Physical Properties Metric English Comments
Density  1.14 g/cc 0.0412 lb/in³ DAM; ISO 1183
Water Absorption   2.7 %
@Temperature 23.0 °C		 2.7 %
@Temperature 73.4 °F		 Equilibrium 50%RH; DAM; ISO 62, Similar to
  8.5 %
@Temperature 23.0 °C		 8.5 %
@Temperature 73.4 °F		 Saturation, immersed; DAM; ISO 62, Similar to
Viscosity   109000 cP
@Shear Rate 7000 1/s,
Temperature 305 °C		 109000 cP
@Shear Rate 7000 1/s,
Temperature 581 °F		 DAM; ISO 11443
  119000 cP
@Shear Rate 7000 1/s,
Temperature 295 °C		 119000 cP
@Shear Rate 7000 1/s,
Temperature 563 °F		 DAM; ISO 11443
  136000 cP
@Shear Rate 5000 1/s,
Temperature 305 °C		 136000 cP
@Shear Rate 5000 1/s,
Temperature 581 °F		 DAM; ISO 11443
  144000 cP
@Shear Rate 7000 1/s,
Temperature 275 °C		 144000 cP
@Shear Rate 7000 1/s,
Temperature 527 °F		 DAM; ISO 11443
  150000 cP
@Shear Rate 5000 1/s,
Temperature 295 °C		 150000 cP
@Shear Rate 5000 1/s,
Temperature 563 °F		 DAM; ISO 11443
  182000 cP
@Shear Rate 5000 1/s,
Temperature 275 °C		 182000 cP
@Shear Rate 5000 1/s,
Temperature 527 °F		 DAM; ISO 11443
  243000 cP
@Shear Rate 2000 1/s,
Temperature 305 °C		 243000 cP
@Shear Rate 2000 1/s,
Temperature 581 °F		 DAM; ISO 11443
  274000 cP
@Shear Rate 2000 1/s,
Temperature 295 °C		 274000 cP
@Shear Rate 2000 1/s,
Temperature 563 °F		 DAM; ISO 11443
  342000 cP
@Shear Rate 2000 1/s,
Temperature 275 °C		 342000 cP
@Shear Rate 2000 1/s,
Temperature 527 °F		 DAM; ISO 11443
  360000 cP
@Shear Rate 1000 1/s,
Temperature 305 °C		 360000 cP
@Shear Rate 1000 1/s,
Temperature 581 °F		 DAM; ISO 11443
  413000 cP
@Shear Rate 1000 1/s,
Temperature 295 °C		 413000 cP
@Shear Rate 1000 1/s,
Temperature 563 °F		 DAM; ISO 11443
  431000 cP
@Shear Rate 700 1/s,
Temperature 305 °C		 431000 cP
@Shear Rate 700 1/s,
Temperature 581 °F		 DAM; ISO 11443
  501000 cP
@Shear Rate 700 1/s,
Temperature 295 °C		 501000 cP
@Shear Rate 700 1/s,
Temperature 563 °F		 DAM; ISO 11443
  504000 cP
@Shear Rate 500 1/s,
Temperature 305 °C		 504000 cP
@Shear Rate 500 1/s,
Temperature 581 °F		 DAM; ISO 11443
  535000 cP
@Shear Rate 1000 1/s,
Temperature 275 °C		 535000 cP
@Shear Rate 1000 1/s,
Temperature 527 °F		 DAM; ISO 11443
  593000 cP
@Shear Rate 500 1/s,
Temperature 295 °C		 593000 cP
@Shear Rate 500 1/s,
Temperature 563 °F		 DAM; ISO 11443
  664000 cP
@Shear Rate 700 1/s,
Temperature 275 °C		 664000 cP
@Shear Rate 700 1/s,
Temperature 527 °F		 DAM; ISO 11443
  806000 cP
@Shear Rate 500 1/s,
Temperature 275 °C		 806000 cP
@Shear Rate 500 1/s,
Temperature 527 °F		 DAM; ISO 11443
Linear Mold Shrinkage, Flow  0.014 cm/cm
@Thickness 2.00 mm		 0.014 in/in
@Thickness 0.0787 in		 DAM; ISO 294-4
Linear Mold Shrinkage, Transverse  0.014 cm/cm
@Thickness 2.00 mm		 0.014 in/in
@Thickness 0.0787 in		 DAM; ISO 294-4
 
Mechanical Properties Metric English Comments
Tensile Stress   13.4 MPa
@Strain 3.00 %,
Temperature 90.0 °C		 1940 psi
@Strain 3.00 %,
Temperature 194 °F		 50%RH; ISO 527
  14.5 MPa
@Strain 5.00 %,
Temperature 120 °C		 2100 psi
@Strain 5.00 %,
Temperature 248 °F		 50%RH; ISO 527
  15.9 MPa
@Strain 3.00 %,
Temperature 60.0 °C		 2310 psi
@Strain 3.00 %,
Temperature 140 °F		 50%RH; ISO 527
  17.6 MPa
@Strain 5.00 %,
Temperature 120 °C		 2550 psi
@Strain 5.00 %,
Temperature 248 °F		 DAM; ISO 527
  19.7 MPa
@Strain 3.00 %,
Temperature 40.0 °C		 2860 psi
@Strain 3.00 %,
Temperature 104 °F		 50%RH; ISO 527
  20.9 MPa
@Strain 10.0 %,
Temperature 120 °C		 3030 psi
@Strain 10.0 %,
Temperature 248 °F		 50%RH; ISO 527
  21.1 MPa
@Strain 6.00 %,
Temperature 90.0 °C		 3060 psi
@Strain 6.00 %,
Temperature 194 °F		 50%RH; ISO 527
  21.8 MPa
@Strain 5.00 %,
Temperature 90.0 °C		 3160 psi
@Strain 5.00 %,
Temperature 194 °F		 DAM; ISO 527
  22.4 MPa
@Strain 0.800 %,
Temperature 40.0 °C		 3250 psi
@Strain 0.800 %,
Temperature 104 °F		 DAM; ISO 527
  23.5 MPa
@Strain 10.0 %,
Temperature 120 °C		 3410 psi
@Strain 10.0 %,
Temperature 248 °F		 DAM; ISO 527
  24.2 MPa
@Strain 15.0 %,
Temperature 120 °C		 3510 psi
@Strain 15.0 %,
Temperature 248 °F		 50%RH; ISO 527
  24.8 MPa
@Strain 6.00 %,
Temperature 60.0 °C		 3600 psi
@Strain 6.00 %,
Temperature 140 °F		 50%RH; ISO 527
  24.9 MPa
@Strain 0.800 %,
Temperature 23.0 °C		 3610 psi
@Strain 0.800 %,
Temperature 73.4 °F		 DAM; ISO 527
  25.8 MPa
@Strain 9.00 %,
Temperature 90.0 °C		 3740 psi
@Strain 9.00 %,
Temperature 194 °F		 50%RH; ISO 527
  26.1 MPa
@Strain 20.0 %,
Temperature 120 °C		 3790 psi
@Strain 20.0 %,
Temperature 248 °F		 50%RH; ISO 527
  26.3 MPa
@Strain 15.0 %,
Temperature 120 °C		 3810 psi
@Strain 15.0 %,
Temperature 248 °F		 DAM; ISO 527
  27.2 MPa
@Strain 25.0 %,
Temperature 120 °C		 3950 psi
@Strain 25.0 %,
Temperature 248 °F		 50%RH; ISO 527
  27.2 MPa
@Strain 3.00 %,
Temperature 60.0 °C		 3950 psi
@Strain 3.00 %,
Temperature 140 °F		 DAM; ISO 527
  27.9 MPa
@Strain 30.0 %,
Temperature 120 °C		 4050 psi
@Strain 30.0 %,
Temperature 248 °F		 50%RH; ISO 527
  27.9 MPa
@Strain 20.0 %,
Temperature 120 °C		 4050 psi
@Strain 20.0 %,
Temperature 248 °F		 DAM; ISO 527
  28.2 MPa
@Strain 35.0 %,
Temperature 120 °C		 4090 psi
@Strain 35.0 %,
Temperature 248 °F		 50%RH; ISO 527
  28.3 MPa
@Strain 40.0 %,
Temperature 120 °C		 4100 psi
@Strain 40.0 %,
Temperature 248 °F		 50%RH; ISO 527
  28.4 MPa
@Strain 45.0 %,
Temperature 120 °C		 4120 psi
@Strain 45.0 %,
Temperature 248 °F		 50%RH; ISO 527
  28.5 MPa
@Strain 50.0 %,
Temperature 120 °C		 4130 psi
@Strain 50.0 %,
Temperature 248 °F		 50%RH; ISO 527
  28.5 MPa
@Strain 3.00 %,
Temperature 23.0 °C		 4130 psi
@Strain 3.00 %,
Temperature 73.4 °F		 50%RH; ISO 527
  28.8 MPa
@Strain 12.0 %,
Temperature 90.0 °C		 4180 psi
@Strain 12.0 %,
Temperature 194 °F		 50%RH; ISO 527
  28.9 MPa
@Strain 25.0 %,
Temperature 120 °C		 4190 psi
@Strain 25.0 %,
Temperature 248 °F		 DAM; ISO 527
  29.6 MPa
@Strain 30.0 %,
Temperature 120 °C		 4290 psi
@Strain 30.0 %,
Temperature 248 °F		 DAM; ISO 527
  29.6 MPa
@Strain 10.0 %,
Temperature 90.0 °C		 4290 psi
@Strain 10.0 %,
Temperature 194 °F		 DAM; ISO 527
  30.0 MPa
@Strain 35.0 %,
Temperature 120 °C		 4350 psi
@Strain 35.0 %,
Temperature 248 °F		 DAM; ISO 527
  30.1 MPa
@Strain 6.00 %,
Temperature 40.0 °C		 4370 psi
@Strain 6.00 %,
Temperature 104 °F		 50%RH; ISO 527
  30.3 MPa
@Strain 9.00 %,
Temperature 60.0 °C		 4390 psi
@Strain 9.00 %,
Temperature 140 °F		 50%RH; ISO 527
  30.4 MPa
@Strain 40.0 %,
Temperature 120 °C		 4410 psi
@Strain 40.0 %,
Temperature 248 °F		 DAM; ISO 527
  30.6 MPa
@Strain 45.0 %,
Temperature 120 °C		 4440 psi
@Strain 45.0 %,
Temperature 248 °F		 DAM; ISO 527
  30.7 MPa
@Strain 50.0 %,
Temperature 120 °C		 4450 psi
@Strain 50.0 %,
Temperature 248 °F		 DAM; ISO 527
  30.7 MPa
@Strain 15.0 %,
Temperature 90.0 °C		 4450 psi
@Strain 15.0 %,
Temperature 194 °F		 50%RH; ISO 527
  31.9 MPa
@Strain 18.0 %,
Temperature 90.0 °C		 4630 psi
@Strain 18.0 %,
Temperature 194 °F		 50%RH; ISO 527
  32.7 MPa
@Strain 21.0 %,
Temperature 90.0 °C		 4740 psi
@Strain 21.0 %,
Temperature 194 °F		 50%RH; ISO 527
  33.1 MPa
@Strain 24.0 %,
Temperature 90.0 °C		 4800 psi
@Strain 24.0 %,
Temperature 194 °F		 50%RH; ISO 527
  33.3 MPa
@Strain 27.0 %,
Temperature 90.0 °C		 4830 psi
@Strain 27.0 %,
Temperature 194 °F		 50%RH; ISO 527
  33.4 MPa
@Strain 30.0 %,
Temperature 90.0 °C		 4840 psi
@Strain 30.0 %,
Temperature 194 °F		 50%RH; ISO 527
  33.4 MPa
@Strain 15.0 %,
Temperature 90.0 °C		 4840 psi
@Strain 15.0 %,
Temperature 194 °F		 DAM; ISO 527
  33.8 MPa
@Strain 12.0 %,
Temperature 60.0 °C		 4900 psi
@Strain 12.0 %,
Temperature 140 °F		 50%RH; ISO 527
  35.6 MPa
@Strain 20.0 %,
Temperature 90.0 °C		 5160 psi
@Strain 20.0 %,
Temperature 194 °F		 DAM; ISO 527
  36.2 MPa
@Strain 15.0 %,
Temperature 60.0 °C		 5250 psi
@Strain 15.0 %,
Temperature 140 °F		 50%RH; ISO 527
  36.2 MPa
@Strain 9.00 %,
Temperature 40.0 °C		 5250 psi
@Strain 9.00 %,
Temperature 104 °F		 50%RH; ISO 527
  36.9 MPa
@Strain 25.0 %,
Temperature 90.0 °C		 5350 psi
@Strain 25.0 %,
Temperature 194 °F		 DAM; ISO 527
  37.7 MPa
@Strain 18.0 %,
Temperature 60.0 °C		 5470 psi
@Strain 18.0 %,
Temperature 140 °F		 50%RH; ISO 527
  37.7 MPa
@Strain 30.0 %,
Temperature 90.0 °C		 5470 psi
@Strain 30.0 %,
Temperature 194 °F		 DAM; ISO 527
  38.2 MPa
@Strain 35.0 %,
Temperature 90.0 °C		 5540 psi
@Strain 35.0 %,
Temperature 194 °F		 DAM; ISO 527
  38.4 MPa
@Strain 6.00 %,
Temperature 60.0 °C		 5570 psi
@Strain 6.00 %,
Temperature 140 °F		 DAM; ISO 527
  38.5 MPa
@Strain 40.0 %,
Temperature 90.0 °C		 5580 psi
@Strain 40.0 %,
Temperature 194 °F		 DAM; ISO 527
  38.6 MPa
@Strain 45.0 %,
Temperature 90.0 °C		 5600 psi
@Strain 45.0 %,
Temperature 194 °F		 DAM; ISO 527
  38.7 MPa
@Strain 50.0 %,
Temperature 90.0 °C		 5610 psi
@Strain 50.0 %,
Temperature 194 °F		 DAM; ISO 527
  38.7 MPa
@Strain 21.0 %,
Temperature 60.0 °C		 5610 psi
@Strain 21.0 %,
Temperature 140 °F		 50%RH; ISO 527
  39.4 MPa
@Strain 24.0 %,
Temperature 60.0 °C		 5710 psi
@Strain 24.0 %,
Temperature 140 °F		 50%RH; ISO 527
  39.5 MPa
@Strain 1.20 %,
Temperature 0.000 °C		 5730 psi
@Strain 1.20 %,
Temperature 32.0 °F		 DAM; ISO 527
  39.8 MPa
@Strain 27.0 %,
Temperature 60.0 °C		 5770 psi
@Strain 27.0 %,
Temperature 140 °F		 50%RH; ISO 527
  40.0 MPa
@Strain 30.0 %,
Temperature 60.0 °C		 5800 psi
@Strain 30.0 %,
Temperature 140 °F		 50%RH; ISO 527
  40.1 MPa
@Strain 12.0 %,
Temperature 40.0 °C		 5820 psi
@Strain 12.0 %,
Temperature 104 °F		 50%RH; ISO 527
  41.3 MPa
@Strain 6.00 %,
Temperature 23.0 °C		 5990 psi
@Strain 6.00 %,
Temperature 73.4 °F		 50%RH; ISO 527
  41.6 MPa
@Strain 1.60 %,
Temperature 40.0 °C		 6030 psi
@Strain 1.60 %,
Temperature 104 °F		 DAM; ISO 527
  42.6 MPa
@Strain 15.0 %,
Temperature 40.0 °C		 6180 psi
@Strain 15.0 %,
Temperature 104 °F		 50%RH; ISO 527
  43.7 MPa
@Strain 1.20 %,
Temperature -20.0 °C		 6340 psi
@Strain 1.20 %,
Temperature -4.00 °F		 DAM; ISO 527
  44.2 MPa
@Strain 9.00 %,
Temperature 60.0 °C		 6410 psi
@Strain 9.00 %,
Temperature 140 °F		 DAM; ISO 527
  44.4 MPa
@Strain 18.0 %,
Temperature 40.0 °C		 6440 psi
@Strain 18.0 %,
Temperature 104 °F		 50%RH; ISO 527
  45.5 MPa
@Strain 21.0 %,
Temperature 40.0 °C		 6600 psi
@Strain 21.0 %,
Temperature 104 °F		 50%RH; ISO 527
  46.3 MPa
@Strain 24.0 %,
Temperature 40.0 °C		 6720 psi
@Strain 24.0 %,
Temperature 104 °F		 50%RH; ISO 527
  46.7 MPa
@Strain 27.0 %,
Temperature 40.0 °C		 6770 psi
@Strain 27.0 %,
Temperature 104 °F		 50%RH; ISO 527
  47.0 MPa
@Strain 30.0 %,
Temperature 40.0 °C		 6820 psi
@Strain 30.0 %,
Temperature 104 °F		 50%RH; ISO 527
  47.6 MPa
@Strain 12.0 %,
Temperature 60.0 °C		 6900 psi
@Strain 12.0 %,
Temperature 140 °F		 DAM; ISO 527
  48.2 MPa
@Strain 9.00 %,
Temperature 23.0 °C		 6990 psi
@Strain 9.00 %,
Temperature 73.4 °F		 50%RH; ISO 527
  48.5 MPa
@Strain 1.60 %,
Temperature 23.0 °C		 7030 psi
@Strain 1.60 %,
Temperature 73.4 °F		 DAM; ISO 527
  49.7 MPa
@Strain 15.0 %,
Temperature 60.0 °C		 7210 psi
@Strain 15.0 %,
Temperature 140 °F		 DAM; ISO 527
  51.0 MPa
@Strain 18.0 %,
Temperature 60.0 °C		 7400 psi
@Strain 18.0 %,
Temperature 140 °F		 DAM; ISO 527
  51.8 MPa
@Strain 21.0 %,
Temperature 60.0 °C		 7510 psi
@Strain 21.0 %,
Temperature 140 °F		 DAM; ISO 527
  52.2 MPa
@Strain 24.0 %,
Temperature 60.0 °C		 7570 psi
@Strain 24.0 %,
Temperature 140 °F		 DAM; ISO 527
  52.2 MPa
@Strain 12.0 %,
Temperature 23.0 °C		 7570 psi
@Strain 12.0 %,
Temperature 73.4 °F		 50%RH; ISO 527
  52.4 MPa
@Strain 27.0 %,
Temperature 60.0 °C		 7600 psi
@Strain 27.0 %,
Temperature 140 °F		 DAM; ISO 527
  52.4 MPa
@Strain 30.0 %,
Temperature 60.0 °C		 7600 psi
@Strain 30.0 %,
Temperature 140 °F		 DAM; ISO 527
  54.6 MPa
@Strain 15.0 %,
Temperature 23.0 °C		 7920 psi
@Strain 15.0 %,
Temperature 73.4 °F		 50%RH; ISO 527
  54.9 MPa
@Strain 2.40 %,
Temperature 40.0 °C		 7960 psi
@Strain 2.40 %,
Temperature 104 °F		 DAM; ISO 527
  56.1 MPa
@Strain 18.0 %,
Temperature 23.0 °C		 8140 psi
@Strain 18.0 %,
Temperature 73.4 °F		 50%RH; ISO 527
  57.0 MPa
@Strain 21.0 %,
Temperature 23.0 °C		 8270 psi
@Strain 21.0 %,
Temperature 73.4 °F		 50%RH; ISO 527
  57.0 MPa
@Strain 2.00 %,
Temperature 0.000 °C		 8270 psi
@Strain 2.00 %,
Temperature 32.0 °F		 50%RH; ISO 527
  57.5 MPa
@Strain 24.0 %,
Temperature 23.0 °C		 8340 psi
@Strain 24.0 %,
Temperature 73.4 °F		 50%RH; ISO 527
  57.7 MPa
@Strain 27.0 %,
Temperature 23.0 °C		 8370 psi
@Strain 27.0 %,
Temperature 73.4 °F		 50%RH; ISO 527
  57.9 MPa
@Strain 30.0 %,
Temperature 23.0 °C		 8400 psi
@Strain 30.0 %,
Temperature 73.4 °F		 50%RH; ISO 527
  58.9 MPa
@Strain 1.60 %,
Temperature -20.0 °C		 8540 psi
@Strain 1.60 %,
Temperature -4.00 °F		 50%RH; ISO 527
  63.0 MPa
@Strain 3.20 %,
Temperature 40.0 °C		 9140 psi
@Strain 3.20 %,
Temperature 104 °F		 DAM; ISO 527
  67.1 MPa
@Strain 4.00 %,
Temperature 40.0 °C		 9730 psi
@Strain 4.00 %,
Temperature 104 °F		 DAM; ISO 527
  67.5 MPa
@Strain 2.40 %,
Temperature 23.0 °C		 9790 psi
@Strain 2.40 %,
Temperature 73.4 °F		 DAM; ISO 527
  71.9 MPa
@Strain 2.40 %,
Temperature 0.000 °C		 10400 psi
@Strain 2.40 %,
Temperature 32.0 °F		 DAM; ISO 527
  72.0 MPa
@Strain 4.00 %,
Temperature 0.000 °C		 10400 psi
@Strain 4.00 %,
Temperature 32.0 °F		 50%RH; ISO 527
  75.8 MPa
@Strain 6.00 %,
Temperature 0.000 °C		 11000 psi
@Strain 6.00 %,
Temperature 32.0 °F		 50%RH; ISO 527
  75.8 MPa
@Strain 2.40 %,
Temperature -20.0 °C		 11000 psi
@Strain 2.40 %,
Temperature -4.00 °F		 DAM; ISO 527
  78.0 MPa
@Strain 8.00 %,
Temperature 0.000 °C		 11300 psi
@Strain 8.00 %,
Temperature 32.0 °F		 50%RH; ISO 527
  79.3 MPa
@Strain 10.0 %,
Temperature 0.000 °C		 11500 psi
@Strain 10.0 %,
Temperature 32.0 °F		 50%RH; ISO 527
  80.0 MPa
@Strain 3.20 %,
Temperature 23.0 °C		 11600 psi
@Strain 3.20 %,
Temperature 73.4 °F		 DAM; ISO 527
  80.1 MPa
@Strain 12.0 %,
Temperature 0.000 °C		 11600 psi
@Strain 12.0 %,
Temperature 32.0 °F		 50%RH; ISO 527
  80.6 MPa
@Strain 14.0 %,
Temperature 0.000 °C		 11700 psi
@Strain 14.0 %,
Temperature 32.0 °F		 50%RH; ISO 527
  80.9 MPa
@Strain 16.0 %,
Temperature 0.000 °C		 11700 psi
@Strain 16.0 %,
Temperature 32.0 °F		 50%RH; ISO 527
  81.1 MPa
@Strain 18.0 %,
Temperature 0.000 °C		 11800 psi
@Strain 18.0 %,
Temperature 32.0 °F		 50%RH; ISO 527
  81.2 MPa
@Strain 20.0 %,
Temperature 0.000 °C		 11800 psi
@Strain 20.0 %,
Temperature 32.0 °F		 50%RH; ISO 527
  86.5 MPa
@Strain 4.00 %,
Temperature 23.0 °C		 12500 psi
@Strain 4.00 %,
Temperature 73.4 °F		 DAM; ISO 527
  89.1 MPa
@Strain 3.20 %,
Temperature -20.0 °C		 12900 psi
@Strain 3.20 %,
Temperature -4.00 °F		 50%RH; ISO 527
  91.6 MPa
@Strain 3.60 %,
Temperature 0.000 °C		 13300 psi
@Strain 3.60 %,
Temperature 32.0 °F		 DAM; ISO 527
  96.5 MPa
@Strain 3.60 %,
Temperature -20.0 °C		 14000 psi
@Strain 3.60 %,
Temperature -4.00 °F		 DAM; ISO 527
  98.1 MPa
@Strain 4.80 %,
Temperature -20.0 °C		 14200 psi
@Strain 4.80 %,
Temperature -4.00 °F		 50%RH; ISO 527
  100 MPa
@Strain 6.40 %,
Temperature -20.0 °C		 14500 psi
@Strain 6.40 %,
Temperature -4.00 °F		 50%RH; ISO 527
  100 MPa
@Strain 4.80 %,
Temperature 0.000 °C		 14500 psi
@Strain 4.80 %,
Temperature 32.0 °F		 DAM; ISO 527
  100 MPa
@Strain 6.00 %,
Temperature 0.000 °C		 14500 psi
@Strain 6.00 %,
Temperature 32.0 °F		 DAM; ISO 527
  101 MPa
@Strain 8.00 %,
Temperature -20.0 °C		 14600 psi
@Strain 8.00 %,
Temperature -4.00 °F		 50%RH; ISO 527
  108 MPa
@Strain 4.80 %,
Temperature -20.0 °C		 15700 psi
@Strain 4.80 %,
Temperature -4.00 °F		 DAM; ISO 527
  113 MPa
@Strain 6.00 %,
Temperature -20.0 °C		 16400 psi
@Strain 6.00 %,
Temperature -4.00 °F		 DAM; ISO 527
Tensile Strength, Yield   52.0 MPa
@Temperature 23.0 °C		 7540 psi
@Temperature 73.4 °F		 50%RH; ISO 527
  86.0 MPa
@Temperature 23.0 °C		 12500 psi
@Temperature 73.4 °F		 DAM; ISO 527
Elongation at Break   >= 50 %
@Temperature 23.0 °C		 >= 50 %
@Temperature 73.4 °F		 50%RH; nominal; ISO 527
  >= 50 %
@Temperature 23.0 °C		 >= 50 %
@Temperature 73.4 °F		 DAM; nominal; ISO 527
Elongation at Yield   5.0 %
@Temperature 23.0 °C		 5.0 %
@Temperature 73.4 °F		 DAM; ISO 527
  27 %
@Temperature 23.0 °C		 27 %
@Temperature 73.4 °F		 50%RH; ISO 527
Tensile Modulus   1.20 GPa
@Temperature 23.0 °C		 174 ksi
@Temperature 73.4 °F		 50%RH; ISO 527
  3.10 GPa
@Temperature 23.0 °C		 450 ksi
@Temperature 73.4 °F		 DAM; ISO 527
Shear Modulus   0.0400 GPa
@Temperature 250 °C		 5.80 ksi
@Temperature 482 °F		 DAM; ISO 6721
  0.0630 GPa
@Temperature 240 °C		 9.14 ksi
@Temperature 464 °F		 DAM; ISO 6721
  0.0830 GPa
@Temperature 230 °C		 12.0 ksi
@Temperature 446 °F		 DAM; ISO 6721
  0.0980 GPa
@Temperature 220 °C		 14.2 ksi
@Temperature 428 °F		 DAM; ISO 6721
  0.107 GPa
@Temperature 210 °C		 15.5 ksi
@Temperature 410 °F		 DAM; ISO 6721
  0.114 GPa
@Temperature 200 °C		 16.5 ksi
@Temperature 392 °F		 DAM; ISO 6721
  0.120 GPa
@Temperature 190 °C		 17.4 ksi
@Temperature 374 °F		 DAM; ISO 6721
  0.125 GPa
@Temperature 180 °C		 18.1 ksi
@Temperature 356 °F		 DAM; ISO 6721
  0.130 GPa
@Temperature 170 °C		 18.9 ksi
@Temperature 338 °F		 DAM; ISO 6721
  0.135 GPa
@Temperature 160 °C		 19.6 ksi
@Temperature 320 °F		 DAM; ISO 6721
  0.139 GPa
@Temperature 150 °C		 20.2 ksi
@Temperature 302 °F		 DAM; ISO 6721
  0.144 GPa
@Temperature 140 °C		 20.9 ksi
@Temperature 284 °F		 DAM; ISO 6721
  0.148 GPa
@Temperature 130 °C		 21.5 ksi
@Temperature 266 °F		 DAM; ISO 6721
  0.153 GPa
@Temperature 120 °C		 22.2 ksi
@Temperature 248 °F		 DAM; ISO 6721
  0.159 GPa
@Temperature 110 °C		 23.1 ksi
@Temperature 230 °F		 DAM; ISO 6721
  0.171 GPa
@Temperature 100 °C		 24.8 ksi
@Temperature 212 °F		 DAM; ISO 6721
  0.191 GPa
@Temperature 90.0 °C		 27.7 ksi
@Temperature 194 °F		 DAM; ISO 6721
  0.233 GPa
@Temperature 80.0 °C		 33.8 ksi
@Temperature 176 °F		 DAM; ISO 6721
  0.322 GPa
@Temperature 70.0 °C		 46.7 ksi
@Temperature 158 °F		 DAM; ISO 6721
  0.431 GPa
@Temperature 60.0 °C		 62.5 ksi
@Temperature 140 °F		 DAM; ISO 6721
  0.667 GPa
@Temperature 50.0 °C		 96.7 ksi
@Temperature 122 °F		 DAM; ISO 6721
  0.776 GPa
@Temperature 40.0 °C		 113 ksi
@Temperature 104 °F		 DAM; ISO 6721
  0.834 GPa
@Temperature 30.0 °C		 121 ksi
@Temperature 86.0 °F		 DAM; ISO 6721
  0.880 GPa
@Temperature 20.0 °C		 128 ksi
@Temperature 68.0 °F		 DAM; ISO 6721
  0.915 GPa
@Temperature 10.0 °C		 133 ksi
@Temperature 50.0 °F		 DAM; ISO 6721
  0.938 GPa
@Temperature 0.000 °C		 136 ksi
@Temperature 32.0 °F		 DAM; ISO 6721
  0.951 GPa
@Temperature -10.0 °C		 138 ksi
@Temperature 14.0 °F		 DAM; ISO 6721
  0.961 GPa
@Temperature -20.0 °C		 139 ksi
@Temperature -4.00 °F		 DAM; ISO 6721
  0.975 GPa
@Temperature -30.0 °C		 141 ksi
@Temperature -22.0 °F		 DAM; ISO 6721
  0.999 GPa
@Temperature -40.0 °C		 145 ksi
@Temperature -40.0 °F		 DAM; ISO 6721
  1.04 GPa
@Temperature -50.0 °C		 151 ksi
@Temperature -58.0 °F		 DAM; ISO 6721
Izod Impact, Notched (ISO)   4.00 kJ/m²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
  4.30 kJ/m²
@Temperature -30.0 °C		 2.05 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
  5.60 kJ/m²
@Temperature 23.0 °C		 2.66 ft-lb/in²
@Temperature 73.4 °F		 DAM; ISO 180/1A
  11.9 kJ/m²@Temperature 23.0 °C 5.66 ft-lb/in²
@Temperature 73.4 °F		 50%RH; ISO 180/1A
Charpy Impact Unnotched   NB
@Temperature 23.0 °C		 NB
@Temperature 73.4 °F		 DAM; ISO 179/1eU
  NB
@Temperature 23.0 °C		 NB
@Temperature 73.4 °F		 50%RH; ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 DAM; ISO 179/1eU
Charpy Impact, Notched   0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
  0.500 J/cm²
@Temperature -30.0 °C		 2.38 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
  0.600 J/cm²
@Temperature 23.0 °C		 2.86 ft-lb/in²
@Temperature 73.4 °F		 DAM; ISO 179/1eA
  2.00 J/cm²
@Temperature 23.0 °C		 9.52 ft-lb/in²
@Temperature 73.4 °F		 50%RH; ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity   1.00e+11 ohm-cm
@Temperature 23.0 °C		 1.00e+11 ohm-cm
@Temperature 73.4 °F		 50%RH; IEC 60093
  1.00e+13 ohm-cm
@Temperature 23.0 °C		 1.00e+13 ohm-cm
@Temperature 73.4 °F		 DAM; IEC 60093
Dielectric Constant   3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		 3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		 DAM; IEC 60250
  4.2
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		 4.2
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		 50%RH; IEC 60250
  4.3
@Frequency 100 Hz,
Temperature 23.0 °C		 4.3
@Frequency 100 Hz,
Temperature 73.4 °F		 DAM; IEC 60250
  10.3
@Frequency 100 Hz,
Temperature 23.0 °C		 10.3
@Frequency 100 Hz,
Temperature 73.4 °F		 50%RH; IEC 60250
Dielectric Strength  30.5 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		 775 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		 DAM; IEC 60243-1
Dissipation Factor   0.015
@Frequency 100 Hz,
Temperature 23.0 °C		 0.015
@Frequency 100 Hz,
Temperature 73.4 °F		 DAM; IEC 60250
  0.024
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		 0.024
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		 DAM; IEC 60250
  0.075
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		 0.075
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		 50%RH; IEC 60250
  0.20
@Frequency 100 Hz,
Temperature 23.0 °C		 0.20
@Frequency 100 Hz,
Temperature 73.4 °F		 50%RH; IEC 60250
Comparative Tracking Index  >= 600 V
@Temperature 23.0 °C		 >= 600 V
@Temperature 73.4 °F		 DAM; UL 746A
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow   500 µm/m-°C
@Temperature 23.0 - 55.0 °C		 278 µin/in-°F
@Temperature 73.4 - 131 °F		 DAM; ASTM E 831
  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		 278 µin/in-°F
@Temperature 73.4 - 131 °F		 DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow   100 µm/m-°C
@Temperature 23.0 - 55.0 °C		 55.6 µin/in-°F
@Temperature 73.4 - 131 °F		 DAM; ISO 11359-1/-2
  100 µm/m-°C
@Temperature 23.0 - 55.0 °C		 55.6 µin/in-°F
@Temperature 73.4 - 131 °F		 DAM; ASTM E 831
Melting Point  263 °C 505 °F 10°C/min; DAM; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  205 °C 401 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  72.0 °C 162 °F DAM; ISO 75-1/-2
Flammability, UL94   HB
@Thickness 0.810 mm		 HB
@Thickness 0.0319 in		 DAM; IEC 60695-11-10
  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; UL94
  HB
@Thickness 0.810 mm		 HB
@Thickness 0.0319 in		 DAM; UL94
  V-2
@Thickness 3.00 mm		 V-2
@Thickness 0.118 in		 DAM; IEC 60695-11-10
  V-2
@Thickness 3.00 mm		 V-2
@Thickness 0.118 in		 DAM; UL94
 
Processing Properties Metric English Comments
Melt Temperature  290 °C 554 °F DAM; Optimum
  280 - 300 °C 536 - 572 °F DAM
Mold Temperature  70.0 °C 158 °F DAM; optimum
  50.0 - 90.0 °C 122 - 194 °F DAM
Drying Temperature  80.0 °C 176 °F DAM
Dry Time  2.00 - 4.00 hour 2.00 - 4.00 hour DAM
Moisture Content  <= 0.050 % <= 0.050 % DAM
 
Descriptive Properties
Drying Recommended Yes, if moisture content of resin exceeds recommended level DAM
Forms Pellets DAM
Generic Nylon 66 DAM
Material Status Preliminary Data DAM
Part Marking Code >PA66< ISO 11469; DAM
Processing Method Extrusion DAM
  Injection Molding DAM
Product Category Extrusion Resins DAM
  Unreinforced Resins DAM
Resin Identification PA66 ISO 1043; DAM
RoHS Compliance Contact Manufacturer DAM

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39995.html

免责声明: 本文 PA66/美国杜邦/E42A NC010 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4