PA6/美国杜邦/73G30L NC010本色 耐磨 耐高温

尼龙PA6/美国杜邦/73G30L NC010 本色加纤30%增强 耐磨 耐高温
 参考图片：

颗粒图片：

包装图片：

成品图片：
images (5)
 

 

 

 

Physical Properties Metric English Comments
Density  1.36 g/cc 0.0491 lb/in³ DAM; ISO 1183
Water Absorption  6.3 %
@Thickness 2.00 mm		 6.3 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  1.90 %
@Thickness 2.00 mm		 1.90 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Viscosity Test  150 cm³/g 150 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0020 cm/cm 0.0020 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0060 cm/cm 0.0060 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  115 MPa 16700 psi 50%RH; ISO 527-1/-2
  185 MPa 26800 psi DAM; ISO 527-1/-2
Tensile Stress   5.50 MPa
@Strain 0.110036 %,
Time 36000 sec		 798 psi
@Strain 0.110036 %,
Time 10.0 hour		 50%RH; isochronous; ISO 11403-1 -2
  5.50 MPa
@Strain 0.0989091 %,
Time 3600 sec		 798 psi
@Strain 0.0989091 %,
Time 1.00 hour		 50%RH; isochronous; ISO 11403-1 -2
  5.50 MPa
@Strain 0.134764 %,
Time 3.60e+6 sec		 798 psi
@Strain 0.134764 %,
Time 1000 hour		 50%RH; isochronous; ISO 11403-1 -2
  5.50 MPa
@Strain 0.148364 %,
Time 3.60e+7 sec		 798 psi
@Strain 0.148364 %,
Time 10000 hour		 50%RH; isochronous; ISO 11403-1 -2
  5.50 MPa
@Strain 0.121164 %,
Time 360000 sec		 798 psi
@Strain 0.121164 %,
Time 100 hour		 50%RH; isochronous; ISO 11403-1 -2
  22.0 MPa
@Strain 0.531636 %,
Time 360000 sec		 3190 psi
@Strain 0.531636 %,
Time 100 hour		 50%RH; isochronous; ISO 11403-1 -2
  22.0 MPa
@Strain 0.635491 %,
Time 3.60e+7 sec		 3190 psi
@Strain 0.635491 %,
Time 10000 hour		 50%RH; isochronous; ISO 11403-1 -2
  22.0 MPa
@Strain 0.582327 %,
Time 3.60e+6 sec		 3190 psi
@Strain 0.582327 %,
Time 1000 hour		 50%RH; isochronous; ISO 11403-1 -2
  22.0 MPa
@Strain 0.433964 %,
Time 3600 sec		 3190 psi
@Strain 0.433964 %,
Time 1.00 hour		 50%RH; isochronous; ISO 11403-1 -2
  22.0 MPa
@Strain 0.480945 %,
Time 36000 sec		 3190 psi
@Strain 0.480945 %,
Time 10.0 hour		 50%RH; isochronous; ISO 11403-1 -2
  44.0 MPa
@Strain 1.27345 %,
Time 36000 sec		 6380 psi
@Strain 1.27345 %,
Time 10.0 hour		 50%RH; isochronous; ISO 11403-1 -2
  44.0 MPa
@Time 3600 sec,
Strain 1.15971 %		 6380 psi
@Time 1.00 hour,
Strain 1.15971 %		 50%RH; isochronous; ISO 11403-1 -2
  44.0 MPa
@Strain 1.48364 %,
Time 3.60e+6 sec		 6380 psi
@Strain 1.48364 %,
Time 1000 hour		 50%RH; isochronous; ISO 11403-1 -2
  44.0 MPa
@Strain 1.58255 %,
Time 3.60e+7 sec		 6380 psi
@Strain 1.58255 %,
Time 10000 hour		 50%RH; isochronous; ISO 11403-1 -2
  44.0 MPa
@Strain 1.38473 %,
Time 360000 sec		 6380 psi
@Strain 1.38473 %,
Time 100 hour		 50%RH; isochronous; ISO 11403-1 -2
Elongation at Break  3.5 % 3.5 % DAM; ISO 527-1/-2
  6.0 % 6.0 % 50%RH; ISO 527-1/-2
Tensile Modulus  6.00 GPa 870 ksi 50%RH; ISO 527-1/-2
  9.80 GPa 1420 ksi DAM; ISO 527-1/-2
Flexural Modulus  8.20 GPa 1190 ksi DAM; ISO 178
Shear Modulus  0.586 GPa
@Temperature 160 °C		 85.0 ksi
@Temperature 320 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.6285 GPa
@Temperature 120 °C		 91.16 ksi
@Temperature 248 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.817 GPa
@Temperature 70.0 °C		 118 ksi
@Temperature 158 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.857 GPa
@Temperature 20.0 °C		 269.3 ksi
@Temperature 68.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.975 GPa
@Temperature -20.0 °C		 286.5 ksi
@Temperature -4.00 °F		 DAM; Dynamic; ISO 11403-1 -2
  2.081 GPa
@Temperature -50.0 °C		 301.8 ksi
@Temperature -58.0 °F		 DAM; Dynamic; ISO 11403-1 -2
Izod Impact, Notched (ISO)  15.0 kJ/m² 7.14 ft-lb/in² DAM; ISO 180/1A
  20.0 kJ/m² 9.52 ft-lb/in² 50%RH; ISO 180/1A
  11.0 kJ/m²
@Temperature -30.0 °C		 5.23 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
  11.0 kJ/m²
@Temperature -30.0 °C		 5.23 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
  11.0 kJ/m²
@Temperature -40.0 °C		 5.23 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)  100 kJ/m² 47.6 ft-lb/in² DAM; ISO 180/1U
  90.0 kJ/m²
@Temperature -30.0 °C		 42.8 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1U
Charpy Impact Unnotched  9.70 J/cm² 46.2 ft-lb/in² 50%RH; ISO 179/1eU
  10.0 J/cm² 47.6 ft-lb/in² DAM; ISO 179/1eU
  8.00 J/cm²
@Temperature -30.0 °C		 38.1 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
  8.40 J/cm²
@Temperature -30.0 °C		 40.0 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
Charpy Impact, Notched  1.60 J/cm² 7.61 ft-lb/in² DAM; ISO 179/1eA
  2.30 J/cm² 10.9 ft-lb/in² 50%RH; ISO 179/1eA
  1.10 J/cm²
@Temperature -30.0 °C		 5.23 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
  1.10 J/cm²
@Temperature -40.0 °C		 5.23 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 179/1eA
  2.10 J/cm²
@Temperature -30.0 °C		 9.99 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour   2590 MPa
@Pressure 30.0 MPa,
Temperature 100 °C		 375000 psi
@Pressure 4350 psi,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2690 MPa
@Pressure 25.0 MPa,
Temperature 100 °C		 391000 psi
@Pressure 3630 psi,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2816.9 MPa
@Pressure 20.0 MPa,
Temperature 100 °C		 408560 psi
@Pressure 2900 psi,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2900 MPa
@Pressure 15.0 MPa,
Temperature 100 °C		 421000 psi
@Pressure 2180 psi,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2940 MPa
@Pressure 10.0 MPa,
Temperature 100 °C		 427000 psi
@Pressure 1450 psi,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2960 MPa
@Pressure 5.00 MPa,
Temperature 100 °C		 429000 psi
@Pressure 725 psi,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  3110 MPa
@Pressure 55.0 MPa,
Temperature 23.0 °C		 451000 psi
@Pressure 7980 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3420 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 496000 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3640 MPa
@Pressure 36.0 MPa,
Temperature 90.0 °C		 527000 psi
@Pressure 5220 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  3680 MPa
@Pressure 35.0 MPa,
Temperature 90.0 °C		 534000 psi
@Pressure 5080 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  3850 MPa
@Pressure 60.0 MPa,
Temperature 60.0 °C		 558000 psi
@Pressure 8700 psi,
Temperature 140 °F		 DAM; ISO 11403-1 -2
  3919.9 MPa
@Pressure 30.0 MPa,
Temperature 90.0 °C		 568530 psi
@Pressure 4350 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  3950 MPa
@Pressure 50.0 MPa,
Temperature 60.0 °C		 573000 psi
@Pressure 7250 psi,
Temperature 140 °F		 DAM; ISO 11403-1 -2
  4010 MPa
@Pressure 40.0 MPa,
Temperature 60.0 °C		 582000 psi
@Pressure 5800 psi,
Temperature 140 °F		 DAM; ISO 11403-1 -2
  4050 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 587000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4070 MPa
@Pressure 30.0 MPa,
Temperature 60.0 °C		 590000 psi
@Pressure 4350 psi,
Temperature 140 °F		 DAM; ISO 11403-1 -2
  4080 MPa
@Pressure 25.0 MPa,
Temperature 90.0 °C		 592000 psi
@Pressure 3630 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  4120 MPa
@Pressure 20.0 MPa,
Temperature 90.0 °C		 597000 psi
@Pressure 2900 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  4130 MPa
@Pressure 15.0 MPa,
Temperature 90.0 °C		 598000 psi
@Pressure 2180 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  4140 MPa
@Pressure 5.00 MPa,
Temperature 90.0 °C		 600000 psi
@Pressure 725 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  4140 MPa
@Pressure 10.0 MPa,
Temperature 90.0 °C		 601000 psi
@Pressure 1450 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  4330 MPa
@Pressure 20.0 MPa,
Temperature 60.0 °C		 628000 psi
@Pressure 2900 psi,
Temperature 140 °F		 DAM; ISO 11403-1 -2
  4610 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 669000 psi
@Pressure 1450 psi,
Temperature 140 °F		 DAM; ISO 11403-1 -2
  4640 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 673000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  5160 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 748000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  5480 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 795000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  5500 MPa
@Time 3600 sec		 798000 psi
@Time 1.00 hour		 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours   2140 MPa
@Pressure 30.0 MPa,
Temperature 100 °C		 311000 psi
@Pressure 4350 psi,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2250 MPa
@Pressure 25.0 MPa,
Temperature 100 °C		 327000 psi
@Pressure 3630 psi,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2380 MPa
@Pressure 20.0 MPa,
Temperature 100 °C		 345000 psi
@Pressure 2900 psi,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2470 MPa
@Pressure 15.0 MPa,
Temperature 100 °C		 358000 psi
@Pressure 2180 psi,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2500 MPa
@Pressure 10.0 MPa,
Temperature 100 °C		 363000 psi
@Pressure 1450 psi,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2510 MPa
@Pressure 5.00 MPa,
Temperature 100 °C		 364000 psi
@Pressure 725 psi,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2510 MPa
@Pressure 55.0 MPa,
Temperature 23.0 °C		 365000 psi
@Pressure 7980 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2530 MPa
@Pressure 60.0 MPa,
Temperature 60.0 °C		 367000 psi
@Pressure 8700 psi,
Temperature 140 °F		 DAM; ISO 11403-1 -2
  2620 MPa
@Pressure 50.0 MPa,
Temperature 60.0 °C		 380000 psi
@Pressure 7250 psi,
Temperature 140 °F		 DAM; ISO 11403-1 -2
  2720 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 395000 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2730 MPa
@Pressure 36.0 MPa,
Temperature 90.0 °C		 396000 psi
@Pressure 5220 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  2730 MPa
@Pressure 35.0 MPa,
Temperature 90.0 °C		 396000 psi
@Pressure 5080 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  2760 MPa
@Pressure 40.0 MPa,
Temperature 60.0 °C		 400000 psi
@Pressure 5800 psi,
Temperature 140 °F		 DAM; ISO 11403-1 -2
  2760 MPa
@Pressure 30.0 MPa,
Temperature 90.0 °C		 401000 psi
@Pressure 4350 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  2800 MPa
@Pressure 25.0 MPa,
Temperature 90.0 °C		 405000 psi
@Pressure 3630 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  2820 MPa
@Pressure 20.0 MPa,
Temperature 90.0 °C		 408000 psi
@Pressure 2900 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  2830 MPa
@Pressure 15.0 MPa,
Temperature 90.0 °C		 411000 psi
@Pressure 2180 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  2850 MPa
@Pressure 10.0 MPa,
Temperature 90.0 °C		 413000 psi
@Pressure 1450 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  2860 MPa
@Pressure 5.00 MPa,
Temperature 90.0 °C		 415000 psi
@Pressure 725 psi,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  2928 MPa
@Pressure 30.0 MPa,
Temperature 60.0 °C		 424700 psi
@Pressure 4350 psi,
Temperature 140 °F		 DAM; ISO 11403-1 -2
  3050 MPa
@Pressure 20.0 MPa,
Temperature 60.0 °C		 443000 psi
@Pressure 2900 psi,
Temperature 140 °F		 DAM; ISO 11403-1 -2
  3130 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 455000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3130 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 455000 psi
@Pressure 1450 psi,
Temperature 140 °F		 DAM; ISO 11403-1 -2
  3517.5 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 510170 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3830 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 556000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4040 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 586000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4400 MPa
@Time 3.60e+6 sec		 638000 psi
@Time 1000 hour		 50%RH; ISO 899-1
 
Electrical Properties Metric English Comments
Comparative Tracking Index  600 V 600 V DAM; IEC 60112
  >= 600 V >= 600 V DAM; UL 746A
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  14.0 µm/m-°C 7.78 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  102 µm/m-°C 56.7 µin/in-°F DAM; ISO 11359-1/-2
Melting Point  221 °C 430 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  220 °C 428 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  210 °C 410 °F DAM; ISO 75-1/-2
Glass Transition Temp, Tg  65.0 °C 149 °F DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 DAM; IEC 60695-11-10
Flame Spread  25 mm/min
@Thickness 1.00 mm		 0.98 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
Oxygen Index  21 % 21 % DAM; ISO 4589-1/-2
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Part Marking Code >PA6-GF30< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA6-GF30  
UL recognition UL DAM

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39811.html

免责声明: 本文 PA6/美国杜邦/73G30L NC010本色 耐磨 耐高温 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4