  4. PA66美国杜邦IG38C1 BK434 矿物玻纤增强38%

PA66美国杜邦IG38C1 BK434 矿物玻纤增强38%

PA66 美国杜邦 IG38C1 BK434 矿物玻纤增强38%
 参考图片：

颗粒图片：

包装图片：

成品图片：
100001041143_13526462585748

 

 

 
Physical Properties Metric English Comments
Density  1.45 g/cc 0.0524 lb/in³ DAM; ISO 1183
Viscosity Test  140 cm³/g 140 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0060 cm/cm 0.0060 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0080 cm/cm 0.0080 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  72.0 MPa 10400 psi 50%RH; ISO 527-1/-2
  120 MPa 17400 psi DAM; ISO 527-1/-2
Tensile Stress   5.20 MPa
@Strain 0.200 %,
Temperature 150 °C		 754 psi
@Strain 0.200 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  6.5826 MPa
@Strain 0.300 %,
Temperature 150 °C		 954.73 psi
@Strain 0.300 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  6.9336 MPa
@Strain 0.100 %,
Temperature 23.0 °C		 1005.6 psi
@Strain 0.100 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  7.776 MPa
@Strain 0.100 %,
Temperature 0.000 °C		 1128 psi
@Strain 0.100 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  8.0574 MPa
@Strain 0.100 %,
Temperature 0.000 °C		 1168.6 psi
@Strain 0.100 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  9.077 MPa
@Strain 0.100 %,
Temperature -40.0 °C		 1317 psi
@Strain 0.100 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  9.35 MPa
@Strain 0.200 %,
Temperature 23.0 °C		 1360 psi
@Strain 0.200 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  14.4 MPa
@Strain 0.600 %,
Temperature 150 °C		 2090 psi
@Strain 0.600 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  15.073 MPa
@Strain 0.800 %,
Temperature 150 °C		 2186.2 psi
@Strain 0.800 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  21.3 MPa
@Strain 1.00 %,
Temperature 150 °C		 3090 psi
@Strain 1.00 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  21.879 MPa
@Strain 0.500 %,
Temperature 23.0 °C		 3173.3 psi
@Strain 0.500 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  22.705 MPa
@Strain 1.40 %,
Temperature 150 °C		 3293.1 psi
@Strain 1.40 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  28.8 MPa
@Strain 0.300 %,
Temperature -40.0 °C		 4180 psi
@Strain 0.300 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  28.811 MPa
@Strain 2.20 %,
Temperature 150 °C		 4178.7 psi
@Strain 2.20 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  33.9 MPa
@Strain 2.00 %,
Temperature 150 °C		 4920 psi
@Strain 2.00 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  35.717 MPa
@Strain 0.900 %,
Temperature 23.0 °C		 5180.3 psi
@Strain 0.900 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  36.644 MPa
@Strain 0.500 %,
Temperature 0.000 °C		 5314.8 psi
@Strain 0.500 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  46.252 MPa
@Strain 0.700 %,
Temperature 23.0 °C		 6708.3 psi
@Strain 0.700 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  46.75 MPa
@Strain 1.30 %,
Temperature 23.0 °C		 6781 psi
@Strain 1.30 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  60.167 MPa
@Strain 0.900 %,
Temperature 0.000 °C		 8726.5 psi
@Strain 0.900 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  60.379 MPa
@Strain 0.800 %,
Temperature 0.000 °C		 8757.2 psi
@Strain 0.800 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  66.744 MPa
@Strain 0.800 %,
Temperature -40.0 °C		 9680.4 psi
@Strain 0.800 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  68.454 MPa
@Strain 1.10 %,
Temperature 23.0 °C		 9928.4 psi
@Strain 1.10 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  72.0 MPa
@Strain 0.800 %,
Temperature -40.0 °C		 10400 psi
@Strain 0.800 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  74.261 MPa
@Strain 1.20 %,
Temperature 0.000 °C		 10771 psi
@Strain 1.20 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  80.016 MPa
@Strain 1.10 %,
Temperature 0.000 °C		 11605 psi
@Strain 1.10 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  81.669 MPa
@Strain 1.40 %,
Temperature 23.0 °C		 11845 psi
@Strain 1.40 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  89.095 MPa
@Strain 1.10 %,
Temperature -40.0 °C		 12922 psi
@Strain 1.10 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  94.3 MPa
@Strain 1.10 %,
Temperature -40.0 °C		 13700 psi
@Strain 1.10 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  96.625 MPa
@Strain 1.40 %,
Temperature 0.000 °C		 14014 psi
@Strain 1.40 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  109.95 MPa
@Strain 2.70 %,
Temperature 23.0 °C		 15947 psi
@Strain 2.70 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  112.8 MPa
@Strain 1.40 %,
Temperature -40.0 °C		 16360 psi
@Strain 1.40 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  121.23 MPa
@Strain 1.60 %,
Temperature -40.0 °C		 17583 psi
@Strain 1.60 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  130.04 MPa
@Strain 2.40 %,
Temperature 0.000 °C		 18861 psi
@Strain 2.40 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
Elongation at Break  2.5 % 2.5 % DAM; ISO 527-1/-2
  4.0 % 4.0 % 50%RH; ISO 527-1/-2
Tensile Modulus  5.00 GPa 725 ksi 50%RH; ISO 527-1/-2
  7.50 GPa 1090 ksi DAM; ISO 527-1/-2
Flexural Modulus  7.00 GPa 1020 ksi DAM; ISO 178
Secant Modulus   1.33 GPa
@Strain 3.00 %,
Temperature 100 °C		 193 ksi
@Strain 3.00 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  1.408 GPa
@Strain 3.30 %,
Temperature 80.0 °C		 204.2 ksi
@Strain 3.30 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  1.57 GPa
@Strain 3.70 %,
Temperature 80.0 °C		 227 ksi
@Strain 3.70 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.71 GPa
@Strain 3.00 %,
Temperature 100 °C		 248 ksi
@Strain 3.00 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  1.83 GPa
@Strain 1.90 %,
Temperature 100 °C		 266 ksi
@Strain 1.90 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  1.86 GPa
@Strain 2.30 %,
Temperature 80.0 °C		 270 ksi
@Strain 2.30 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2.15 GPa
@Strain 2.40 %,
Temperature 80.0 °C		 311 ksi
@Strain 2.40 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  2.1489 GPa
@Strain 2.00 %,
Temperature 100 °C		 311.68 ksi
@Strain 2.00 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2.18 GPa
@Strain 1.20 %,
Temperature 100 °C		 316 ksi
@Strain 1.20 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  2.23 GPa
@Strain 1.50 %,
Temperature 80.0 °C		 324 ksi
@Strain 1.50 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2.47 GPa
@Strain 0.700 %,
Temperature 100 °C		 359 ksi
@Strain 0.700 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  2.61 GPa
@Strain 1.10 %,
Temperature 100 °C		 378 ksi
@Strain 1.10 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2.66 GPa
@Strain 0.700 %,
Temperature 80.0 °C		 385 ksi
@Strain 0.700 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2.71 GPa
@Strain 2.50 %,
Temperature 23.0 °C		 393 ksi
@Strain 2.50 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2.71 GPa
@Strain 1.30 %,
Temperature 80.0 °C		 393 ksi
@Strain 1.30 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  2.9326 GPa
@Strain 0.200 %,
Temperature 100 °C		 425.34 ksi
@Strain 0.200 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  3.0154 GPa
@Strain 0.500 %,
Temperature 100 °C		 437.35 ksi
@Strain 0.500 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  3.0481 GPa
@Strain 2.00 %,
Temperature 23.0 °C		 442.10 ksi
@Strain 2.00 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.0492 GPa
@Strain 0.200 %,
Temperature 80.0 °C		 442.26 ksi
@Strain 0.200 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  3.2307 GPa
@Strain 0.200 %,
Temperature 100 °C		 468.58 ksi
@Strain 0.200 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  3.24 GPa
@Strain 0.600 %,
Temperature 80.0 °C		 469 ksi
@Strain 0.600 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  3.57 GPa
@Strain 0.200 %,
Temperature 80.0 °C		 518 ksi
@Strain 0.200 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  3.8709 GPa
@Strain 1.00 %,
Temperature 23.0 °C		 561.44 ksi
@Strain 1.00 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.3758 GPa
@Strain 0.500 %,
Temperature 23.0 °C		 634.67 ksi
@Strain 0.500 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.675 GPa
@Strain 0.200 %,
Temperature 23.0 °C		 678.1 ksi
@Strain 0.200 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.71 GPa
@Strain 2.20 %,
Temperature 23.0 °C		 682 ksi
@Strain 2.20 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  4.9232 GPa
@Strain 2.00 %,
Temperature 0.000 °C		 714.06 ksi
@Strain 2.00 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.54 GPa
@Strain 1.60 %,
Temperature 23.0 °C		 804 ksi
@Strain 1.60 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.86 GPa
@Strain 1.40 %,
Temperature 0.000 °C		 850 ksi
@Strain 1.40 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.88 GPa
@Strain 2.10 %,
Temperature 0.000 °C		 852 ksi
@Strain 2.10 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  6.11 GPa
@Strain 1.20 %,
Temperature 23.0 °C		 886 ksi
@Strain 1.20 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  6.5513 GPa
@Strain 1.00 %,
Temperature 0.000 °C		 950.20 ksi
@Strain 1.00 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  6.61 GPa
@Strain 0.700 %,
Temperature 23.0 °C		 958 ksi
@Strain 0.700 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  6.61 GPa
@Strain 1.60 %,
Temperature 0.000 °C		 959 ksi
@Strain 1.60 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  6.82 GPa
@Strain 2.20 %,
Temperature -40.0 °C		 989 ksi
@Strain 2.20 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  6.9336 GPa
@Strain 0.100 %,
Temperature 23.0 °C		 1005.6 ksi
@Strain 0.100 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  6.975 GPa
@Strain 2.00 %,
Temperature -40.0 °C		 1012 ksi
@Strain 2.00 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  7.16 GPa
@Strain 1.20 %,
Temperature 0.000 °C		 1040 ksi
@Strain 1.20 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  7.3288 GPa
@Strain 0.500 %,
Temperature 0.000 °C		 1063.0 ksi
@Strain 0.500 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  7.34 GPa
@Strain 1.80 %,
Temperature -40.0 °C		 1060 ksi
@Strain 1.80 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  7.55 GPa
@Strain 0.800 %,
Temperature 0.000 °C		 1090 ksi
@Strain 0.800 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  7.71 GPa
@Strain 1.60 %,
Temperature -40.0 °C		 1120 ksi
@Strain 1.60 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  7.776 GPa
@Strain 0.100 %,
Temperature 0.000 °C		 1128 ksi
@Strain 0.100 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  8.03 GPa
@Strain 1.20 %,
Temperature -40.0 °C		 1160 ksi
@Strain 1.20 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  8.0574 GPa
@Strain 0.100 %,
Temperature 0.000 °C		 1168.6 ksi
@Strain 0.100 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  8.343 GPa
@Strain 0.800 %,
Temperature -40.0 °C		 1210 ksi
@Strain 0.800 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  8.39 GPa
@Strain 1.20 %,
Temperature -40.0 °C		 1220 ksi
@Strain 1.20 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  9.00 GPa
@Strain 0.800 %,
Temperature -40.0 °C		 1310 ksi
@Strain 0.800 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  9.077 GPa
@Strain 0.100 %,
Temperature -40.0 °C		 1317 ksi
@Strain 0.100 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  9.60 GPa
@Strain 0.300 %,
Temperature -40.0 °C		 1390 ksi
@Strain 0.300 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  4.00 kJ/m² 1.90 ft-lb/in² DAM; ISO 180/1A
  4.00 kJ/m² 1.90 ft-lb/in² 50%RH; ISO 180/1A
  3.80 kJ/m²
@Temperature -40.0 °C		 1.81 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)  35.0 kJ/m² 16.7 ft-lb/in² DAM; ISO 180/1U
Charpy Impact Unnotched  4.00 J/cm² 19.0 ft-lb/in² DAM; ISO 179/1eU
Charpy Impact, Notched  0.300 J/cm² 1.43 ft-lb/in² DAM; ISO 179/1eA
  0.300 J/cm²
@Temperature -30.0 °C		 1.43 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
  0.300 J/cm²
@Temperature -40.0 °C		 1.43 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 179/1eA
 
Thermal Properties Metric English Comments
Melting Point  263 °C 505 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  255 °C 491 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  230 °C 446 °F DAM; ISO 75-1/-2
 
Descriptive Properties
Delivery form Pellets  
Part Marking Code >PA66-(MD+GF)38< ISO 11469
Processing Injection Moulding  
Regional Availability North America  
  South and Central America  
Resin Identification PA66-(MD+GF)38  
Special characteristics Heat stabilised or stable to heat  

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39760.html

免责声明: 本文 PA66美国杜邦IG38C1 BK434 矿物玻纤增强38% 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4