| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | |||
| 1.60 g/cc | 0.0578 lb/in³ | DAM; ISO 1183 | |||
| Moisture Absorption | 0.700 % @Thickness 2.00 mm |
0.700 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Viscosity | 79440 cP @Shear Rate 5000 1/s, Temperature 280 °C |
79440 cP @Shear Rate 5000 1/s, Temperature 536 °F |
ISO 11403-1 -2 | ||
| 101000 cP @Shear Rate 5000 1/s, Temperature 270 °C |
101000 cP @Shear Rate 5000 1/s, Temperature 518 °F |
ISO 11403-1 -2 | |||
| 131520 cP @Shear Rate 5000 1/s, Temperature 260 °C |
131520 cP @Shear Rate 5000 1/s, Temperature 500 °F |
ISO 11403-1 -2 | |||
| 259970 cP @Shear Rate 500 1/s, Temperature 280 °C |
259970 cP @Shear Rate 500 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| 350400 cP @Shear Rate 500 1/s, Temperature 270 °C |
350400 cP @Shear Rate 500 1/s, Temperature 518 °F |
ISO 11403-1 -2 | |||
| 474700 cP @Shear Rate 500 1/s, Temperature 260 °C |
474700 cP @Shear Rate 500 1/s, Temperature 500 °F |
ISO 11403-1 -2 | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 170 MPa | 24700 psi | DAM; ISO 527-1/-2 | ||
| Tensile Stress | 3.79 MPa @Strain 0.100 %, Temperature 150 °C |
550 psi @Strain 0.100 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | ||
| 8.28 MPa @Strain 0.100 %, Temperature -40.0 °C |
1200 psi @Strain 0.100 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 9.09 MPa @Strain 0.100 %, Temperature 23.0 °C |
1320 psi @Strain 0.100 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 32.28 MPa @Strain 0.400 %, Temperature -40.0 °C |
4682 psi @Strain 0.400 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 32.69 MPa @Strain 0.700 %, Temperature 150 °C |
4741 psi @Strain 0.700 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 34.85 MPa @Strain 0.400 %, Temperature 23.0 °C |
5055 psi @Strain 0.400 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 47.98 MPa @Strain 1.30 %, Temperature 150 °C |
6959 psi @Strain 1.30 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 57.17 MPa @Strain 1.90 %, Temperature 150 °C |
8292 psi @Strain 1.90 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 61.31 MPa @Strain 0.700 %, Temperature -40.0 °C |
8892 psi @Strain 0.700 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 63.02 MPa @Strain 0.700 %, Temperature 23.0 °C |
9140 psi @Strain 0.700 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 68.67 MPa @Strain 3.70 %, Temperature 150 °C |
9960 psi @Strain 3.70 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 87.65 MPa @Strain 1.00 %, Temperature 23.0 °C |
12710 psi @Strain 1.00 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 88.75 MPa @Strain 1.00 %, Temperature -40.0 °C |
12870 psi @Strain 1.00 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 141.41 MPa @Strain 2.00 %, Temperature 23.0 °C |
20510 psi @Strain 2.00 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 186.16 MPa @Strain 2.60 %, Temperature -40.0 °C |
27000 psi @Strain 2.60 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| Elongation at Break | 2.5 % | 2.5 % | DAM; ISO 527-1/-2 | ||
| Tensile Modulus | 7.50 GPa | 1090 ksi | 50%RH; ISO 527-1/-2 | ||
| 10.64 GPa | 1543 ksi | DAM; ISO 527-1/-2 | |||
| Flexural Modulus | 9.45 GPa | 1370 ksi | DAM; ISO 178 | ||
| Secant Modulus | 2.77 GPa @Strain 2.90 %, Temperature 100 °C |
402 ksi @Strain 2.90 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | ||
| 3.45 GPa @Strain 2.10 %, Temperature 100 °C |
500 ksi @Strain 2.10 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 4.35 GPa @Strain 1.30 %, Temperature 100 °C |
631 ksi @Strain 1.30 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 5.892 GPa @Strain 0.500 %, Temperature 100 °C |
854.6 ksi @Strain 0.500 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 6.60 GPa @Strain 0.100 %, Temperature 100 °C |
957 ksi @Strain 0.100 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 7.80 GPa @Strain 1.60 %, Temperature 23.0 °C |
1130 ksi @Strain 1.60 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 7.9245 GPa @Strain 2.00 %, Temperature -40.0 °C |
1149.4 ksi @Strain 2.00 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 8.07 GPa @Strain 0.400 %, Temperature -40.0 °C |
1170 ksi @Strain 0.400 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 8.28 GPa @Strain 0.100 %, Temperature -40.0 °C |
1200 ksi @Strain 0.100 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 8.46 GPa @Strain 1.20 %, Temperature 23.0 °C |
1230 ksi @Strain 1.20 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 8.7125 GPa @Strain 0.400 %, Temperature 23.0 °C |
1263.7 ksi @Strain 0.400 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 8.81 GPa @Strain 1.20 %, Temperature -40.0 °C |
1280 ksi @Strain 1.20 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 8.84 GPa @Strain 0.800 %, Temperature -40.0 °C |
1280 ksi @Strain 0.800 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 8.975 GPa @Strain 0.800 %, Temperature 23.0 °C |
1302 ksi @Strain 0.800 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 9.09 GPa @Strain 0.100 %, Temperature 23.0 °C |
1320 ksi @Strain 0.100 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 1.13 J/cm² | 5.38 ft-lb/in² | DAM; ISO 179/1eA | ||
| 1.08 J/cm² @Temperature -40.0 °C |
5.14 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | DAM; IEC 60093 | ||
| Dielectric Strength | 38.0 kV/mm | 965 kV/in | DAM; IEC 60243-1 | ||
| Dissipation Factor | 0.018 @Frequency 100 Hz |
0.018 @Frequency 100 Hz |
DAM; IEC 60250 | ||
| 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
DAM; IEC 60250 | |||
| Comparative Tracking Index | 285 V | 285 V | DAM; IEC 60112 | ||
| 250 - 400 V | 250 - 400 V | DAM; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C | 10.6 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.66 J/g-°C | 0.397 BTU/lb-°F | |||
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | of melt | ||
| Melting Point | 261 °C | 502 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 256 °C | 493 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | DAM; 10°C/min; DS; ISO 11357-1/-2 | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | ||
| V-0 @Thickness 0.300 mm |
V-0 @Thickness 0.0118 in |
DAM; IEC 60695-11-10 | |||
| 5VA @Thickness 1.50 mm |
5VA @Thickness 0.0591 in |
DAM; IEC 60695-11-20 | |||
| De |
|||||
| Additives | Release agent | ||||
| Delivery form | Pellets | ||||
| Emission of organic compounds | 4.7 µgC/g | VDA 277 | |||
| Odour | class 4.5 | VDA 270 | |||
| Part Marking Code | >PA66-GF25FR(17)< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA66-GF25FR(17) | ||||
| UL recognition | UL | DAM | |||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。
上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！
可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：
联系人：邓小姐
联系电话：13917657923
联系QQ:996152797
联系邮箱：996152797@qq.com