PA612/美国杜邦/77G43L NC010注塑级 稳定性

PA612/美国杜邦/77G43L NC010 注塑级 稳定性
 参考图片：

颗粒图片：

包装图片：

成品图片：
images (33)

 

 

 
Physical Properties Metric English Comments
Density  1.42 g/cc 0.0513 lb/in³ DAM; ISO 1183
Water Absorption  1.7 %
@Thickness 2.00 mm		 1.7 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  0.700 %
@Thickness 2.00 mm		 0.700 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Viscosity Test  145 cm³/g 145 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0080 cm/cm 0.0080 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Hardness, Rockwell R  118 118 DAM; ISO 2039-2
Tensile Strength at Break  165 MPa 23900 psi 50%RH; ISO 527-1/-2
  200 MPa 29000 psi DAM; ISO 527-1/-2
Tensile Stress   11.65 MPa
@Strain 0.230 %,
Temperature 150 °C		 1690 psi
@Strain 0.230 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  12.11 MPa
@Strain 0.220 %,
Temperature 150 °C		 1756 psi
@Strain 0.220 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  18.25 MPa
@Strain 0.220 %,
Temperature 90.0 °C		 2647 psi
@Strain 0.220 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  18.81 MPa
@Strain 0.240 %,
Temperature 90.0 °C		 2728 psi
@Strain 0.240 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  23.06 MPa
@Strain 0.220 %,
Temperature 40.0 °C		 3345 psi
@Strain 0.220 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  25.22 MPa
@Strain 0.230 %,
Temperature 40.0 °C		 3658 psi
@Strain 0.230 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  28.59 MPa
@Strain 0.670 %,
Temperature 150 °C		 4147 psi
@Strain 0.670 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  33.27 MPa
@Strain 0.230 %,
Temperature 23.0 °C		 4825 psi
@Strain 0.230 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  34.16 MPa
@Strain 0.230 %,
Temperature 0.000 °C		 4954 psi
@Strain 0.230 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  38.37 MPa
@Strain 0.910 %,
Temperature 150 °C		 5565 psi
@Strain 0.910 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  38.78 MPa
@Strain 0.540 %,
Temperature 90.0 °C		 5625 psi
@Strain 0.540 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  40.89 MPa
@Strain 0.410 %,
Temperature 40.0 °C		 5931 psi
@Strain 0.410 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  41.15 MPa
@Strain 0.340 %,
Temperature 23.0 °C		 5968 psi
@Strain 0.340 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  42.43 MPa
@Strain 1.26 %,
Temperature 150 °C		 6154 psi
@Strain 1.26 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  44.21 MPa
@Strain 0.330 %,
Temperature 0.000 °C		 6412 psi
@Strain 0.330 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  45.35 MPa
@Strain 0.640 %,
Temperature 90.0 °C		 6577 psi
@Strain 0.640 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  53.67 MPa
@Strain 2.05 %,
Temperature 150 °C		 7784 psi
@Strain 2.05 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  59.11 MPa
@Strain 1.98 %,
Temperature 150 °C		 8573 psi
@Strain 1.98 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  59.5 MPa
@Strain 0.960 %,
Temperature 90.0 °C		 8630 psi
@Strain 0.960 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  59.61 MPa
@Strain 0.580 %,
Temperature 40.0 °C		 8646 psi
@Strain 0.580 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  66.9 MPa
@Strain 0.420 %,
Temperature -40.0 °C		 9700 psi
@Strain 0.420 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  71.96 MPa
@Strain 0.820 %,
Temperature 40.0 °C		 10440 psi
@Strain 0.820 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  72.96 MPa
@Strain 0.660 %,
Temperature 23.0 °C		 10580 psi
@Strain 0.660 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  73.4 MPa
@Strain 3.36 %,
Temperature 150 °C		 10600 psi
@Strain 3.36 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  74.39 MPa
@Strain 0.560 %,
Temperature 23.0 °C		 10790 psi
@Strain 0.560 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  76.78 MPa
@Strain 0.550 %,
Temperature 0.000 °C		 11140 psi
@Strain 0.550 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  77.36 MPa
@Strain 1.35 %,
Temperature 90.0 °C		 11220 psi
@Strain 1.35 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  79.92 MPa
@Strain 0.630 %,
Temperature 0.000 °C		 11590 psi
@Strain 0.630 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  80.08 MPa
@Strain 1.55 %,
Temperature 90.0 °C		 11610 psi
@Strain 1.55 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  100.88 MPa
@Strain 1.16 %,
Temperature 40.0 °C		 14631 psi
@Strain 1.16 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  101.31 MPa
@Strain 1.34 %,
Temperature 40.0 °C		 14694 psi
@Strain 1.34 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  101.76 MPa
@Strain 2.22 %,
Temperature 90.0 °C		 14759 psi
@Strain 2.22 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  102.71 MPa
@Strain 0.730 %,
Temperature -40.0 °C		 14897 psi
@Strain 0.730 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  103.38 MPa
@Strain 1.03 %,
Temperature 23.0 °C		 14994 psi
@Strain 1.03 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  115.95 MPa
@Strain 0.970 %,
Temperature 0.000 °C		 16817 psi
@Strain 0.970 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  122.2 MPa
@Strain 1.02 %,
Temperature 23.0 °C		 17720 psi
@Strain 1.02 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  126 MPa
@Strain 0.990 %,
Temperature 0.000 °C		 18300 psi
@Strain 0.990 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  129.98 MPa
@Strain 1.47 %,
Temperature 23.0 °C		 18852 psi
@Strain 1.47 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  130.54 MPa
@Strain 0.870 %,
Temperature -40.0 °C		 18933 psi
@Strain 0.870 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  135.21 MPa
@Strain 1.83 %,
Temperature 40.0 °C		 19611 psi
@Strain 1.83 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  141.03 MPa
@Strain 1.05 %,
Temperature -40.0 °C		 20455 psi
@Strain 1.05 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  149.29 MPa
@Strain 1.35 %,
Temperature 0.000 °C		 21653 psi
@Strain 1.35 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  161.61 MPa
@Strain 1.55 %,
Temperature 23.0 °C		 23440 psi
@Strain 1.55 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  174.83 MPa
@Strain 1.52 %,
Temperature 0.000 °C		 25357 psi
@Strain 1.52 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  175.37 MPa
@Strain 1.39 %,
Temperature -40.0 °C		 25435 psi
@Strain 1.39 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  183.58 MPa
@Strain 1.34 %,
Temperature -40.0 °C		 26626 psi
@Strain 1.34 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  234.23 MPa
@Strain 1.92 %,
Temperature -40.0 °C		 33972 psi
@Strain 1.92 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  10.0 MPa
@Strain 0.107 %,
Time 3600 sec		 1450 psi
@Strain 0.107 %,
Time 1.00 hour		 50%RH; isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.119 %,
Time 360000 sec		 1450 psi
@Strain 0.119 %,
Time 100 hour		 50%RH; isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.133 %,
Time 3.60e+6 sec		 1450 psi
@Strain 0.133 %,
Time 1000 hour		 50%RH; isochronous; ISO 11403-1 -2
  10.0 MPa
@Time 360 sec,
Strain 0.102 %		 1450 psi
@Time 0.100 hour,
Strain 0.102 %		 50%RH; isochronous; ISO 11403-1 -2
Elongation at Break  3.0 % 3.0 % DAM; ISO 527-1/-2
  5.0 % 5.0 % 50%RH; ISO 527-1/-2
Tensile Modulus  11.5 GPa 1670 ksi 50%RH; ISO 527-1/-2
  12.5 GPa 1810 ksi DAM; ISO 527-1/-2
Flexural Modulus  11.0 GPa 1600 ksi DAM; ISO 178
Secant Modulus   2.22 GPa
@Strain 5.39 %,
Temperature 100 °C		 322 ksi
@Strain 5.39 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  3.46 GPa
@Strain 3.16 %,
Temperature 100 °C		 501 ksi
@Strain 3.16 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  3.93 GPa
@Strain 2.26 %,
Temperature 100 °C		 571 ksi
@Strain 2.26 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  4.87 GPa
@Strain 1.72 %,
Temperature 100 °C		 706 ksi
@Strain 1.72 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  5.26 GPa
@Strain 1.28 %,
Temperature 100 °C		 763 ksi
@Strain 1.28 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  6.48 GPa
@Strain 0.630 %,
Temperature 100 °C		 940 ksi
@Strain 0.630 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  6.51 GPa
@Strain 2.38 %,
Temperature 40.0 °C		 944 ksi
@Strain 2.38 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  6.57 GPa
@Strain 0.670 %,
Temperature 100 °C		 953 ksi
@Strain 0.670 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  6.73 GPa
@Strain 1.77 %,
Temperature 40.0 °C		 975 ksi
@Strain 1.77 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  7.32 GPa
@Strain 0.250 %,
Temperature 100 °C		 1060 ksi
@Strain 0.250 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  7.5913 GPa
@Strain 0.230 %,
Temperature 100 °C		 1101.0 ksi
@Strain 0.230 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  7.9456 GPa
@Strain 1.82 %,
Temperature 23.0 °C		 1152.4 ksi
@Strain 1.82 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  8.23 GPa
@Strain 1.38 %,
Temperature 40.0 °C		 1190 ksi
@Strain 1.38 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  8.36 GPa
@Strain 0.980 %,
Temperature 40.0 °C		 1210 ksi
@Strain 0.980 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  9.3132 GPa
@Strain 1.97 %,
Temperature 23.0 °C		 1350.8 ksi
@Strain 1.97 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  9.60 GPa
@Strain 1.18 %,
Temperature 23.0 °C		 1390 ksi
@Strain 1.18 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  9.97 GPa
@Strain 0.410 %,
Temperature 40.0 °C		 1450 ksi
@Strain 0.410 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  10.1 GPa
@Strain 1.67 %,
Temperature 0.000 °C		 1460 ksi
@Strain 1.67 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  10.3 GPa
@Strain 0.580 %,
Temperature 40.0 °C		 1490 ksi
@Strain 0.580 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  10.5 GPa
@Strain 1.94 %,
Temperature 0.000 °C		 1520 ksi
@Strain 1.94 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  10.5 GPa
@Strain 0.220 %,
Temperature 40.0 °C		 1520 ksi
@Strain 0.220 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  11.0 GPa
@Strain 0.230 %,
Temperature 40.0 °C		 1590 ksi
@Strain 0.230 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  11.1 GPa
@Strain 0.660 %,
Temperature 23.0 °C		 1600 ksi
@Strain 0.660 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  11.2 GPa
@Strain 2.40 %,
Temperature -40.0 °C		 1620 ksi
@Strain 2.40 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  11.5 GPa
@Strain 1.19 %,
Temperature 23.0 °C		 1660 ksi
@Strain 1.19 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  11.7 GPa
@Strain 1.09 %,
Temperature 0.000 °C		 1700 ksi
@Strain 1.09 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  12.1 GPa
@Strain 0.340 %,
Temperature 23.0 °C		 1760 ksi
@Strain 0.340 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  12.2 GPa
@Strain 1.52 %,
Temperature -40.0 °C		 1780 ksi
@Strain 1.52 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  12.4 GPa
@Strain 1.15 %,
Temperature 0.000 °C		 1800 ksi
@Strain 1.15 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  12.7 GPa
@Strain 0.630 %,
Temperature 0.000 °C		 1840 ksi
@Strain 0.630 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  13.1 GPa
@Strain 1.53 %,
Temperature -40.0 °C		 1910 ksi
@Strain 1.53 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  13.3 GPa
@Strain 0.560 %,
Temperature 23.0 °C		 1930 ksi
@Strain 0.560 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  13.397 GPa
@Strain 0.330 %,
Temperature 0.000 °C		 1943.1 ksi
@Strain 0.330 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  13.4 GPa
@Strain 1.05 %,
Temperature -40.0 °C		 1950 ksi
@Strain 1.05 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  13.96 GPa
@Strain 0.550 %,
Temperature 0.000 °C		 2025 ksi
@Strain 0.550 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  14.1 GPa
@Strain 0.730 %,
Temperature -40.0 °C		 2040 ksi
@Strain 0.730 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  14.5 GPa
@Strain 0.230 %,
Temperature 23.0 °C		 2100 ksi
@Strain 0.230 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  14.9 GPa
@Strain 0.230 %,
Temperature 0.000 °C		 2150 ksi
@Strain 0.230 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  15.0 GPa
@Strain 0.870 %,
Temperature -40.0 °C		 2180 ksi
@Strain 0.870 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  15.9 GPa
@Strain 0.420 %,
Temperature -40.0 °C		 2310 ksi
@Strain 0.420 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
Izod Impact, Notched (ISO)  17.0 kJ/m² 8.09 ft-lb/in² DAM; ISO 180/1A
  15.0 kJ/m²
@Temperature -40.0 °C		 7.14 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1A
Charpy Impact Unnotched  10.0 J/cm² 47.6 ft-lb/in² DAM; ISO 179/1eU
  10.0 J/cm² 47.6 ft-lb/in² 50%RH; ISO 179/1eU
  8.00 J/cm²
@Temperature -30.0 °C		 38.1 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
  8.50 J/cm²
@Temperature -30.0 °C		 40.4 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
Charpy Impact, Notched  1.40 J/cm² 6.66 ft-lb/in² 50%RH; ISO 179/1eA
  1.70 J/cm² 8.09 ft-lb/in² DAM; ISO 179/1eA
  1.30 J/cm²
@Temperature -30.0 °C		 6.19 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
  1.70 J/cm²
@Temperature -40.0 °C		 8.09 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 179/1eA
  1.70 J/cm²
@Temperature -30.0 °C		 8.09 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour   7750 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 1.12e+6 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  8140 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 1.18e+6 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  8620 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 1.25e+6 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  9040 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 1.31e+6 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  9350 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 1.36e+6 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  9530 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 1.38e+6 psi
@Pressure 725 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
Tensile Creep Modulus, 1000 hours   6490 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 942000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  6770 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 982000 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  7092.2 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 1.0286e+6 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  7350 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 1.07e+6 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  7518.8 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 1.0905e+6 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  7610 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 1.10e+6 psi
@Pressure 725 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+15 ohm-cm 1.00e+15 ohm-cm DAM; IEC 60093
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  10.0 µm/m-°C 5.56 µin/in-°F DAM; ISO 11359-1/-2
  16.0 µm/m-°C
@Temperature 55.0 - 160 °C		 8.89 µin/in-°F
@Temperature 131 - 320 °F		 DAM; ISO 11359-1/-2
  21.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		 11.7 µin/in-°F
@Temperature -40.0 - 73.4 °F		 DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  104 µm/m-°C 57.8 µin/in-°F DAM; ISO 11359-1/-2
  73.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		 40.6 µin/in-°F
@Temperature -40.0 - 73.4 °F		 DAM; ISO 11359-1/-2
  139 µm/m-°C
@Temperature 55.0 - 160 °C		 77.2 µin/in-°F
@Temperature 131 - 320 °F		 DAM; ISO 11359-1/-2
Melting Point  218 °C 424 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  217 °C 423 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  203 °C 397 °F DAM; ISO 75-1/-2
Glass Transition Temp, Tg  65.0 °C 149 °F DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
  HB
@Thickness 0.700 mm		 HB
@Thickness 0.0276 in		 DAM; IEC 60695-11-10
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Part Marking Code >PA612-GF43< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA612-GF43  
  PA612-GF43 ISO 1043
UL recognition UL DAM

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39825.html

免责声明: 本文 PA612/美国杜邦/77G43L NC010注塑级 稳定性 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4