  4. PA6/美国杜邦/73M40 NC010增强级 注塑 热稳定

PA6/美国杜邦/73M40 NC010增强级 注塑 热稳定

PA6/美国杜邦/73M40 NC010增强级 注塑级 热稳定
 参考图片：

颗粒图片：

包装图片：

成品图片：
100001041143_13526462585748

 

 

 
Physical Properties Metric English Comments
Density  1.28 g/cc 0.0462 lb/in³  
  1.45 g/cc 0.0524 lb/in³ DAM; ISO 1183
Water Absorption  5.4 %
@Thickness 2.00 mm		 5.4 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  1.80 %
@Thickness 2.00 mm		 1.80 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Viscosity   105300 cP
@Shear Rate 5000 1/s,
Temperature 280 °C		 105300 cP
@Shear Rate 5000 1/s,
Temperature 536 °F		 ISO 11403-1 -2
  117100 cP
@Shear Rate 5000 1/s,
Temperature 270 °C		 117100 cP
@Shear Rate 5000 1/s,
Temperature 518 °F		 ISO 11403-1 -2
  130500 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 130500 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  326200 cP
@Shear Rate 500 1/s,
Temperature 280 °C		 326200 cP
@Shear Rate 500 1/s,
Temperature 536 °F		 ISO 11403-1 -2
  404600 cP
@Shear Rate 500 1/s,
Temperature 270 °C		 404600 cP
@Shear Rate 500 1/s,
Temperature 518 °F		 ISO 11403-1 -2
  500200 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 500200 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
Viscosity Test  145 cm³/g 145 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0080 cm/cm 0.0080 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0080 cm/cm 0.0080 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  59.0 MPa 8560 psi 50%RH; ISO 527-1/-2
  87.0 MPa 12600 psi DAM; ISO 527-1/-2
Tensile Stress  7.55 MPa
@Strain 0.600 %,
Temperature 90.0 °C		 1100 psi
@Strain 0.600 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  8.62 MPa
@Strain 1.25 %,
Temperature 150 °C		 1250 psi
@Strain 1.25 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  8.99 MPa
@Strain 0.870 %,
Temperature 90.0 °C		 1300 psi
@Strain 0.870 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  20.73 MPa
@Strain 0.960 %,
Temperature 23.0 °C		 3007 psi
@Strain 0.960 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  23.1 MPa
@Strain 8.78 %,
Temperature 150 °C		 3350 psi
@Strain 8.78 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  24.23 MPa
@Strain 3.51 %,
Temperature 90.0 °C		 3514 psi
@Strain 3.51 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  27.06 MPa
@Strain 17.23 %,
Temperature 150 °C		 3925 psi
@Strain 17.23 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  29.08 MPa
@Strain 26.18 %,
Temperature 150 °C		 4218 psi
@Strain 26.18 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  30.54 MPa
@Strain 6.08 %,
Temperature 90.0 °C		 4429 psi
@Strain 6.08 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  32.34 MPa
@Strain 6.02 %,
Temperature 90.0 °C		 4691 psi
@Strain 6.02 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  33.59 MPa
@Strain 8.65 %,
Temperature 90.0 °C		 4872 psi
@Strain 8.65 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  39.29 MPa
@Strain 12.38 %,
Temperature 90.0 °C		 5699 psi
@Strain 12.38 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  40.94 MPa
@Strain 0.800 %,
Temperature 40.0 °C		 5938 psi
@Strain 0.800 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  42.34 MPa
@Strain 19.17 %,
Temperature 90.0 °C		 6141 psi
@Strain 19.17 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  42.45 MPa
@Strain 3.81 %,
Temperature 23.0 °C		 6157 psi
@Strain 3.81 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  50.59 MPa
@Strain 0.720 %,
Temperature -40.0 °C		 7337 psi
@Strain 0.720 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  52.12 MPa
@Strain 6.65 %,
Temperature 23.0 °C		 7559 psi
@Strain 6.65 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  56.95 MPa
@Strain 9.50 %,
Temperature 23.0 °C		 8260 psi
@Strain 9.50 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  61.67 MPa
@Strain 18.04 %,
Temperature 23.0 °C		 8944 psi
@Strain 18.04 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  66.28 MPa
@Strain 2.93 %,
Temperature 40.0 °C		 9613 psi
@Strain 2.93 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  68.33 MPa
@Strain 6.04 %,
Temperature 40.0 °C		 9910 psi
@Strain 6.04 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  70.17 MPa
@Strain 9.22 %,
Temperature 40.0 °C		 10180 psi
@Strain 9.22 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  73.04 MPa
@Strain 1.41 %,
Temperature 23.0 °C		 10590 psi
@Strain 1.41 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  76.08 MPa
@Strain 1.16 %,
Temperature -40.0 °C		 11030 psi
@Strain 1.16 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  92.16 MPa
@Strain 2.56 %,
Temperature 23.0 °C		 13370 psi
@Strain 2.56 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  93.81 MPa
@Strain 1.80 %,
Temperature 0.000 °C		 13610 psi
@Strain 1.80 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  95.68 MPa
@Strain 1.60 %,
Temperature -40.0 °C		 13880 psi
@Strain 1.60 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  108 MPa
@Strain 2.00 %,
Temperature -40.0 °C		 15700 psi
@Strain 2.00 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  108.25 MPa
@Strain 2.89 %,
Temperature 0.000 °C		 15700 psi
@Strain 2.89 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  108.64 MPa
@Strain 2.02 %,
Temperature -40.0 °C		 15757 psi
@Strain 2.02 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  110.15 MPa
@Strain 2.08 %,
Temperature -20.0 °C		 15976 psi
@Strain 2.08 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  121.44 MPa
@Strain 3.10 %,
Temperature -20.0 °C		 17613 psi
@Strain 3.10 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  122.61 MPa
@Strain 2.54 %,
Temperature -40.0 °C		 17783 psi
@Strain 2.54 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  124.84 MPa
@Strain 3.61 %,
Temperature -40.0 °C		 18107 psi
@Strain 3.61 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  133.68 MPa
@Strain 3.33 %,
Temperature -40.0 °C		 19389 psi
@Strain 3.33 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  138.48 MPa
@Strain 4.29 %,
Temperature -40.0 °C		 20085 psi
@Strain 4.29 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  5.00 MPa
@Strain 0.370 %,
Time 3600 sec		 725 psi
@Strain 0.370 %,
Time 1.00 hour		 50%RH; isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.430 %,
Time 36000 sec		 725 psi
@Strain 0.430 %,
Time 10.0 hour		 50%RH; isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.490 %,
Time 360000 sec		 725 psi
@Strain 0.490 %,
Time 100 hour		 50%RH; isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.600 %,
Time 3.60e+6 sec		 725 psi
@Strain 0.600 %,
Time 1000 hour		 50%RH; isochronous; ISO 11403-1 -2
Elongation at Break  10 % 10 % DAM; ISO 527-1/-2
  25 % 25 % 50%RH; ISO 527-1/-2
Tensile Modulus  2.20 GPa 319 ksi 50%RH; ISO 527-1/-2
  6.00 GPa 870 ksi DAM; ISO 527-1/-2
  0.936 GPa
@Temperature 120 °C		 136 ksi
@Temperature 248 °F		 DAM; ISO 11403-1 -2
  4.911 GPa
@Temperature 40.0 °C		 712.3 ksi
@Temperature 104 °F		 DAM; ISO 11403-1 -2
  8.087 GPa
@Temperature -40.0 °C		 1173 ksi
@Temperature -40.0 °F		 DAM; ISO 11403-1 -2
Flexural Modulus  5.90 GPa 856 ksi DAM; ISO 178
Secant Modulus   0.401 GPa
@Strain 15.19 %,
Temperature 23.0 °C		 58.2 ksi
@Strain 15.19 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  0.51614 GPa
@Strain 11.4 %,
Temperature 23.0 °C		 74.861 ksi
@Strain 11.4 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  0.712 GPa
@Strain 7.60 %,
Temperature 23.0 °C		 103 ksi
@Strain 7.60 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  0.965 GPa
@Strain 7.15 %,
Temperature 40.0 °C		 140 ksi
@Strain 7.15 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  1.11 GPa
@Strain 3.81 %,
Temperature 23.0 °C		 162 ksi
@Strain 3.81 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2.16 GPa
@Strain 0.960 %,
Temperature 23.0 °C		 313 ksi
@Strain 0.960 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2.26 GPa
@Strain 2.93 %,
Temperature 40.0 °C		 328 ksi
@Strain 2.93 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  3.60 GPa
@Strain 2.56 %,
Temperature 23.0 °C		 522 ksi
@Strain 2.56 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  3.73 GPa
@Strain 3.64 %,
Temperature -40.0 °C		 541 ksi
@Strain 3.64 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  3.75 GPa
@Strain 2.89 %,
Temperature 0.000 °C		 543 ksi
@Strain 2.89 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  3.92 GPa
@Strain 3.10 %,
Temperature -20.0 °C		 568 ksi
@Strain 3.10 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  4.21 GPa
@Strain 2.88 %,
Temperature -40.0 °C		 611 ksi
@Strain 2.88 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  4.83 GPa
@Strain 2.54 %,
Temperature -40.0 °C		 700 ksi
@Strain 2.54 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  4.95 GPa
@Strain 2.31 %,
Temperature -40.0 °C		 717 ksi
@Strain 2.31 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  5.1175 GPa
@Strain 0.800 %,
Temperature 40.0 °C		 742.24 ksi
@Strain 0.800 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  5.18 GPa
@Strain 1.41 %,
Temperature 23.0 °C		 751 ksi
@Strain 1.41 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.21 GPa
@Strain 1.80 %,
Temperature 0.000 °C		 756 ksi
@Strain 1.80 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.30 GPa
@Strain 2.08 %,
Temperature -20.0 °C		 768 ksi
@Strain 2.08 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  5.40 GPa
@Strain 2.00 %,
Temperature -40.0 °C		 783 ksi
@Strain 2.00 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  5.80 GPa
@Strain 1.73 %,
Temperature -40.0 °C		 841 ksi
@Strain 1.73 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  6.56 GPa
@Strain 1.16 %,
Temperature -40.0 °C		 951 ksi
@Strain 1.16 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  7.03 GPa
@Strain 0.720 %,
Temperature -40.0 °C		 1020 ksi
@Strain 0.720 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  5.00 kJ/m² 2.38 ft-lb/in² DAM; ISO 180/1A
  7.00 kJ/m² 3.33 ft-lb/in² 50%RH; ISO 180/1A
  4.00 kJ/m²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
  4.50 kJ/m²
@Temperature -30.0 °C		 2.14 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
Charpy Impact Unnotched  13.0 J/cm² 61.9 ft-lb/in² DAM; ISO 179/1eU
  NB NB 50%RH; ISO 179/1eU
  9.50 J/cm²
@Temperature -30.0 °C		 45.2 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
  9.50 J/cm²
@Temperature -30.0 °C		 45.2 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
Charpy Impact, Notched  0.550 J/cm² 2.62 ft-lb/in² DAM; ISO 179/1eA
  0.800 J/cm² 3.81 ft-lb/in² 50%RH; ISO 179/1eA
  0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
  0.500 J/cm²
@Temperature -30.0 °C		 2.38 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour  940 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 136000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  947 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 137000 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  963 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 140000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  1010 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 146000 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  1125.4 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 163230 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  1350 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 196000 psi
@Pressure 725 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  1400 MPa
@Time 3600 sec		 203000 psi
@Time 1.00 hour		 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours   659 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 95600 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  667 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 96800 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  680 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 98600 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  704 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 102000 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  755 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 109000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  833 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 121000 psi
@Pressure 725 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  850 MPa
@Time 3.60e+6 sec		 123000 psi
@Time 1000 hour		 50%RH; ISO 899-1
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  65.0 µm/m-°C 36.1 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  75.0 µm/m-°C 41.7 µin/in-°F DAM; ISO 11359-1/-2
Specific Heat Capacity  1.94 J/g-°C 0.464 BTU/lb-°F  
Thermal Conductivity  0.270 W/m-K 1.87 BTU-in/hr-ft²-°F of melt
Melting Point  221 °C 430 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  196 °C 385 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  110 °C 230 °F DAM; ISO 75-1/-2
Vicat Softening Point  210 °C 410 °F DAM; 50°C/h 50N; ISO 306
Flammability, UL94  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 DAM; IEC 60695-11-10
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PA6-MD40< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA6-MD40  
Special characteristics Heat stabilised or stable to heat  
  Platable  

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39758.html

免责声明: 本文 PA6/美国杜邦/73M40 NC010增强级 注塑 热稳定 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4