  4. PA6/美国杜邦/73G15L NC010 增强级

PA6/美国杜邦/73G15L NC010 增强级

PA6/美国杜邦/73G15L NC010 增强级
 参考图片：

颗粒图片：

包装图片：

成品图片：
f99c6df6dda12fe1_1

 

 

 
Physical Properties Metric English Comments
Density  1.07 g/cc 0.0387 lb/in³  
  1.23 g/cc 0.0444 lb/in³ DAM; ISO 1183
Water Absorption  7.6 %
@Thickness 2.00 mm		 7.6 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  2.50 %
@Thickness 2.00 mm		 2.50 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Viscosity Test  150 cm³/g 150 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0080 cm/cm 0.0080 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  72.0 MPa 10400 psi 50%RH; ISO 527-1/-2
  135 MPa 19600 psi DAM; ISO 527-1/-2
Tensile Stress   4.30 MPa
@Strain 0.240 %,
Temperature 150 °C		 624 psi
@Strain 0.240 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  7.19 MPa
@Strain 0.270 %,
Temperature 40.0 °C		 1040 psi
@Strain 0.270 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  7.60 MPa
@Strain 0.250 %,
Temperature 23.0 °C		 1100 psi
@Strain 0.250 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  12.69 MPa
@Strain 0.620 %,
Temperature 150 °C		 1841 psi
@Strain 0.620 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  15.61 MPa
@Strain 1.08 %,
Temperature 150 °C		 2264 psi
@Strain 1.08 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  16.85 MPa
@Strain 0.330 %,
Temperature 0.000 °C		 2444 psi
@Strain 0.330 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  23.05 MPa
@Strain 2.05 %,
Temperature 150 °C		 3343 psi
@Strain 2.05 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  28.13 MPa
@Strain 3.05 %,
Temperature 150 °C		 4080 psi
@Strain 3.05 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  28.97 MPa
@Strain 0.400 %,
Temperature -40.0 °C		 4201 psi
@Strain 0.400 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  29.16 MPa
@Strain 1.85 %,
Temperature 150 °C		 4229 psi
@Strain 1.85 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  33.36 MPa
@Strain 1.49 %,
Temperature 40.0 °C		 4838 psi
@Strain 1.49 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  37.35 MPa
@Strain 1.43 %,
Temperature 23.0 °C		 5417 psi
@Strain 1.43 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  39.21 MPa
@Strain 3.13 %,
Temperature 150 °C		 5687 psi
@Strain 3.13 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  42.59 MPa
@Strain 0.810 %,
Temperature 40.0 °C		 6177 psi
@Strain 0.810 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  45.14 MPa
@Strain 4.46 %,
Temperature 150 °C		 6547 psi
@Strain 4.46 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  49.68 MPa
@Strain 2.64 %,
Temperature 40.0 °C		 7205 psi
@Strain 2.64 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  56.39 MPa
@Strain 2.57 %,
Temperature 23.0 °C		 8179 psi
@Strain 2.57 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  56.95 MPa
@Strain 0.900 %,
Temperature -20.0 °C		 8260 psi
@Strain 0.900 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  58.81 MPa
@Strain 1.32 %,
Temperature 0.000 °C		 8530 psi
@Strain 1.32 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  59.7 MPa
@Strain 3.93 %,
Temperature 40.0 °C		 8660 psi
@Strain 3.93 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  63.4 MPa
@Strain 1.10 %,
Temperature 23.0 °C		 9200 psi
@Strain 1.10 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  68.83 MPa
@Strain 3.84 %,
Temperature 23.0 °C		 9983 psi
@Strain 3.84 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  70.36 MPa
@Strain 1.44 %,
Temperature 40.0 °C		 10200 psi
@Strain 1.44 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  84.36 MPa
@Strain 1.46 %,
Temperature 0.000 °C		 12240 psi
@Strain 1.46 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  85.29 MPa
@Strain 2.35 %,
Temperature 0.000 °C		 12370 psi
@Strain 2.35 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  90.95 MPa
@Strain 2.07 %,
Temperature 40.0 °C		 13190 psi
@Strain 2.07 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  93.32 MPa
@Strain 1.60 %,
Temperature -20.0 °C		 13530 psi
@Strain 1.60 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  94.32 MPa
@Strain 1.74 %,
Temperature 23.0 °C		 13680 psi
@Strain 1.74 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  98.54 MPa
@Strain 1.69 %,
Temperature -20.0 °C		 14290 psi
@Strain 1.69 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  101.18 MPa
@Strain 3.43 %,
Temperature 0.000 °C		 14675 psi
@Strain 3.43 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  105.22 MPa
@Strain 2.84 %,
Temperature 40.0 °C		 15261 psi
@Strain 2.84 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  106.2 MPa
@Strain 1.60 %,
Temperature -40.0 °C		 15400 psi
@Strain 1.60 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  107.08 MPa
@Strain 1.94 %,
Temperature 0.000 °C		 15531 psi
@Strain 1.94 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  114.51 MPa
@Strain 2.25 %,
Temperature 23.0 °C		 16608 psi
@Strain 2.25 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  119.26 MPa
@Strain 2.35 %,
Temperature -20.0 °C		 17297 psi
@Strain 2.35 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  122.31 MPa
@Strain 2.20 %,
Temperature -20.0 °C		 17740 psi
@Strain 2.20 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  125.45 MPa
@Strain 2.39 %,
Temperature 0.000 °C		 18195 psi
@Strain 2.39 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  130.93 MPa
@Strain 2.89 %,
Temperature 23.0 °C		 18990 psi
@Strain 2.89 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  134.96 MPa
@Strain 3.12 %,
Temperature -20.0 °C		 19574 psi
@Strain 3.12 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  140.72 MPa
@Strain 2.87 %,
Temperature 0.000 °C		 20410 psi
@Strain 2.87 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  141.08 MPa
@Strain 2.68 %,
Temperature -20.0 °C		 20462 psi
@Strain 2.68 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  156.08 MPa
@Strain 3.17 %,
Temperature -20.0 °C		 22638 psi
@Strain 3.17 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  161.7 MPa
@Strain 2.80 %,
Temperature -40.0 °C		 23460 psi
@Strain 2.80 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
Elongation at Break  4.0 % 4.0 % DAM; ISO 527-1/-2
  10 % 10 % 50%RH; ISO 527-1/-2
Tensile Modulus  3.50 GPa 508 ksi 50%RH; ISO 527-1/-2
  6.00 GPa 870 ksi DAM; ISO 527-1/-2
  1.693 GPa
@Temperature 150 °C		 245.5 ksi
@Temperature 302 °F		 50%RH; ISO 11403-1 -2
  1.988 GPa
@Temperature 150 °C		 288.3 ksi
@Temperature 302 °F		 DAM; ISO 11403-1 -2
  2.427 GPa
@Temperature 60.0 °C		 352.0 ksi
@Temperature 140 °F		 50%RH; ISO 11403-1 -2
  3.007 GPa
@Temperature 60.0 °C		 436.1 ksi
@Temperature 140 °F		 DAM; ISO 11403-1 -2
  6.325 GPa
@Temperature -20.0 °C		 917.4 ksi
@Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  6.451 GPa
@Temperature -20.0 °C		 935.6 ksi
@Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
Flexural Modulus  5.00 GPa 725 ksi DAM; ISO 178
Shear Modulus   0.407 GPa
@Temperature 160 °C		 59.0 ksi
@Temperature 320 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.429 GPa
@Temperature 120 °C		 62.2 ksi
@Temperature 248 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.537 GPa
@Temperature 70.0 °C		 77.9 ksi
@Temperature 158 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.374 GPa
@Temperature 20.0 °C		 199.3 ksi
@Temperature 68.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.475 GPa
@Temperature -20.0 °C		 213.9 ksi
@Temperature -4.00 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.557 GPa
@Temperature -50.0 °C		 225.8 ksi
@Temperature -58.0 °F		 DAM; Dynamic; ISO 11403-1 -2
Secant Modulus   0.956 GPa
@Strain 4.91 %,
Temperature 80.0 °C		 139 ksi
@Strain 4.91 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  1.09 GPa
@Strain 5.67 %,
Temperature 80.0 °C		 158 ksi
@Strain 5.67 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.25 GPa
@Strain 5.03 %,
Temperature 40.0 °C		 181 ksi
@Strain 5.03 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  1.32 GPa
@Strain 3.12 %,
Temperature 80.0 °C		 192 ksi
@Strain 3.12 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  1.46 GPa
@Strain 4.95 %,
Temperature 23.0 °C		 212 ksi
@Strain 4.95 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  1.54 GPa
@Strain 3.44 %,
Temperature 80.0 °C		 223 ksi
@Strain 3.44 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.72 GPa
@Strain 1.60 %,
Temperature 80.0 °C		 250 ksi
@Strain 1.60 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  1.7682 GPa
@Strain 3.05 %,
Temperature 40.0 °C		 256.46 ksi
@Strain 3.05 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  2.028 GPa
@Strain 1.50 %,
Temperature 80.0 °C		 294.1 ksi
@Strain 1.50 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  2.08 GPa
@Strain 2.95 %,
Temperature 23.0 °C		 302 ksi
@Strain 2.95 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2.18 GPa
@Strain 0.470 %,
Temperature 80.0 °C		 316 ksi
@Strain 0.470 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2.24 GPa
@Strain 1.49 %,
Temperature 40.0 °C		 325 ksi
@Strain 1.49 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  2.3381 GPa
@Strain 0.210 %,
Temperature 80.0 °C		 339.12 ksi
@Strain 0.210 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  2.61 GPa
@Strain 1.43 %,
Temperature 23.0 °C		 379 ksi
@Strain 1.43 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2.66 GPa
@Strain 0.270 %,
Temperature 40.0 °C		 386 ksi
@Strain 0.270 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  3.04 GPa
@Strain 0.250 %,
Temperature 23.0 °C		 441 ksi
@Strain 0.250 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.13 GPa
@Strain 3.53 %,
Temperature 40.0 °C		 454 ksi
@Strain 3.53 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  3.39 GPa
@Strain 2.70 %,
Temperature 0.000 °C		 492 ksi
@Strain 2.70 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  3.85 GPa
@Strain 3.68 %,
Temperature -20.0 °C		 558 ksi
@Strain 3.68 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  4.01 GPa
@Strain 3.44 %,
Temperature 23.0 °C		 581 ksi
@Strain 3.44 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  4.18 GPa
@Strain 2.30 %,
Temperature 40.0 °C		 607 ksi
@Strain 2.30 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  4.4553 GPa
@Strain 1.32 %,
Temperature 0.000 °C		 646.20 ksi
@Strain 1.32 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  4.65 GPa
@Strain 3.20 %,
Temperature 0.000 °C		 674 ksi
@Strain 3.20 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  4.83 GPa
@Strain 2.60 %,
Temperature -20.0 °C		 700 ksi
@Strain 2.60 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  4.89 GPa
@Strain 1.44 %,
Temperature 40.0 °C		 709 ksi
@Strain 1.44 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  4.93 GPa
@Strain 2.45 %,
Temperature 23.0 °C		 714 ksi
@Strain 2.45 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.11 GPa
@Strain 0.330 %,
Temperature 0.000 °C		 741 ksi
@Strain 0.330 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.13 GPa
@Strain 2.55 %,
Temperature 0.000 °C		 744 ksi
@Strain 2.55 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.14 GPa
@Strain 2.85 %,
Temperature -20.0 °C		 746 ksi
@Strain 2.85 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  5.26 GPa
@Strain 0.810 %,
Temperature 40.0 °C		 763 ksi
@Strain 0.810 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  5.42 GPa
@Strain 1.74 %,
Temperature 23.0 °C		 786 ksi
@Strain 1.74 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.47 GPa
@Strain 3.20 %,
Temperature -40.0 °C		 793 ksi
@Strain 3.20 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  5.52 GPa
@Strain 1.94 %,
Temperature 0.000 °C		 801 ksi
@Strain 1.94 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.56 GPa
@Strain 2.20 %,
Temperature -20.0 °C		 806 ksi
@Strain 2.20 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  5.76 GPa
@Strain 1.10 %,
Temperature 23.0 °C		 836 ksi
@Strain 1.10 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.78 GPa
@Strain 1.46 %,
Temperature 0.000 °C		 838 ksi
@Strain 1.46 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.83 GPa
@Strain 1.69 %,
Temperature -20.0 °C		 846 ksi
@Strain 1.69 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  5.8325 GPa
@Strain 1.60 %,
Temperature -20.0 °C		 845.95 ksi
@Strain 1.60 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  6.33 GPa
@Strain 0.900 %,
Temperature -20.0 °C		 918 ksi
@Strain 0.900 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  6.64 GPa
@Strain 1.60 %,
Temperature -40.0 °C		 963 ksi
@Strain 1.60 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  7.24 GPa
@Strain 0.400 %,
Temperature -40.0 °C		 1050 ksi
@Strain 0.400 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
Izod Impact, Notched (ISO)  6.00 kJ/m² 2.86 ft-lb/in² DAM; ISO 180/1A
  12.0 kJ/m² 5.71 ft-lb/in² 50%RH; ISO 180/1A
  5.00 kJ/m²
@Temperature -30.0 °C		 2.38 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
  5.00 kJ/m²
@Temperature -40.0 °C		 2.38 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)  45.0 kJ/m² 21.4 ft-lb/in² DAM; ISO 180/1U
  40.0 kJ/m²
@Temperature -40.0 °C		 19.0 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1U
Charpy Impact Unnotched  5.00 J/cm² 23.8 ft-lb/in² DAM; ISO 179/1eU
  9.50 J/cm² 45.2 ft-lb/in² 50%RH; ISO 179/1eU
  4.50 J/cm²
@Temperature -30.0 °C		 21.4 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
  5.40 J/cm²
@Temperature -30.0 °C		 25.7 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
Charpy Impact, Notched  0.700 J/cm² 3.33 ft-lb/in² DAM; ISO 179/1eA
  1.50 J/cm² 7.14 ft-lb/in² 50%RH; ISO 179/1eA
  0.600 J/cm²
@Temperature -30.0 °C		 2.86 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
  0.600 J/cm²
@Temperature -40.0 °C		 2.86 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 179/1eA
  1.40 J/cm²
@Temperature -30.0 °C		 6.66 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  37.0 µm/m-°C 20.6 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  109 µm/m-°C 60.6 µin/in-°F DAM; ISO 11359-1/-2
Specific Heat Capacity  2.47 J/g-°C 0.590 BTU/lb-°F  
Thermal Conductivity  0.190 W/m-K 1.32 BTU-in/hr-ft²-°F of melt
Melting Point  221 °C 430 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  220 °C 428 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  200 °C 392 °F DAM; ISO 75-1/-2
Vicat Softening Point  215 °C 419 °F DAM; 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
Flame Spread  25 mm/min
@Thickness 1.00 mm		 0.98 in/min
@Thickness 0.0394 in		 DS; Burning Rate; ISO 3795 (FMVSS 302)
Oxygen Index  21 % 21 % DAM; ISO 4589-1/-2
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Emission of organic compounds 8.5 µgC/g VDA 277; DS
Odour class 4 VDA 270; DS
Part Marking Code >PA6-GF15< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA6-GF15  
UL recognition UL DAM

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39806.html

免责声明: 本文 PA6/美国杜邦/73G15L NC010 增强级 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4