  4. PA66/美国杜邦/70K20HSL NC010热稳定 耐磨

PA66/美国杜邦/70K20HSL NC010热稳定 耐磨

PA66/美国杜邦/70K20HSL NC010 热稳定 耐磨尼龙
 参考图片：

颗粒图片：

包装图片：

成品图片：
100001041143_13526462585748

 

 

 
Physical Properties Metric English Comments
Density  1.19 g/cc 0.0430 lb/in³ DAM; ISO 1183
Water Absorption  6.8 %
@Thickness 2.00 mm		 6.8 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  2.70 %
@Thickness 2.00 mm		 2.70 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Viscosity Test  135 cm³/g 135 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0090 cm/cm 0.0090 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.014 cm/cm 0.014 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  85.0 MPa 12300 psi 50%RH; ISO 527-1/-2
  110 MPa 16000 psi DAM; ISO 527-1/-2
Tensile Stress   8.75 MPa
@Strain 0.880 %,
Temperature 150 °C		 1270 psi
@Strain 0.880 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  9.04 MPa
@Strain 0.820 %,
Temperature 150 °C		 1310 psi
@Strain 0.820 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  12.5 MPa
@Strain 0.830 %,
Temperature 90.0 °C		 1810 psi
@Strain 0.830 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  13.93 MPa
@Strain 0.860 %,
Temperature 90.0 °C		 2020 psi
@Strain 0.860 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  18.52 MPa
@Strain 0.900 %,
Temperature 40.0 °C		 2686 psi
@Strain 0.900 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  25.19 MPa
@Strain 3.50 %,
Temperature 150 °C		 3654 psi
@Strain 3.50 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  25.82 MPa
@Strain 0.870 %,
Temperature 23.0 °C		 3745 psi
@Strain 0.870 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  26.02 MPa
@Strain 0.540 %,
Temperature 23.0 °C		 3774 psi
@Strain 0.540 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  26.2 MPa
@Strain 3.25 %,
Temperature 150 °C		 3800 psi
@Strain 3.25 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  27.21 MPa
@Strain 0.540 %,
Temperature 0.000 °C		 3946 psi
@Strain 0.540 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  28.08 MPa
@Strain 0.660 %,
Temperature 40.0 °C		 4073 psi
@Strain 0.660 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  29.33 MPa
@Strain 0.560 %,
Temperature -20.0 °C		 4254 psi
@Strain 0.560 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  33.12 MPa
@Strain 0.710 %,
Temperature 0.000 °C		 4804 psi
@Strain 0.710 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  33.22 MPa
@Strain 0.610 %,
Temperature -20.0 °C		 4818 psi
@Strain 0.610 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  33.89 MPa
@Strain 3.32 %,
Temperature 90.0 °C		 4915 psi
@Strain 3.32 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  35.54 MPa
@Strain 6.10 %,
Temperature 150 °C		 5155 psi
@Strain 6.10 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  37.55 MPa
@Strain 8.70 %,
Temperature 150 °C		 5446 psi
@Strain 8.70 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  37.59 MPa
@Strain 3.36 %,
Temperature 90.0 °C		 5452 psi
@Strain 3.36 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  37.79 MPa
@Strain 5.68 %,
Temperature 150 °C		 5481 psi
@Strain 5.68 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  41.14 MPa
@Strain 8.11 %,
Temperature 150 °C		 5967 psi
@Strain 8.11 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  46.25 MPa
@Strain 3.57 %,
Temperature 40.0 °C		 6708 psi
@Strain 3.57 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  48.34 MPa
@Strain 5.83 %,
Temperature 90.0 °C		 7011 psi
@Strain 5.83 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  52.2 MPa
@Strain 8.30 %,
Temperature 90.0 °C		 7570 psi
@Strain 8.30 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  53.89 MPa
@Strain 5.86 %,
Temperature 90.0 °C		 7816 psi
@Strain 5.86 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  58.0 MPa
@Strain 3.38 %,
Temperature 23.0 °C		 8410 psi
@Strain 3.38 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  59.5 MPa
@Strain 9.30 %,
Temperature 90.0 °C		 8630 psi
@Strain 9.30 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  64.42 MPa
@Strain 6.25 %,
Temperature 40.0 °C		 9343 psi
@Strain 6.25 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  69.0 MPa
@Strain 8.90 %,
Temperature 40.0 °C		 10000 psi
@Strain 8.90 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  75.18 MPa
@Strain 2.60 %,
Temperature 40.0 °C		 10900 psi
@Strain 2.60 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  75.85 MPa
@Strain 5.90 %,
Temperature 23.0 °C		 11000 psi
@Strain 5.90 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  81.52 MPa
@Strain 2.17 %,
Temperature 23.0 °C		 11820 psi
@Strain 2.17 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  81.65 MPa
@Strain 2.85 %,
Temperature 0.000 °C		 11840 psi
@Strain 2.85 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  81.8 MPa
@Strain 8.40 %,
Temperature 23.0 °C		 11900 psi
@Strain 8.40 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  87.33 MPa
@Strain 4.57 %,
Temperature 40.0 °C		 12670 psi
@Strain 4.57 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  88.63 MPa
@Strain 2.12 %,
Temperature -20.0 °C		 12850 psi
@Strain 2.12 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  89.2 MPa
@Strain 2.21 %,
Temperature 0.000 °C		 12900 psi
@Strain 2.21 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  93.68 MPa
@Strain 2.45 %,
Temperature -20.0 °C		 13590 psi
@Strain 2.45 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  94.4 MPa
@Strain 6.50 %,
Temperature 40.0 °C		 13700 psi
@Strain 6.50 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  96.83 MPa
@Strain 4.97 %,
Temperature 0.000 °C		 14040 psi
@Strain 4.97 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  98.62 MPa
@Strain 3.79 %,
Temperature 23.0 °C		 14300 psi
@Strain 3.79 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  104.7 MPa
@Strain 7.10 %,
Temperature 0.000 °C		 15190 psi
@Strain 7.10 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  105.34 MPa
@Strain 5.40 %,
Temperature 23.0 °C		 15278 psi
@Strain 5.40 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  112.16 MPa
@Strain 4.27 %,
Temperature -20.0 °C		 16267 psi
@Strain 4.27 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  115.95 MPa
@Strain 3.71 %,
Temperature -20.0 °C		 16817 psi
@Strain 3.71 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  122.32 MPa
@Strain 6.11 %,
Temperature -20.0 °C		 17741 psi
@Strain 6.11 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  127.35 MPa
@Strain 5.30 %,
Temperature -20.0 °C		 18471 psi
@Strain 5.30 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
Elongation at Break  5.2 % 5.2 % DAM; ISO 527-1/-2
  7.2 % 7.2 % 50%RH; ISO 527-1/-2
Tensile Modulus  3.50 GPa 508 ksi 50%RH; ISO 527-1/-2
  5.30 GPa 769 ksi DAM; ISO 527-1/-2
  0.910 GPa
@Temperature 230 °C		 132 ksi
@Temperature 446 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.449 GPa
@Temperature 150 °C		 210.2 ksi
@Temperature 302 °F		 DAM; Dynamic; ISO 11403-1 -2
  2.039 GPa
@Temperature 100 °C		 295.7 ksi
@Temperature 212 °F		 DAM; Dynamic; ISO 11403-1 -2
  4.223 GPa
@Temperature 50.0 °C		 612.5 ksi
@Temperature 122 °F		 DAM; Dynamic; ISO 11403-1 -2
  4.50 GPa
@Temperature 23.0 °C		 653 ksi
@Temperature 73.4 °F		 DAM; Dynamic; ISO 11403-1 -2
Flexural Modulus  3.30 GPa 479 ksi 50%RH; ISO 178
  4.90 GPa 711 ksi DAM; ISO 178
Secant Modulus   0.949 GPa
@Strain 7.13 %,
Temperature 40.0 °C		 138 ksi
@Strain 7.13 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  1.18 GPa
@Strain 6.75 %,
Temperature 23.0 °C		 172 ksi
@Strain 6.75 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  1.30 GPa
@Strain 3.57 %,
Temperature 40.0 °C		 188 ksi
@Strain 3.57 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  1.72 GPa
@Strain 3.38 %,
Temperature 23.0 °C		 249 ksi
@Strain 3.38 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  1.73 GPa
@Strain 5.22 %,
Temperature 40.0 °C		 252 ksi
@Strain 5.22 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  1.77 GPa
@Strain 5.69 %,
Temperature 0.000 °C		 257 ksi
@Strain 5.69 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  2.06 GPa
@Strain 0.900 %,
Temperature 40.0 °C		 298 ksi
@Strain 0.900 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  2.35 GPa
@Strain 4.32 %,
Temperature 23.0 °C		 340 ksi
@Strain 4.32 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  2.38 GPa
@Strain 4.89 %,
Temperature -20.0 °C		 345 ksi
@Strain 4.89 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  2.84 GPa
@Strain 4.25 %,
Temperature -20.0 °C		 412 ksi
@Strain 4.25 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  2.86 GPa
@Strain 2.85 %,
Temperature 0.000 °C		 416 ksi
@Strain 2.85 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  2.89 GPa
@Strain 2.60 %,
Temperature 40.0 °C		 419 ksi
@Strain 2.60 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  2.97 GPa
@Strain 0.870 %,
Temperature 23.0 °C		 430 ksi
@Strain 0.870 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.76 GPa
@Strain 2.17 %,
Temperature 23.0 °C		 545 ksi
@Strain 2.17 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  3.82 GPa
@Strain 2.45 %,
Temperature -20.0 °C		 555 ksi
@Strain 2.45 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  4.0362 GPa
@Strain 2.21 %,
Temperature 0.000 °C		 585.41 ksi
@Strain 2.21 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  4.18 GPa
@Strain 2.12 %,
Temperature -20.0 °C		 606 ksi
@Strain 2.12 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  4.25 GPa
@Strain 0.660 %,
Temperature 40.0 °C		 617 ksi
@Strain 0.660 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  4.66 GPa
@Strain 0.710 %,
Temperature 0.000 °C		 677 ksi
@Strain 0.710 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  4.82 GPa
@Strain 0.540 %,
Temperature 23.0 °C		 699 ksi
@Strain 0.540 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.04 GPa
@Strain 0.540 %,
Temperature 0.000 °C		 731 ksi
@Strain 0.540 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.2375 GPa
@Strain 0.560 %,
Temperature -20.0 °C		 759.65 ksi
@Strain 0.560 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  5.4459 GPa
@Strain 0.610 %,
Temperature -20.0 °C		 789.87 ksi
@Strain 0.610 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  5.00 kJ/m² 2.38 ft-lb/in² DAM; ISO 180/1A
  7.00 kJ/m² 3.33 ft-lb/in² 50%RH; ISO 180/1A
Charpy Impact Unnotched  5.00 J/cm² 23.8 ft-lb/in² DAM; ISO 179/1eU
  6.50 J/cm² 30.9 ft-lb/in² 50%RH; ISO 179/1eU
  4.00 J/cm²
@Temperature -30.0 °C		 19.0 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
Charpy Impact, Notched  0.600 J/cm² 2.86 ft-lb/in² DAM; ISO 179/1eA
  0.900 J/cm² 4.28 ft-lb/in² 50%RH; ISO 179/1eA
  0.500 J/cm²
@Temperature -30.0 °C		 2.38 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+11 ohm-cm 1.00e+11 ohm-cm DAM; IEC 60093
Surface Resistance  >= 1.00e+15 ohm >= 1.00e+15 ohm 50%RH; IEC 60093
Dielectric Strength  23.0 kV/mm 584 kV/in DAM; IEC 60243-1
Dissipation Factor   0.014
@Frequency 100 Hz		 0.014
@Frequency 100 Hz		 DAM; IEC 60250
  0.014
@Frequency 1.00e+6 Hz		 0.014
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  47.0 µm/m-°C 26.1 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  75.0 µm/m-°C 41.7 µin/in-°F DAM; ISO 11359-1/-2
Melting Point  263 °C 505 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  255 °C 491 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  222 °C 432 °F DAM; ISO 75-1/-2
Vicat Softening Point  240 °C 464 °F DAM; 50°C/h 50N; ISO 306
Glass Transition Temp, Tg  80.0 °C 176 °F DAM; 10°C/min; ISO 11357-1/-2
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Part Marking Code >PA66-AF20< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA66-AF20  
Special characteristics Heat stabilised or stable to heat  

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39801.html

免责声明: 本文 PA66/美国杜邦/70K20HSL NC010热稳定 耐磨 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4