| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 5.4 % @Thickness 2.00 mm |
5.4 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Moisture Absorption | 1.70 % @Thickness 2.00 mm |
1.70 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Viscosity Test | 115 cm³/g | 115 cm³/g | DAM; ISO 307 1157 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 128 MPa | 18600 psi | 50%RH; ISO 527-1/-2 | ||
| 185 MPa | 26800 psi | DAM; ISO 527-1/-2 | |||
| Tensile Stress | 36.46 MPa @Strain 0.890 %, Temperature 90.0 °C |
5288 psi @Strain 0.890 %, Temperature 194 °F |
50%RH; ISO 11403-1 -2 | ||
| 41.97 MPa @Strain 1.01 %, Temperature 90.0 °C |
6087 psi @Strain 1.01 %, Temperature 194 °F |
DAM; ISO 11403-1 -2 | |||
| 46.11 MPa @Strain 0.630 %, Temperature 23.0 °C |
6688 psi @Strain 0.630 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |||
| 47.33 MPa @Strain 0.390 %, Temperature -40.0 °C |
6865 psi @Strain 0.390 %, Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |||
| 48.66 MPa @Strain 0.450 %, Temperature 23.0 °C |
7058 psi @Strain 0.450 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 49.87 MPa @Strain 0.450 %, Temperature -40.0 °C |
7233 psi @Strain 0.450 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 75.34 MPa @Strain 3.50 %, Temperature 90.0 °C |
10930 psi @Strain 3.50 %, Temperature 194 °F |
50%RH; ISO 11403-1 -2 | |||
| 85.05 MPa @Strain 4.04 %, Temperature 90.0 °C |
12340 psi @Strain 4.04 %, Temperature 194 °F |
DAM; ISO 11403-1 -2 | |||
| 86.69 MPa @Strain 6.10 %, Temperature 90.0 °C |
12570 psi @Strain 6.10 %, Temperature 194 °F |
50%RH; ISO 11403-1 -2 | |||
| 100.39 MPa @Strain 7.07 %, Temperature 90.0 °C |
14560 psi @Strain 7.07 %, Temperature 194 °F |
DAM; ISO 11403-1 -2 | |||
| 128.03 MPa @Strain 4.35 %, Temperature 23.0 °C |
18569 psi @Strain 4.35 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |||
| 147.57 MPa @Strain 1.77 %, Temperature 23.0 °C |
21403 psi @Strain 1.77 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 156.63 MPa @Strain 1.57 %, Temperature -40.0 °C |
22717 psi @Strain 1.57 %, Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |||
| 171.69 MPa @Strain 1.76 %, Temperature -40.0 °C |
24902 psi @Strain 1.76 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 177.18 MPa @Strain 3.08 %, Temperature 23.0 °C |
25698 psi @Strain 3.08 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 216.33 MPa @Strain 2.73 %, Temperature -40.0 °C |
31376 psi @Strain 2.73 %, Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |||
| 237.23 MPa @Strain 3.91 %, Temperature -40.0 °C |
34407 psi @Strain 3.91 %, Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |||
| 238.46 MPa @Strain 3.09 %, Temperature -40.0 °C |
34586 psi @Strain 3.09 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 263.49 MPa @Strain 4.41 %, Temperature -40.0 °C |
38216 psi @Strain 4.41 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| Elongation at Break | 3.5 % | 3.5 % | DAM; ISO 527-1/-2 | ||
| 7.3 % | 7.3 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 7.50 GPa | 1090 ksi | 50%RH; ISO 527-1/-2 | ||
| 12.2 GPa | 1770 ksi | DAM; ISO 527-1/-2 | |||
| 4.625 GPa @Temperature 120 °C |
670.8 ksi @Temperature 248 °F |
DAM; ISO 11403-1 -2 | |||
| 11.395 GPa @Temperature -40.0 °C |
1652.7 ksi @Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 12.275 GPa @Temperature -40.0 °C |
1780.3 ksi @Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |||
| Secant Modulus | 2.94 GPa @Strain 4.35 %, Temperature 23.0 °C |
427 ksi @Strain 4.35 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | ||
| 5.09 GPa @Strain 3.53 %, Temperature 23.0 °C |
739 ksi @Strain 3.53 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 7.13 GPa @Strain 3.52 %, Temperature -40.0 °C |
1030 ksi @Strain 3.52 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 7.29 GPa @Strain 3.13 %, Temperature -40.0 °C |
1060 ksi @Strain 3.13 %, Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |||
| 7.32 GPa @Strain 0.630 %, Temperature 23.0 °C |
1060 ksi @Strain 0.630 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |||
| 8.34 GPa @Strain 1.77 %, Temperature 23.0 °C |
1210 ksi @Strain 1.77 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 9.76 GPa @Strain 1.76 %, Temperature -40.0 °C |
1410 ksi @Strain 1.76 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 9.98 GPa @Strain 1.57 %, Temperature -40.0 °C |
1450 ksi @Strain 1.57 %, Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |||
| 10.8 GPa @Strain 0.450 %, Temperature 23.0 °C |
1570 ksi @Strain 0.450 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 11.1 GPa @Strain 0.450 %, Temperature -40.0 °C |
1610 ksi @Strain 0.450 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 12.1 GPa @Strain 0.390 %, Temperature -40.0 °C |
1760 ksi @Strain 0.390 %, Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | DAM; ISO 180/1A | ||
| 30.0 kJ/m² | 14.3 ft-lb/in² | 50%RH; ISO 180/1A | |||
| 18.0 kJ/m² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 180/1A | |||
| 19.0 kJ/m² @Temperature -30.0 °C |
9.04 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 180/1A | |||
| Charpy Impact Unnotched | 11.0 J/cm² | 52.3 ft-lb/in² | DAM; ISO 179/1eU | ||
| 11.3 J/cm² | 53.8 ft-lb/in² | 50%RH; ISO 179/1eU | |||
| 10.5 J/cm² @Temperature -30.0 °C |
50.0 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eU | |||
| 11.8 J/cm² @Temperature -30.0 °C |
56.1 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 2.40 J/cm² | 11.4 ft-lb/in² | DAM; ISO 179/1eA | ||
| 3.30 J/cm² | 15.7 ft-lb/in² | 50%RH; ISO 179/1eA | |||
| 1.70 J/cm² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |||
| 1.80 J/cm² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 221 °C | 430 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | DAM; ISO 75-1/-2 | ||
| De |
|||||
| Delivery form | Pellets | ||||
| Processing | Injection Moulding | ||||
| Regional Availability | Europe | ||||
| Near East/Africa | |||||
| Special characteristics | Heat stabilised or stable to heat | ||||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。