高粘度 高韧性PA612/美国杜邦/LC6200 BK385

高粘度 高韧性 PA612/美国杜邦/LC6200 BK385
 参考图片：

颗粒图片：

包装图片：

成品图片：
100001041143_13526462585748

 

 

 
Physical Properties Metric English Comments
Density  0.820 g/cc 0.0296 lb/in³  
  1.00 g/cc 0.0361 lb/in³ DAM; ISO 1183
Viscosity   74000 cP
@Shear Rate 5000 1/s,
Temperature 270 °C		 74000 cP
@Shear Rate 5000 1/s,
Temperature 518 °F		 ISO 11403-1 -2
  88000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 88000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  109890 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 109890 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  280000 cP
@Shear Rate 500 1/s,
Temperature 270 °C		 280000 cP
@Shear Rate 500 1/s,
Temperature 518 °F		 ISO 11403-1 -2
  349000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 349000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  425090 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 425090 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.028 cm/cm 0.028 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.011 cm/cm 0.011 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Stress  0.850 MPa
@Strain 0.110 %,
Temperature 40.0 °C		 123 psi
@Strain 0.110 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  1.13 MPa
@Strain 0.0800 %,
Temperature 23.0 °C		 164 psi
@Strain 0.0800 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  1.21 MPa
@Strain 0.0800 %,
Temperature 0.000 °C		 175 psi
@Strain 0.0800 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  1.33 MPa
@Strain 0.0600 %,
Temperature -20.0 °C		 193 psi
@Strain 0.0600 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  2.37 MPa
@Strain 0.920 %,
Temperature 90.0 °C		 344 psi
@Strain 0.920 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  2.82 MPa
@Strain 3.27 %,
Temperature 150 °C		 409 psi
@Strain 3.27 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  2.83 MPa
@Strain 0.440 %,
Temperature 40.0 °C		 410 psi
@Strain 0.440 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  3.18 MPa
@Strain 4.50 %,
Temperature 150 °C		 461 psi
@Strain 4.50 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  3.44 MPa
@Strain 0.230 %,
Temperature 0.000 °C		 499 psi
@Strain 0.230 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  4.05 MPa
@Strain 0.400 %,
Temperature 23.0 °C		 587 psi
@Strain 0.400 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.23 MPa
@Strain 0.240 %,
Temperature -20.0 °C		 614 psi
@Strain 0.240 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  5.32 MPa
@Strain 0.230 %,
Temperature -40.0 °C		 772 psi
@Strain 0.230 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  5.51 MPa
@Strain 2.96 %,
Temperature 90.0 °C		 799 psi
@Strain 2.96 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  7.10 MPa
@Strain 48.0 %,
Temperature 150 °C		 1030 psi
@Strain 48.0 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  13.6 MPa
@Strain 48.45 %,
Temperature 90.0 °C		 1970 psi
@Strain 48.45 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  14.12 MPa
@Strain 39.22 %,
Temperature 90.0 °C		 2048 psi
@Strain 39.22 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  14.93 MPa
@Strain 0.710 %,
Temperature -40.0 °C		 2165 psi
@Strain 0.710 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  17.6 MPa
@Strain 1.36 %,
Temperature 0.000 °C		 2550 psi
@Strain 1.36 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  20.87 MPa
@Strain 11.52 %,
Temperature 40.0 °C		 3027 psi
@Strain 11.52 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  21.0 MPa
@Strain 5.34 %,
Temperature 40.0 °C		 3050 psi
@Strain 5.34 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  21.54 MPa
@Strain 2.11 %,
Temperature 23.0 °C		 3124 psi
@Strain 2.11 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  22.66 MPa
@Strain 24.42 %,
Temperature 40.0 °C		 3287 psi
@Strain 24.42 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  24.84 MPa
@Strain 17.81 %,
Temperature 40.0 °C		 3603 psi
@Strain 17.81 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  25.45 MPa
@Strain 31.26 %,
Temperature 40.0 °C		 3691 psi
@Strain 31.26 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  27.84 MPa
@Strain 9.53 %,
Temperature 23.0 °C		 4038 psi
@Strain 9.53 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  29.26 MPa
@Strain 20.72 %,
Temperature 23.0 °C		 4244 psi
@Strain 20.72 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  32.3 MPa
@Strain 12.4 %,
Temperature 23.0 °C		 4680 psi
@Strain 12.4 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  39.26 MPa
@Strain 8.21 %,
Temperature 0.000 °C		 5694 psi
@Strain 8.21 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  40.8 MPa
@Strain 10.85 %,
Temperature 0.000 °C		 5920 psi
@Strain 10.85 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  47.34 MPa
@Strain 3.08 %,
Temperature -40.0 °C		 6866 psi
@Strain 3.08 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  47.91 MPa
@Strain 8.21 %,
Temperature -20.0 °C		 6949 psi
@Strain 8.21 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  53.18 MPa
@Strain 4.52 %,
Temperature -40.0 °C		 7713 psi
@Strain 4.52 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  60.95 MPa
@Strain 8.91 %,
Temperature -40.0 °C		 8840 psi
@Strain 8.91 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  62.14 MPa
@Strain 7.35 %,
Temperature -40.0 °C		 9013 psi
@Strain 7.35 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Tensile Strength, Yield  28.0 MPa 4060 psi 50%RH; ISO 527-1/-2
  30.0 MPa 4350 psi DAM; ISO 527-1/-2
Elongation at Break  >= 50 % >= 50 % DAM; Nominal; ISO 527-1/-2
  >= 50 % >= 50 % 50%RH; Nominal; ISO 527-1/-2
Elongation at Yield  20 % 20 % DAM; ISO 527-1/-2
  30 % 30 % 50%RH; ISO 527-1/-2
Tensile Modulus  0.720 GPa 104 ksi 50%RH; ISO 527-1/-2
  1.08 GPa 157 ksi DAM; ISO 527-1/-2
  0.110 GPa
@Temperature 120 °C		 16.0 ksi
@Temperature 248 °F		 50%RH; ISO 11403-1 -2
  0.130 GPa
@Temperature 120 °C		 18.9 ksi
@Temperature 248 °F		 DAM; ISO 11403-1 -2
  0.455 GPa
@Temperature 40.0 °C		 66.0 ksi
@Temperature 104 °F		 50%RH; ISO 11403-1 -2
  0.680 GPa
@Temperature 40.0 °C		 98.6 ksi
@Temperature 104 °F		 DAM; ISO 11403-1 -2
  2.119 GPa
@Temperature -40.0 °C		 307.3 ksi
@Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  2.196 GPa
@Temperature -40.0 °C		 318.5 ksi
@Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Secant Modulus   0.0786 GPa
@Strain 29.03 %,
Temperature 40.0 °C		 11.4 ksi
@Strain 29.03 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  0.114 GPa
@Strain 22.16 %,
Temperature 40.0 °C		 16.5 ksi
@Strain 22.16 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  0.181 GPa
@Strain 11.52 %,
Temperature 40.0 °C		 26.3 ksi
@Strain 11.52 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  0.29213 GPa
@Strain 9.53 %,
Temperature 23.0 °C		 42.371 ksi
@Strain 9.53 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  0.393 GPa
@Strain 5.34 %,
Temperature 40.0 °C		 57.0 ksi
@Strain 5.34 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  0.402 GPa
@Strain 12.06 %,
Temperature -20.0 °C		 58.3 ksi
@Strain 12.06 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  0.478 GPa
@Strain 8.21 %,
Temperature 0.000 °C		 69.4 ksi
@Strain 8.21 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  0.583 GPa
@Strain 10.5 %,
Temperature -40.0 °C		 84.6 ksi
@Strain 10.5 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  0.643 GPa
@Strain 0.440 %,
Temperature 40.0 °C		 93.3 ksi
@Strain 0.440 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  0.700 GPa
@Strain 9.00 %,
Temperature -40.0 °C		 102 ksi
@Strain 9.00 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  0.773 GPa
@Strain 0.110 %,
Temperature 40.0 °C		 112 ksi
@Strain 0.110 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  1.0125 GPa
@Strain 0.400 %,
Temperature 23.0 °C		 146.85 ksi
@Strain 0.400 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  1.02 GPa
@Strain 2.11 %,
Temperature 23.0 °C		 148 ksi
@Strain 2.11 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  1.18 GPa
@Strain 4.52 %,
Temperature -40.0 °C		 171 ksi
@Strain 4.52 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  1.29 GPa
@Strain 1.36 %,
Temperature 0.000 °C		 188 ksi
@Strain 1.36 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  1.4125 GPa
@Strain 0.0800 %,
Temperature 23.0 °C		 204.87 ksi
@Strain 0.0800 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  1.50 GPa
@Strain 0.230 %,
Temperature 0.000 °C		 217 ksi
@Strain 0.230 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  1.5125 GPa
@Strain 0.0800 %,
Temperature 0.000 °C		 219.37 ksi
@Strain 0.0800 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  1.54 GPa
@Strain 3.08 %,
Temperature -40.0 °C		 223 ksi
@Strain 3.08 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  1.7625 GPa
@Strain 0.240 %,
Temperature -20.0 °C		 255.63 ksi
@Strain 0.240 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  2.10 GPa
@Strain 0.710 %,
Temperature -40.0 °C		 305 ksi
@Strain 0.710 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  2.22 GPa
@Strain 0.0600 %,
Temperature -20.0 °C		 322 ksi
@Strain 0.0600 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  2.31 GPa
@Strain 0.230 %,
Temperature -40.0 °C		 335 ksi
@Strain 0.230 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  27.0 kJ/m² 12.8 ft-lb/in² DAM; ISO 180/1A
  66.0 kJ/m² 31.4 ft-lb/in² 50%RH; ISO 180/1A
  13.0 kJ/m²
@Temperature -30.0 °C		 6.19 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
  13.0 kJ/m²
@Temperature -30.0 °C		 6.19 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
Charpy Impact, Notched  4.00 J/cm² 19.0 ft-lb/in² DAM; ISO 179/1eA
  8.00 J/cm² 38.1 ft-lb/in² 50%RH; ISO 179/1eA
  1.50 J/cm²
@Temperature -30.0 °C		 7.14 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
  1.50 J/cm²
@Temperature -30.0 °C		 7.14 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
 
Thermal Properties Metric English Comments
Specific Heat Capacity  2.70 J/g-°C 0.645 BTU/lb-°F  
Thermal Conductivity  0.170 W/m-K 1.18 BTU-in/hr-ft²-°F of melt
Melting Point  218 °C 424 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  85.0 °C 185 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  46.0 °C 115 °F DAM; ISO 75-1/-2
 
Descriptive Properties
Delivery form Pellets  
Part Marking Code >PA612-HI< ISO 11469
Processing Film Extrusion  
  Other Extrusion  
  Profile Extrusion  
  Sheet Extrusion  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA612-HI  
  PA612-HI ISO 1043
Special characteristics Heat stabilised or stable to heat  

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39989.html

免责声明: 本文 高粘度 高韧性PA612/美国杜邦/LC6200 BK385 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4