| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | |||
| 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 | |||
| Water Absorption | 8.5 % @Thickness 2.00 mm |
8.5 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Moisture Absorption | 2.60 % @Thickness 2.00 mm |
2.60 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Viscosity | 92024 cP @Shear Rate 5000 1/s, Temperature 300 °C |
92024 cP @Shear Rate 5000 1/s, Temperature 572 °F |
ISO 11403-1 -2 | ||
| 104500 cP @Shear Rate 5000 1/s, Temperature 290 °C |
104500 cP @Shear Rate 5000 1/s, Temperature 554 °F |
ISO 11403-1 -2 | |||
| 119500 cP @Shear Rate 5000 1/s, Temperature 280 °C |
119500 cP @Shear Rate 5000 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| 358900 cP @Shear Rate 500 1/s, Temperature 300 °C |
358900 cP @Shear Rate 500 1/s, Temperature 572 °F |
ISO 11403-1 -2 | |||
| 447000 cP @Shear Rate 500 1/s, Temperature 290 °C |
447000 cP @Shear Rate 500 1/s, Temperature 554 °F |
ISO 11403-1 -2 | |||
| 551300 cP @Shear Rate 500 1/s, Temperature 280 °C |
551300 cP @Shear Rate 500 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| Viscosity Test | 330 cm³/g | 330 cm³/g | DAM; ISO 307 1157 1628 | ||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 6.00 MPa @Strain 1.60 %, Temperature 150 °C |
870 psi @Strain 1.60 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | ||
| 8.60 MPa @Strain 2.40 %, Temperature 150 °C |
1250 psi @Strain 2.40 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 10.2 MPa @Strain 3.00 %, Temperature 150 °C |
1480 psi @Strain 3.00 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 16.1 MPa @Strain 6.00 %, Temperature 150 °C |
2340 psi @Strain 6.00 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 19.5 MPa @Strain 0.600 %, Temperature 23.0 °C |
2830 psi @Strain 0.600 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 36.9 MPa @Strain 1.10 %, Temperature -40.0 °C |
5350 psi @Strain 1.10 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 72.1 MPa @Strain 2.60 %, Temperature 23.0 °C |
10500 psi @Strain 2.60 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 76.8 MPa @Strain 2.90 %, Temperature 23.0 °C |
11100 psi @Strain 2.90 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 80.8 MPa @Strain 3.20 %, Temperature 23.0 °C |
11700 psi @Strain 3.20 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 88.7 MPa @Strain 2.90 %, Temperature -40.0 °C |
12900 psi @Strain 2.90 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 110 MPa @Strain 4.10 %, Temperature -40.0 °C |
16000 psi @Strain 4.10 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 124.9 MPa @Strain 6.00 %, Temperature -40.0 °C |
18120 psi @Strain 6.00 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50%RH; ISO 527-1/-2 | ||
| 84.0 MPa | 12200 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 35 % | 35 % | DAM; Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 4.3 % | 4.3 % | DAM; ISO 527-1/-2 | ||
| 29 % | 29 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 1.20 GPa | 174 ksi | 50%RH; ISO 527-1/-2 | ||
| 3.10 GPa | 450 ksi | DAM; ISO 527-1/-2 | |||
| Flexural Modulus | 2.80 GPa | 406 ksi | DAM; ISO 178 | ||
| Secant Modulus | 0.178 GPa @Strain 19.0 %, Temperature 100 °C |
25.8 ksi @Strain 19.0 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | ||
| 0.301 GPa @Strain 8.50 %, Temperature 100 °C |
43.7 ksi @Strain 8.50 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 0.402 GPa @Strain 4.10 %, Temperature 100 °C |
58.4 ksi @Strain 4.10 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 0.471 GPa @Strain 2.10 %, Temperature 100 °C |
68.4 ksi @Strain 2.10 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 0.536 GPa @Strain 1.10 %, Temperature 100 °C |
77.8 ksi @Strain 1.10 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 2.44 GPa @Strain 3.40 %, Temperature 23.0 °C |
354 ksi @Strain 3.40 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 2.55 GPa @Strain 4.50 %, Temperature -40.0 °C |
370 ksi @Strain 4.50 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 2.60 GPa @Strain 3.00 %, Temperature 23.0 °C |
378 ksi @Strain 3.00 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 2.77 GPa @Strain 2.60 %, Temperature 23.0 °C |
402 ksi @Strain 2.60 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 3.06 GPa @Strain 2.90 %, Temperature -40.0 °C |
444 ksi @Strain 2.90 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 3.25 GPa @Strain 0.600 %, Temperature 23.0 °C |
471 ksi @Strain 0.600 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 3.35 GPa @Strain 1.10 %, Temperature -40.0 °C |
487 ksi @Strain 1.10 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | DAM; ISO 180/1A | ||
| Charpy Impact Unnotched | NB | NB | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | DAM; ISO 179/1eA | ||
| 2.10 J/cm² | 9.99 ft-lb/in² | 50%RH; ISO 179/1eA | |||
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |||
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | 50%RH; IEC 60093 | ||
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | DAM; IEC 60093 | |||
| Comparative Tracking Index | 600 V | 600 V | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 2.79 J/g-°C | 0.667 BTU/lb-°F | |||
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft²-°F | of melt | ||
| Melting Point | 262 °C | 504 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | ||
| Vicat Softening Point | 221 °C | 430 °F | DAM; 50°C/h 50N; ISO 306 | ||
| Oxygen Index | 20 % | 20 % | DAM; ISO 4589-1/-2 | ||
| De |
|||||
| Additives | Release agent | ||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PA66< | ISO 11469 | |||
| Processing | Casting | ||||
| Coatable | |||||
| Film Extrusion | |||||
| Injection Moulding | |||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Sheet Extrusion | |||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA66 | ||||
| Special characteristics | Heat stabilised or stable to heat | ||||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。