  4. PA6美国杜邦73G30HSL NC010阻燃 耐磨 耐高温

PA6美国杜邦73G30HSL NC010阻燃 耐磨 耐高温

PA6/美国杜邦/73G30HSL NC010 阻燃 耐磨 耐高温
 参考图片：

颗粒图片：

包装图片：

成品图片：
images (37)

 

 

 
Physical Properties Metric English Comments
Density  1.20 g/cc 0.0434 lb/in³  
  1.36 g/cc 0.0491 lb/in³ DAM; ISO 1183
Water Absorption  6.3 %
@Thickness 2.00 mm		 6.3 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  1.90 %
@Thickness 2.00 mm		 1.90 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Viscosity   79560 cP
@Shear Rate 5000 1/s,
Temperature 280 °C		 79560 cP
@Shear Rate 5000 1/s,
Temperature 536 °F		 ISO 11403-1 -2
  94020 cP
@Shear Rate 5000 1/s,
Temperature 270 °C		 94020 cP
@Shear Rate 5000 1/s,
Temperature 518 °F		 ISO 11403-1 -2
  112700 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 112700 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  269600 cP
@Shear Rate 500 1/s,
Temperature 280 °C		 269600 cP
@Shear Rate 500 1/s,
Temperature 536 °F		 ISO 11403-1 -2
  326300 cP
@Shear Rate 500 1/s,
Temperature 270 °C		 326300 cP
@Shear Rate 500 1/s,
Temperature 518 °F		 ISO 11403-1 -2
  398300 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 398300 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  747100 cP
@Shear Rate 10.0 1/s,
Temperature 280 °C		 747100 cP
@Shear Rate 10.0 1/s,
Temperature 536 °F		 ISO 11403-1 -2
  1.061e+6 cP
@Shear Rate 10.0 1/s,
Temperature 270 °C		 1.061e+6 cP
@Shear Rate 10.0 1/s,
Temperature 518 °F		 ISO 11403-1 -2
  1.538e+6 cP
@Shear Rate 10.0 1/s,
Temperature 260 °C		 1.538e+6 cP
@Shear Rate 10.0 1/s,
Temperature 500 °F		 ISO 11403-1 -2
Viscosity Test  150 cm³/g 150 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0020 cm/cm 0.0020 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0060 cm/cm 0.0060 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  115 MPa 16700 psi 50%RH; ISO 527-1/-2
  185 MPa 26800 psi DAM; ISO 527-1/-2
Tensile Stress   4.15 MPa
@Strain 0.120 %,
Temperature 150 °C		 602 psi
@Strain 0.120 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  10.82 MPa
@Strain 0.260 %,
Temperature 90.0 °C		 1569 psi
@Strain 0.260 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  12.61 MPa
@Strain 0.370 %,
Temperature 150 °C		 1829 psi
@Strain 0.370 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  13.18 MPa
@Strain 0.440 %,
Temperature 150 °C		 1912 psi
@Strain 0.440 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  18.6 MPa
@Strain 0.340 %,
Temperature 40.0 °C		 2700 psi
@Strain 0.340 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  19.37 MPa
@Strain 0.450 %,
Temperature 90.0 °C		 2809 psi
@Strain 0.450 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  20.57 MPa
@Strain 0.310 %,
Temperature 23.0 °C		 2983 psi
@Strain 0.310 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  26.93 MPa
@Strain 1.22 %,
Temperature 150 °C		 3906 psi
@Strain 1.22 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  31.46 MPa
@Strain 0.920 %,
Temperature 90.0 °C		 4563 psi
@Strain 0.920 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  31.71 MPa
@Strain 1.26 %,
Temperature 150 °C		 4599 psi
@Strain 1.26 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  34.13 MPa
@Strain 0.390 %,
Temperature 0.000 °C		 4950 psi
@Strain 0.390 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  37.71 MPa
@Strain 2.35 %,
Temperature 150 °C		 5469 psi
@Strain 2.35 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  47.3 MPa
@Strain 1.36 %,
Temperature 90.0 °C		 6860 psi
@Strain 1.36 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  47.67 MPa
@Strain 2.58 %,
Temperature 150 °C		 6914 psi
@Strain 2.58 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  48.97 MPa
@Strain 1.09 %,
Temperature 40.0 °C		 7103 psi
@Strain 1.09 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  51.29 MPa
@Strain 1.94 %,
Temperature 90.0 °C		 7439 psi
@Strain 1.94 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  54.04 MPa
@Strain 0.930 %,
Temperature 23.0 °C		 7838 psi
@Strain 0.930 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  59.25 MPa
@Strain 4.18 %,
Temperature 150 °C		 8594 psi
@Strain 4.18 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  61.95 MPa
@Strain 0.700 %,
Temperature 40.0 °C		 8985 psi
@Strain 0.700 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  66.51 MPa
@Strain 3.29 %,
Temperature 90.0 °C		 9646 psi
@Strain 3.29 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  71.64 MPa
@Strain 2.62 %,
Temperature 90.0 °C		 10390 psi
@Strain 2.62 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  74.12 MPa
@Strain 0.750 %,
Temperature 23.0 °C		 10750 psi
@Strain 0.750 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  76.43 MPa
@Strain 2.13 %,
Temperature 40.0 °C		 11090 psi
@Strain 2.13 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  76.74 MPa
@Strain 0.940 %,
Temperature 0.000 °C		 11130 psi
@Strain 0.940 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  85.37 MPa
@Strain 1.82 %,
Temperature 23.0 °C		 12380 psi
@Strain 1.82 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  89.11 MPa
@Strain 4.20 %,
Temperature 90.0 °C		 12920 psi
@Strain 4.20 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  90.29 MPa
@Strain 0.910 %,
Temperature -20.0 °C		 13100 psi
@Strain 0.910 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  96.2 MPa
@Strain 3.47 %,
Temperature 40.0 °C		 14000 psi
@Strain 3.47 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  105.04 MPa
@Strain 1.01 %,
Temperature -40.0 °C		 15235 psi
@Strain 1.01 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  108.03 MPa
@Strain 1.38 %,
Temperature 40.0 °C		 15668 psi
@Strain 1.38 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  109.8 MPa
@Strain 1.05 %,
Temperature -40.0 °C		 15930 psi
@Strain 1.05 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  110.62 MPa
@Strain 2.91 %,
Temperature 23.0 °C		 16044 psi
@Strain 2.91 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  112 MPa
@Strain 1.13 %,
Temperature 0.000 °C		 16200 psi
@Strain 1.13 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  116.22 MPa
@Strain 1.61 %,
Temperature 0.000 °C		 16856 psi
@Strain 1.61 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  129 MPa
@Strain 1.29 %,
Temperature -20.0 °C		 18700 psi
@Strain 1.29 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  129.21 MPa
@Strain 1.47 %,
Temperature 23.0 °C		 18740 psi
@Strain 1.47 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  146.3 MPa
@Strain 2.38 %,
Temperature 40.0 °C		 21220 psi
@Strain 2.38 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  149.5 MPa
@Strain 2.46 %,
Temperature 0.000 °C		 21680 psi
@Strain 2.46 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  151.47 MPa
@Strain 1.74 %,
Temperature -20.0 °C		 21969 psi
@Strain 1.74 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  155.94 MPa
@Strain 1.69 %,
Temperature 0.000 °C		 22617 psi
@Strain 1.69 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  162.42 MPa
@Strain 1.71 %,
Temperature -40.0 °C		 23557 psi
@Strain 1.71 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  177.89 MPa
@Strain 2.47 %,
Temperature 23.0 °C		 25801 psi
@Strain 2.47 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  182.47 MPa
@Strain 1.97 %,
Temperature -40.0 °C		 26465 psi
@Strain 1.97 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  190.65 MPa
@Strain 2.57 %,
Temperature -20.0 °C		 27651 psi
@Strain 2.57 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  191.45 MPa
@Strain 2.13 %,
Temperature -20.0 °C		 27768 psi
@Strain 2.13 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  205.87 MPa
@Strain 2.72 %,
Temperature 0.000 °C		 29859 psi
@Strain 2.72 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  212.72 MPa
@Strain 2.53 %,
Temperature -40.0 °C		 30852 psi
@Strain 2.53 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  214.97 MPa
@Strain 3.85 %,
Temperature -20.0 °C		 31179 psi
@Strain 3.85 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  227.37 MPa
@Strain 2.70 %,
Temperature -40.0 °C		 32977 psi
@Strain 2.70 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  247.74 MPa
@Strain 3.61 %,
Temperature -40.0 °C		 35932 psi
@Strain 3.61 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  251.68 MPa
@Strain 3.30 %,
Temperature -20.0 °C		 36503 psi
@Strain 3.30 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
Elongation at Break  3.5 % 3.5 % DAM; ISO 527-1/-2
  6.0 % 6.0 % 50%RH; ISO 527-1/-2
Tensile Modulus  5.80 GPa 841 ksi 50%RH; ISO 527-1/-2
  9.70 GPa 1410 ksi DAM; ISO 527-1/-2
  2.968 GPa
@Temperature 120 °C		 430.5 ksi
@Temperature 248 °F		 50%RH; ISO 11403-1 -2
  3.15 GPa
@Temperature 170 °C		 456 ksi
@Temperature 338 °F		 50%RH; Dynamic; ISO 11403-1 -2
  3.77 GPa
@Temperature 110 °C		 547 ksi
@Temperature 230 °F		 50%RH; Dynamic; ISO 11403-1 -2
  3.912 GPa
@Temperature 120 °C		 567.4 ksi
@Temperature 248 °F		 DAM; ISO 11403-1 -2
  5.152 GPa
@Temperature 40.0 °C		 747.2 ksi
@Temperature 104 °F		 50%RH; ISO 11403-1 -2
  5.65 GPa
@Temperature 30.0 °C		 820 ksi
@Temperature 86.0 °F		 50%RH; Dynamic; ISO 11403-1 -2
  8.40 GPa
@Temperature -20.0 °C		 1220 ksi
@Temperature -4.00 °F		 50%RH; Dynamic; ISO 11403-1 -2
  8.647 GPa
@Temperature 40.0 °C		 1254 ksi
@Temperature 104 °F		 DAM; ISO 11403-1 -2
  9.17 GPa
@Temperature -70.0 °C		 1330 ksi
@Temperature -94.0 °F		 50%RH; Dynamic; ISO 11403-1 -2
  9.45 GPa
@Temperature -100 °C		 1370 ksi
@Temperature -148 °F		 50%RH; Dynamic; ISO 11403-1 -2
  10.874 GPa
@Temperature -40.0 °C		 1577.1 ksi
@Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  11.871 GPa
@Temperature -40.0 °C		 1721.7 ksi
@Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Shear Strength   0.007471 MPa
@Shear Rate 10.0 1/s,
Temperature 280 °C		 1.084 psi
@Shear Rate 10.0 1/s,
Temperature 536 °F		 ISO 11403-1 -2
  0.01061 MPa
@Shear Rate 10.0 1/s,
Temperature 270 °C		 1.539 psi
@Shear Rate 10.0 1/s,
Temperature 518 °F		 ISO 11403-1 -2
  0.01538 MPa
@Shear Rate 10.0 1/s,
Temperature 260 °C		 2.230 psi
@Shear Rate 10.0 1/s,
Temperature 500 °F		 ISO 11403-1 -2
Secant Modulus   2.22 GPa
@Strain 4.65 %,
Temperature 40.0 °C		 321 ksi
@Strain 4.65 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  3.15 GPa
@Strain 3.86 %,
Temperature 23.0 °C		 457 ksi
@Strain 3.86 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.31 GPa
@Strain 2.54 %,
Temperature 40.0 °C		 480 ksi
@Strain 2.54 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  4.38 GPa
@Strain 2.16 %,
Temperature 23.0 °C		 635 ksi
@Strain 2.16 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.49 GPa
@Strain 1.09 %,
Temperature 40.0 °C		 652 ksi
@Strain 1.09 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  5.23 GPa
@Strain 3.19 %,
Temperature 0.000 °C		 758 ksi
@Strain 3.19 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.40 GPa
@Strain 2.88 %,
Temperature 40.0 °C		 783 ksi
@Strain 2.88 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  5.47 GPa
@Strain 0.340 %,
Temperature 40.0 °C		 793 ksi
@Strain 0.340 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  5.81 GPa
@Strain 0.930 %,
Temperature 23.0 °C		 843 ksi
@Strain 0.930 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  6.50 GPa
@Strain 2.93 %,
Temperature 23.0 °C		 943 ksi
@Strain 2.93 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  6.64 GPa
@Strain 0.310 %,
Temperature 23.0 °C		 962 ksi
@Strain 0.310 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  6.88 GPa
@Strain 3.17 %,
Temperature 0.000 °C		 997 ksi
@Strain 3.17 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  6.88 GPa
@Strain 1.86 %,
Temperature 0.000 °C		 998 ksi
@Strain 1.86 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  6.94 GPa
@Strain 2.91 %,
Temperature -20.0 °C		 1010 ksi
@Strain 2.91 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  7.83 GPa
@Strain 1.38 %,
Temperature 40.0 °C		 1140 ksi
@Strain 1.38 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  7.91 GPa
@Strain 2.84 %,
Temperature -40.0 °C		 1150 ksi
@Strain 2.84 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  8.0023 GPa
@Strain 3.04 %,
Temperature -40.0 °C		 1160.7 ksi
@Strain 3.04 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  8.16 GPa
@Strain 0.940 %,
Temperature 0.000 °C		 1180 ksi
@Strain 0.940 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  8.71 GPa
@Strain 1.74 %,
Temperature -20.0 °C		 1260 ksi
@Strain 1.74 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  8.75 GPa
@Strain 0.390 %,
Temperature 0.000 °C		 1270 ksi
@Strain 0.390 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  8.7898 GPa
@Strain 1.47 %,
Temperature 23.0 °C		 1274.9 ksi
@Strain 1.47 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  8.85 GPa
@Strain 0.700 %,
Temperature 40.0 °C		 1280 ksi
@Strain 0.700 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  8.99 GPa
@Strain 2.13 %,
Temperature -20.0 °C		 1300 ksi
@Strain 2.13 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  9.23 GPa
@Strain 1.69 %,
Temperature 0.000 °C		 1340 ksi
@Strain 1.69 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  9.26 GPa
@Strain 1.97 %,
Temperature -40.0 °C		 1340 ksi
@Strain 1.97 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  9.50 GPa
@Strain 1.71 %,
Temperature -40.0 °C		 1380 ksi
@Strain 1.71 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  9.88 GPa
@Strain 0.750 %,
Temperature 23.0 °C		 1430 ksi
@Strain 0.750 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  9.9115 GPa
@Strain 1.13 %,
Temperature 0.000 °C		 1437.6 ksi
@Strain 1.13 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  9.92 GPa
@Strain 0.910 %,
Temperature -20.0 °C		 1440 ksi
@Strain 0.910 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  10.0 GPa
@Strain 1.29 %,
Temperature -20.0 °C		 1450 ksi
@Strain 1.29 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  10.4 GPa
@Strain 1.01 %,
Temperature -40.0 °C		 1510 ksi
@Strain 1.01 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  10.5 GPa
@Strain 1.05 %,
Temperature -40.0 °C		 1520 ksi
@Strain 1.05 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  15.0 kJ/m² 7.14 ft-lb/in² DAM; ISO 180/1A
  20.0 kJ/m² 9.52 ft-lb/in² 50%RH; ISO 180/1A
  10.0 kJ/m²
@Temperature -30.0 °C		 4.76 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
  11.0 kJ/m²
@Temperature -30.0 °C		 5.23 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
Charpy Impact Unnotched  10.0 J/cm² 47.6 ft-lb/in² DAM; ISO 179/1eU
  10.0 J/cm² 47.6 ft-lb/in² 50%RH; ISO 179/1eU
  8.00 J/cm²
@Temperature -30.0 °C		 38.1 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
  8.00 J/cm²
@Temperature -30.0 °C		 38.1 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
Charpy Impact, Notched  1.60 J/cm² 7.61 ft-lb/in² DAM; ISO 179/1eA
  2.30 J/cm² 10.9 ft-lb/in² 50%RH; ISO 179/1eA
  1.00 J/cm²
@Temperature -30.0 °C		 4.76 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
  2.10 J/cm²
@Temperature -30.0 °C		 9.99 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
Puncture Energy  3.50 J 2.58 ft-lb DAM; ISO 6603-2
  6.50 J 4.79 ft-lb 50%RH; ISO 6603-2
Tensile Creep Modulus, 1 hour   1700 MPa
@Pressure 30.0 MPa,
Temperature 150 °C		 246000 psi
@Pressure 4350 psi,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  1770 MPa
@Pressure 25.0 MPa,
Temperature 150 °C		 256000 psi
@Pressure 3630 psi,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  1850 MPa
@Pressure 20.0 MPa,
Temperature 150 °C		 268000 psi
@Pressure 2900 psi,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  1900 MPa
@Pressure 15.0 MPa,
Temperature 150 °C		 276000 psi
@Pressure 2180 psi,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  1930 MPa
@Pressure 10.0 MPa,
Temperature 150 °C		 280000 psi
@Pressure 1450 psi,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  1940 MPa
@Pressure 5.00 MPa,
Temperature 150 °C		 281000 psi
@Pressure 725 psi,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  6190 MPa
@Time 3600 sec		 898000 psi
@Time 1.00 hour		 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours   1400 MPa
@Pressure 30.0 MPa,
Temperature 150 °C		 204000 psi
@Pressure 4350 psi,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  1480 MPa
@Pressure 25.0 MPa,
Temperature 150 °C		 214000 psi
@Pressure 3630 psi,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  1560 MPa
@Pressure 20.0 MPa,
Temperature 150 °C		 226000 psi
@Pressure 2900 psi,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  1620 MPa
@Pressure 15.0 MPa,
Temperature 150 °C		 235000 psi
@Pressure 2180 psi,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  1640 MPa
@Pressure 10.0 MPa,
Temperature 150 °C		 238000 psi
@Pressure 1450 psi,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  1650 MPa
@Pressure 5.00 MPa,
Temperature 150 °C		 239000 psi
@Pressure 725 psi,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  4630 MPa
@Time 3.60e+6 sec		 672000 psi
@Time 1000 hour		 50%RH; ISO 899-1
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  26.0 µm/m-°C 14.4 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  75.0 µm/m-°C 41.7 µin/in-°F DAM; ISO 11359-1/-2
  75.0 µm/m-°C
@Temperature -30.0 °C		 41.7 µin/in-°F
@Temperature -22.0 °F		 ISO 11403-1 -2
  105 µm/m-°C
@Temperature 45.0 °C		 58.3 µin/in-°F
@Temperature 113 °F		 ISO 11403-1 -2
  130 µm/m-°C
@Temperature 160 °C		 72.2 µin/in-°F
@Temperature 320 °F		 ISO 11403-1 -2
Specific Heat Capacity  2.28 J/g-°C 0.545 BTU/lb-°F  
Thermal Conductivity  0.260 W/m-K 1.80 BTU-in/hr-ft²-°F of melt
Melting Point  221 °C 430 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  220 °C 428 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  210 °C 410 °F DAM; ISO 75-1/-2
Vicat Softening Point  215 °C 419 °F DAM; 50°C/h 50N; ISO 306
Glass Transition Temp, Tg  65.0 °C 149 °F DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 DAM; IEC 60695-11-10
Flame Spread  50 mm/min
@Thickness 1.00 mm		 2.0 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
Oxygen Index  21 % 21 % DAM; DS; ISO 4589-1/-2
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Eff. thermal diffusivity 9.10E-08 m²/s  
Emission of organic compounds 8.5 µgC/g VDA 277
Part Marking Code >PA6-GF30< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA6-GF30  
Special characteristics Heat stabilised or stable to heat  
UL recognition UL DAM

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39810.html

免责声明: 本文 PA6美国杜邦73G30HSL NC010阻燃 耐磨 耐高温 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4