM; ISO 179/1eU
  33.0 J/cm² 157 ft-lb/in² 50%RH; ISO 179/1eU
  9.00 J/cm²
@Temperature -30.0 °C		 42.8 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
  12.0 J/cm²
@Temperature -30.0 °C		 57.1 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
Charpy Impact, Notched  0.900 J/cm² 4.28 ft-lb/in² DAM; ISO 179/1eA
  1.50 J/cm² 7.14 ft-lb/in² 50%RH; ISO 179/1eA
  0.300 J/cm²
@Temperature -40.0 °C		 1.43 ft-lb/in²
@Temperature -40.0 °F		 50%RH; ISO 179/1eA
  0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
  0.400 J/cm²
@Temperature -40.0 °C		 1.90 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 179/1eA
  0.500 J/cm²
@Temperature -30.0 °C		 2.38 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+13 ohm-cm 1.00e+13 ohm-cm DAM; IEC 60093
Dielectric Constant   3.8
@Frequency 1.00e+6 Hz		 3.8
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
  4.0
@Frequency 100 Hz		 4.0
@Frequency 100 Hz		 DAM; IEC 60250
Dielectric Strength  24.0 kV/mm 610 kV/in DAM; IEC 60243-1
Dissipation Factor   0.010
@Frequency 100 Hz		 0.010
@Frequency 100 Hz		 DAM; IEC 60250
  0.010
@Frequency 1.00e+6 Hz		 0.010
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
Comparative Tracking Index  400 V 400 V DAM; IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  64.0 µm/m-°C 35.6 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  65.0 µm/m-°C 36.1 µin/in-°F DAM; ISO 11359-1/-2
Melting Point  256 °C 493 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  205 °C 401 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  80.0 °C 176 °F DAM; ISO 75-1/-2
Flammability, UL94  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 DAM; IEC 60695-11-10
Oxygen Index  25 % 25 % DAM; ISO 4589-1/-2
 
Descriptive Properties
Delivery form Pellets  
Part Marking Code >PA66-IMD36< ISO 11469
Processing Injection Moulding  
Regional Availability North America  
  South and Central America  
Resin Identification PA66-IMD36  
Special characteristics Heat stabilised or stable to heat  

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39752.html

免责声明: 本文 PA66/美国杜邦/12T NC010 矿物增强 耐高温 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4