  4. PA66/美国杜邦/FE270038 BK267 热稳定

PA66/美国杜邦/FE270038 BK267 热稳定

PA66/美国杜邦/FE270038 BK267 40%玻纤 热稳定
 参考图片：

颗粒图片：

包装图片：

成品图片：
images (5)

 

 

 
Physical Properties Metric English Comments
Density  1.30 g/cc 0.0470 lb/in³  
  1.46 g/cc 0.0527 lb/in³ DAM; ISO 1183
Water Absorption  5.0 %
@Thickness 2.00 mm		 5.0 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  1.50 %
@Thickness 2.00 mm		 1.50 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Viscosity   69730 cP
@Shear Rate 5000 1/s,
Temperature 300 °C		 69730 cP
@Shear Rate 5000 1/s,
Temperature 572 °F		 ISO 11403-1 -2
  92504 cP
@Shear Rate 5000 1/s,
Temperature 290 °C		 92504 cP
@Shear Rate 5000 1/s,
Temperature 554 °F		 ISO 11403-1 -2
  127400 cP
@Shear Rate 5000 1/s,
Temperature 280 °C		 127400 cP
@Shear Rate 5000 1/s,
Temperature 536 °F		 ISO 11403-1 -2
  318080 cP
@Shear Rate 500 1/s,
Temperature 300 °C		 318080 cP
@Shear Rate 500 1/s,
Temperature 572 °F		 ISO 11403-1 -2
  438400 cP
@Shear Rate 500 1/s,
Temperature 290 °C		 438400 cP
@Shear Rate 500 1/s,
Temperature 554 °F		 ISO 11403-1 -2
  615000 cP
@Shear Rate 500 1/s,
Temperature 280 °C		 615000 cP
@Shear Rate 500 1/s,
Temperature 536 °F		 ISO 11403-1 -2
Viscosity Test  130 cm³/g 130 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0070 cm/cm 0.0070 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  110 MPa 16000 psi 50%RH; ISO 527-1/-2
  145 MPa 21000 psi DAM; ISO 527-1/-2
Tensile Stress   9.12 MPa
@Strain 0.230 %,
Temperature 90.0 °C		 1320 psi
@Strain 0.230 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  10.3 MPa
@Strain 0.410 %,
Temperature 150 °C		 1490 psi
@Strain 0.410 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  11.92 MPa
@Strain 0.390 %,
Temperature 150 °C		 1729 psi
@Strain 0.390 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  13.89 MPa
@Strain 0.560 %,
Temperature 180 °C		 2015 psi
@Strain 0.560 %,
Temperature 356 °F		 DAM; ISO 11403-1 -2
  17.77 MPa
@Strain 0.370 %,
Temperature 90.0 °C		 2577 psi
@Strain 0.370 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  18.46 MPa
@Strain 0.240 %,
Temperature 23.0 °C		 2677 psi
@Strain 0.240 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  24.88 MPa
@Strain 0.440 %,
Temperature 40.0 °C		 3609 psi
@Strain 0.440 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  25.55 MPa
@Strain 1.53 %,
Temperature 150 °C		 3706 psi
@Strain 1.53 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  28.83 MPa
@Strain 0.930 %,
Temperature 90.0 °C		 4181 psi
@Strain 0.930 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  28.98 MPa
@Strain 1.80 %,
Temperature 180 °C		 4203 psi
@Strain 1.80 %,
Temperature 356 °F		 DAM; ISO 11403-1 -2
  30.54 MPa
@Strain 1.40 %,
Temperature 150 °C		 4429 psi
@Strain 1.40 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  33.2 MPa
@Strain 2.68 %,
Temperature 150 °C		 4820 psi
@Strain 2.68 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  36.61 MPa
@Strain 3.06 %,
Temperature 180 °C		 5310 psi
@Strain 3.06 %,
Temperature 356 °F		 DAM; ISO 11403-1 -2
  37.55 MPa
@Strain 3.99 %,
Temperature 150 °C		 5446 psi
@Strain 3.99 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  37.6 MPa
@Strain 0.930 %,
Temperature 90.0 °C		 5450 psi
@Strain 0.930 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  40.07 MPa
@Strain 2.35 %,
Temperature 150 °C		 5812 psi
@Strain 2.35 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  40.99 MPa
@Strain 1.71 %,
Temperature 90.0 °C		 5945 psi
@Strain 1.71 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  41.45 MPa
@Strain 4.41 %,
Temperature 180 °C		 6012 psi
@Strain 4.41 %,
Temperature 356 °F		 DAM; ISO 11403-1 -2
  43.89 MPa
@Strain 0.900 %,
Temperature 40.0 °C		 6366 psi
@Strain 0.900 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  46.09 MPa
@Strain 0.480 %,
Temperature 0.000 °C		 6685 psi
@Strain 0.480 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  46.66 MPa
@Strain 3.50 %,
Temperature 150 °C		 6767 psi
@Strain 3.50 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  48.39 MPa
@Strain 2.71 %,
Temperature 90.0 °C		 7018 psi
@Strain 2.71 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  51.91 MPa
@Strain 1.51 %,
Temperature 90.0 °C		 7529 psi
@Strain 1.51 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  56.04 MPa
@Strain 0.580 %,
Temperature -20.0 °C		 8128 psi
@Strain 0.580 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  56.38 MPa
@Strain 0.620 %,
Temperature 0.000 °C		 8177 psi
@Strain 0.620 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  59.41 MPa
@Strain 1.39 %,
Temperature 40.0 °C		 8617 psi
@Strain 1.39 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  60.48 MPa
@Strain 0.910 %,
Temperature 23.0 °C		 8772 psi
@Strain 0.910 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  62.79 MPa
@Strain 0.710 %,
Temperature 40.0 °C		 9107 psi
@Strain 0.710 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  63.34 MPa
@Strain 2.22 %,
Temperature 90.0 °C		 9187 psi
@Strain 2.22 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  70.92 MPa
@Strain 0.780 %,
Temperature 23.0 °C		 10290 psi
@Strain 0.780 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  71.24 MPa
@Strain 0.760 %,
Temperature -20.0 °C		 10330 psi
@Strain 0.760 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  71.32 MPa
@Strain 1.99 %,
Temperature 40.0 °C		 10340 psi
@Strain 1.99 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  77.68 MPa
@Strain 0.860 %,
Temperature 0.000 °C		 11270 psi
@Strain 0.860 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  77.99 MPa
@Strain 1.30 %,
Temperature 23.0 °C		 11310 psi
@Strain 1.30 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  83.91 MPa
@Strain 1.00 %,
Temperature 40.0 °C		 12170 psi
@Strain 1.00 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  89.13 MPa
@Strain 0.960 %,
Temperature -20.0 °C		 12930 psi
@Strain 0.960 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  93.57 MPa
@Strain 1.79 %,
Temperature 23.0 °C		 13570 psi
@Strain 1.79 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  98.89 MPa
@Strain 1.13 %,
Temperature 0.000 °C		 14340 psi
@Strain 1.13 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  102.34 MPa
@Strain 1.21 %,
Temperature 23.0 °C		 14843 psi
@Strain 1.21 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  104.57 MPa
@Strain 1.35 %,
Temperature 40.0 °C		 15167 psi
@Strain 1.35 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  105.98 MPa
@Strain 1.31 %,
Temperature 0.000 °C		 15371 psi
@Strain 1.31 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  113.5 MPa
@Strain 1.29 %,
Temperature -20.0 °C		 16460 psi
@Strain 1.29 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  122.88 MPa
@Strain 1.79 %,
Temperature 40.0 °C		 17822 psi
@Strain 1.79 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  123.75 MPa
@Strain 1.50 %,
Temperature 0.000 °C		 17948 psi
@Strain 1.50 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  124.19 MPa
@Strain 1.59 %,
Temperature 23.0 °C		 18012 psi
@Strain 1.59 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  124.89 MPa
@Strain 1.73 %,
Temperature 0.000 °C		 18114 psi
@Strain 1.73 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  134.88 MPa
@Strain 1.58 %,
Temperature -20.0 °C		 19563 psi
@Strain 1.58 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  137.07 MPa
@Strain 1.69 %,
Temperature -20.0 °C		 19880 psi
@Strain 1.69 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  142.25 MPa
@Strain 2.05 %,
Temperature 23.0 °C		 20632 psi
@Strain 2.05 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  146.77 MPa
@Strain 1.93 %,
Temperature 0.000 °C		 21287 psi
@Strain 1.93 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  159.71 MPa
@Strain 2.04 %,
Temperature -20.0 °C		 23164 psi
@Strain 2.04 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  180.18 MPa
@Strain 2.58 %,
Temperature -20.0 °C		 26133 psi
@Strain 2.58 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  10.0 MPa
@Strain 0.160 %,
Time 360000 sec		 1450 psi
@Strain 0.160 %,
Time 100 hour		 50%RH; isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.170 %,
Time 3.60e+6 sec		 1450 psi
@Strain 0.170 %,
Time 1000 hour		 50%RH; isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.140 %,
Time 3600 sec		 1450 psi
@Strain 0.140 %,
Time 1.00 hour		 50%RH; isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.150 %,
Time 36000 sec		 1450 psi
@Strain 0.150 %,
Time 10.0 hour		 50%RH; isochronous; ISO 11403-1 -2
Elongation at Break  2.5 % 2.5 % DAM; ISO 527-1/-2
  2.6 % 2.6 % 50%RH; ISO 527-1/-2
Tensile Modulus  7.80 GPa 1130 ksi 50%RH; ISO 527-1/-2
  8.80 GPa 1280 ksi DAM; ISO 527-1/-2
  2.343 GPa
@Temperature 150 °C		 339.8 ksi
@Temperature 302 °F		 50%RH; ISO 11403-1 -2
  2.383 GPa
@Temperature 170 °C		 345.6 ksi
@Temperature 338 °F		 50%RH; Dynamic; ISO 11403-1 -2
  2.60 GPa
@Temperature 170 °C		 377 ksi
@Temperature 338 °F		 DAM; Dynamic; ISO 11403-1 -2
  2.865 GPa
@Temperature 150 °C		 415.5 ksi
@Temperature 302 °F		 DAM; ISO 11403-1 -2
  3.164 GPa
@Temperature 110 °C		 458.9 ksi
@Temperature 230 °F		 50%RH; Dynamic; ISO 11403-1 -2
  3.85 GPa
@Temperature 110 °C		 558 ksi
@Temperature 230 °F		 DAM; Dynamic; ISO 11403-1 -2
  4.501 GPa
@Temperature 60.0 °C		 652.8 ksi
@Temperature 140 °F		 50%RH; ISO 11403-1 -2
  7.371 GPa
@Temperature 60.0 °C		 1069 ksi
@Temperature 140 °F		 DAM; ISO 11403-1 -2
  7.863 GPa
@Temperature 30.0 °C		 1140 ksi
@Temperature 86.0 °F		 50%RH; Dynamic; ISO 11403-1 -2
  7.974 GPa
@Temperature 30.0 °C		 1157 ksi
@Temperature 86.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  8.223 GPa
@Temperature -20.0 °C		 1193 ksi
@Temperature -4.00 °F		 DAM; Dynamic; ISO 11403-1 -2
  8.911 GPa
@Temperature -70.0 °C		 1292 ksi
@Temperature -94.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  9.102 GPa
@Temperature -20.0 °C		 1320 ksi
@Temperature -4.00 °F		 50%RH; Dynamic; ISO 11403-1 -2
  9.311 GPa
@Temperature -100 °C		 1350 ksi
@Temperature -148 °F		 DAM; Dynamic; ISO 11403-1 -2
  9.975 GPa
@Temperature -20.0 °C		 1447 ksi
@Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  10.062 GPa
@Temperature -70.0 °C		 1459.4 ksi
@Temperature -94.0 °F		 50%RH; Dynamic; ISO 11403-1 -2
  10.237 GPa
@Temperature -20.0 °C		 1484.8 ksi
@Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  10.491 GPa
@Temperature -100 °C		 1521.6 ksi
@Temperature -148 °F		 50%RH; Dynamic; ISO 11403-1 -2
Shear Modulus   1.297 GPa
@Temperature 100 °C		 188.1 ksi
@Temperature 212 °F		 50%RH; Dynamic; ISO 11403-1 -2
  1.604 GPa
@Temperature 100 °C		 232.6 ksi
@Temperature 212 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.87 GPa
@Temperature 60.0 °C		 271 ksi
@Temperature 140 °F		 50%RH; Dynamic; ISO 11403-1 -2
  2.637 GPa
@Temperature 60.0 °C		 382.5 ksi
@Temperature 140 °F		 DAM; Dynamic; ISO 11403-1 -2
  3.02 GPa
@Temperature 10.0 °C		 438 ksi
@Temperature 50.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  3.138 GPa
@Temperature -40.0 °C		 455.1 ksi
@Temperature -40.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  3.253 GPa
@Temperature 10.0 °C		 471.8 ksi
@Temperature 50.0 °F		 50%RH; Dynamic; ISO 11403-1 -2
  3.331 GPa
@Temperature -70.0 °C		 483.1 ksi
@Temperature -94.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  3.469 GPa
@Temperature -100 °C		 503.1 ksi
@Temperature -148 °F		 DAM; Dynamic; ISO 11403-1 -2
  3.485 GPa
@Temperature -40.0 °C		 505.5 ksi
@Temperature -40.0 °F		 50%RH; Dynamic; ISO 11403-1 -2
  3.754 GPa
@Temperature -70.0 °C		 544.5 ksi
@Temperature -94.0 °F		 50%RH; Dynamic; ISO 11403-1 -2
  3.915 GPa
@Temperature -100 °C		 567.8 ksi
@Temperature -148 °F		 50%RH; Dynamic; ISO 11403-1 -2
Secant Modulus   0.516 GPa
@Strain 8.09 %,
Temperature 200 °C		 74.9 ksi
@Strain 8.09 %,
Temperature 392 °F		 DAM; ISO 11403-1 -2
  0.660 GPa
@Strain 5.90 %,
Temperature 200 °C		 95.8 ksi
@Strain 5.90 %,
Temperature 392 °F		 DAM; ISO 11403-1 -2
  0.887 GPa
@Strain 3.88 %,
Temperature 200 °C		 129 ksi
@Strain 3.88 %,
Temperature 392 °F		 DAM; ISO 11403-1 -2
  1.33 GPa
@Strain 1.99 %,
Temperature 200 °C		 193 ksi
@Strain 1.99 %,
Temperature 392 °F		 DAM; ISO 11403-1 -2
  2.14 GPa
@Strain 0.640 %,
Temperature 200 °C		 311 ksi
@Strain 0.640 %,
Temperature 392 °F		 DAM; ISO 11403-1 -2
  2.87 GPa
@Strain 2.62 %,
Temperature 40.0 °C		 416 ksi
@Strain 2.62 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  4.04 GPa
@Strain 1.58 %,
Temperature 40.0 °C		 587 ksi
@Strain 1.58 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  4.32 GPa
@Strain 2.29 %,
Temperature 23.0 °C		 627 ksi
@Strain 2.29 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.88 GPa
@Strain 0.900 %,
Temperature 40.0 °C		 707 ksi
@Strain 0.900 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  5.65 GPa
@Strain 2.28 %,
Temperature 40.0 °C		 820 ksi
@Strain 2.28 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  5.65 GPa
@Strain 0.440 %,
Temperature 40.0 °C		 820 ksi
@Strain 0.440 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  5.76 GPa
@Strain 1.45 %,
Temperature 23.0 °C		 835 ksi
@Strain 1.45 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  6.35 GPa
@Strain 2.11 %,
Temperature 0.000 °C		 921 ksi
@Strain 2.11 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  6.65 GPa
@Strain 0.910 %,
Temperature 23.0 °C		 964 ksi
@Strain 0.910 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  6.99 GPa
@Strain 2.28 %,
Temperature 0.000 °C		 1010 ksi
@Strain 2.28 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  7.5027 GPa
@Strain 1.48 %,
Temperature 40.0 °C		 1088.2 ksi
@Strain 1.48 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  7.5578 GPa
@Strain 1.73 %,
Temperature 23.0 °C		 1096.2 ksi
@Strain 1.73 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  7.58 GPa
@Strain 1.99 %,
Temperature -20.0 °C		 1100 ksi
@Strain 1.99 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  7.60 GPa
@Strain 2.20 %,
Temperature -20.0 °C		 1100 ksi
@Strain 2.20 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  7.69 GPa
@Strain 0.240 %,
Temperature 23.0 °C		 1120 ksi
@Strain 0.240 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  7.87 GPa
@Strain 1.43 %,
Temperature 0.000 °C		 1140 ksi
@Strain 1.43 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  8.04 GPa
@Strain 1.64 %,
Temperature 0.000 °C		 1170 ksi
@Strain 1.64 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  8.391 GPa
@Strain 1.00 %,
Temperature 40.0 °C		 1217 ksi
@Strain 1.00 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  8.46 GPa
@Strain 1.21 %,
Temperature 23.0 °C		 1230 ksi
@Strain 1.21 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  8.54 GPa
@Strain 1.58 %,
Temperature -20.0 °C		 1240 ksi
@Strain 1.58 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  8.61 GPa
@Strain 1.41 %,
Temperature -20.0 °C		 1250 ksi
@Strain 1.41 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  8.75 GPa
@Strain 1.13 %,
Temperature 0.000 °C		 1270 ksi
@Strain 1.13 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  8.84 GPa
@Strain 0.710 %,
Temperature 40.0 °C		 1280 ksi
@Strain 0.710 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  9.03 GPa
@Strain 0.860 %,
Temperature 0.000 °C		 1310 ksi
@Strain 0.860 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  9.09 GPa
@Strain 0.780 %,
Temperature 23.0 °C		 1320 ksi
@Strain 0.780 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  9.09 GPa
@Strain 0.620 %,
Temperature 0.000 °C		 1320 ksi
@Strain 0.620 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  9.28 GPa
@Strain 0.960 %,
Temperature -20.0 °C		 1350 ksi
@Strain 0.960 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  9.37 GPa
@Strain 0.760 %,
Temperature -20.0 °C		 1360 ksi
@Strain 0.760 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  9.60 GPa
@Strain 0.480 %,
Temperature 0.000 °C		 1390 ksi
@Strain 0.480 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  9.66 GPa
@Strain 0.580 %,
Temperature -20.0 °C		 1400 ksi
@Strain 0.580 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
Charpy Impact Unnotched  4.10 J/cm² 19.5 ft-lb/in² DAM; ISO 179/1eU
  4.10 J/cm² 19.5 ft-lb/in² 50%RH; ISO 179/1eU
  4.00 J/cm²
@Temperature -30.0 °C		 19.0 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
  4.00 J/cm²
@Temperature -30.0 °C		 19.0 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm² 1.90 ft-lb/in² DAM; ISO 179/1eA
  0.400 J/cm² 1.90 ft-lb/in² 50%RH; ISO 179/1eA
  0.300 J/cm²
@Temperature -30.0 °C		 1.43 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
  0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour   5290 MPa
@Pressure 55.0 MPa,
Temperature 23.0 °C		 767000 psi
@Pressure 7980 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  5380 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 781000 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  5638 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 817700 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  6000 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 870000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  6510 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 944000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  7140 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 1.04e+6 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  7000 MPa
@Time 3600 sec		 1.02e+6 psi
@Time 1.00 hour		 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours   3793.1 MPa
@Pressure 55.0 MPa,
Temperature 23.0 °C		 550140 psi
@Pressure 7980 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3920 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 569000 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4280 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 620000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4761.9 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 690660 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  5320 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 772000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  5880 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 853000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  6000 MPa
@Time 3.60e+6 sec		 870000 psi
@Time 1000 hour		 50%RH; ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  2.00e+12 ohm-cm 2.00e+12 ohm-cm 50%RH; IEC 60093
  8.00e+14 ohm-cm 8.00e+14 ohm-cm DAM; IEC 60093
Surface Resistance  3.00e+14 ohm 3.00e+14 ohm 50%RH; IEC 60093
Dielectric Strength  41.0 kV/mm 1040 kV/in DAM; IEC 60243-1
  41.0 kV/mm 1040 kV/in 50%RH; IEC 60243-1
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  23.0 µm/m-°C 12.8 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  60.0 µm/m-°C 33.3 µin/in-°F DAM; ISO 11359-1/-2
Specific Heat Capacity  2.28 J/g-°C 0.545 BTU/lb-°F  
Thermal Conductivity  0.260 W/m-K 1.80 BTU-in/hr-ft²-°F of melt
Melting Point  245 °C 473 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)  230 °C 446 °F DAM; ISO 75-1/-2
Glass Transition Temp, Tg  90.0 °C 194 °F DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
 
Descriptive Properties
Delivery form Pellets  
Processing Injection Moulding  
Regional Availability Europe  
  Near East/Africa  
Special characteristics Heat stabilised or stable to heat  

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39954.html

免责声明: 本文 PA66/美国杜邦/FE270038 BK267 热稳定 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4