  4. PBT/美国杜邦/HR5330HF NC010 耐磨 耐高温

PBT/美国杜邦/HR5330HF NC010 耐磨 耐高温

PBT/美国杜邦/HR5330HF NC010 耐磨 耐高温
 参考图片：

颗粒图片：

包装图片：

成品图片：

8-1031642-801394

 

 

 

Physical Properties Metric English Comments
Density  1.29 g/cc 0.0466 lb/in³  
  1.50 g/cc 0.0542 lb/in³ ISO 1183
Water Absorption  0.35 %
@Thickness 2.00 mm		 0.35 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.150 %
@Thickness 2.00 mm		 0.150 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   68560 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 68560 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  79300 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 79300 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  92760 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 92760 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  221300 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 221300 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  260930 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 260930 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  310000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 310000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Viscosity Test  95 cm³/g 95 cm³/g ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.010 cm/cm 0.010 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  132 MPa 19100 psi ISO 527-1/-2
Tensile Stress   11.63 MPa
@Strain 0.370 %,
Temperature 150 °C		 1687 psi
@Strain 0.370 %,
Temperature 302 °F		 ISO 11403-1 -2
  18.68 MPa
@Strain 0.400 %,
Temperature 90.0 °C		 2709 psi
@Strain 0.400 %,
Temperature 194 °F		 ISO 11403-1 -2
  24.27 MPa
@Strain 0.360 %,
Temperature 40.0 °C		 3520 psi
@Strain 0.360 %,
Temperature 104 °F		 ISO 11403-1 -2
  28.72 MPa
@Strain 1.24 %,
Temperature 150 °C		 4165 psi
@Strain 1.24 %,
Temperature 302 °F		 ISO 11403-1 -2
  35.72 MPa
@Strain 0.440 %,
Temperature 23.0 °C		 5181 psi
@Strain 0.440 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  38.12 MPa
@Strain 0.420 %,
Temperature 0.000 °C		 5529 psi
@Strain 0.420 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  38.53 MPa
@Strain 2.20 %,
Temperature 150 °C		 5588 psi
@Strain 2.20 %,
Temperature 302 °F		 ISO 11403-1 -2
  41.17 MPa
@Strain 1.10 %,
Temperature 90.0 °C		 5971 psi
@Strain 1.10 %,
Temperature 194 °F		 ISO 11403-1 -2
  44.43 MPa
@Strain 3.16 %,
Temperature 150 °C		 6444 psi
@Strain 3.16 %,
Temperature 302 °F		 ISO 11403-1 -2
  53.57 MPa
@Strain 6.46 %,
Temperature 150 °C		 7770 psi
@Strain 6.46 %,
Temperature 302 °F		 ISO 11403-1 -2
  55.58 MPa
@Strain 0.920 %,
Temperature 40.0 °C		 8061 psi
@Strain 0.920 %,
Temperature 104 °F		 ISO 11403-1 -2
  55.85 MPa
@Strain 1.87 %,
Temperature 90.0 °C		 8100 psi
@Strain 1.87 %,
Temperature 194 °F		 ISO 11403-1 -2
  62.8 MPa
@Strain 0.660 %,
Temperature -20.0 °C		 9110 psi
@Strain 0.660 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  64.86 MPa
@Strain 2.72 %,
Temperature 90.0 °C		 9407 psi
@Strain 2.72 %,
Temperature 194 °F		 ISO 11403-1 -2
  68.1 MPa
@Strain 0.880 %,
Temperature 23.0 °C		 9880 psi
@Strain 0.880 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  75.05 MPa
@Strain 1.44 %,
Temperature 40.0 °C		 10890 psi
@Strain 1.44 %,
Temperature 104 °F		 ISO 11403-1 -2
  84.36 MPa
@Strain 0.960 %,
Temperature 0.000 °C		 12240 psi
@Strain 0.960 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  88.7 MPa
@Strain 1.99 %,
Temperature 40.0 °C		 12900 psi
@Strain 1.99 %,
Temperature 104 °F		 ISO 11403-1 -2
  89.21 MPa
@Strain 1.26 %,
Temperature 23.0 °C		 12940 psi
@Strain 1.26 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  99.12 MPa
@Strain 1.01 %,
Temperature -40.0 °C		 14380 psi
@Strain 1.01 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  107.95 MPa
@Strain 1.72 %,
Temperature 23.0 °C		 15657 psi
@Strain 1.72 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  109.81 MPa
@Strain 1.33 %,
Temperature 0.000 °C		 15927 psi
@Strain 1.33 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  111.73 MPa
@Strain 1.23 %,
Temperature -20.0 °C		 16205 psi
@Strain 1.23 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  132.69 MPa
@Strain 1.77 %,
Temperature 0.000 °C		 19245 psi
@Strain 1.77 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  140.62 MPa
@Strain 1.49 %,
Temperature -40.0 °C		 20395 psi
@Strain 1.49 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  147.79 MPa
@Strain 1.77 %,
Temperature -20.0 °C		 21435 psi
@Strain 1.77 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  169.84 MPa
@Strain 2.23 %,
Temperature -20.0 °C		 24633 psi
@Strain 2.23 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  170.93 MPa
@Strain 1.91 %,
Temperature -40.0 °C		 24791 psi
@Strain 1.91 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  197.31 MPa
@Strain 2.38 %,
Temperature -40.0 °C		 28617 psi
@Strain 2.38 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Elongation at Break  3.5 % 3.5 % ISO 527-1/-2
Tensile Modulus  8.50 GPa 1230 ksi ISO 527-1/-2
  3.672 GPa
@Temperature 120 °C		 532.6 ksi
@Temperature 248 °F		 ISO 11403-1 -2
  6.643 GPa
@Temperature 40.0 °C		 963.5 ksi
@Temperature 104 °F		 ISO 11403-1 -2
  9.965 GPa
@Temperature -40.0 °C		 1445 ksi
@Temperature -40.0 °F		 ISO 11403-1 -2
Flexural Strength  200 MPa 29000 psi ISO 178
Flexural Modulus  7.70 GPa 1120 ksi ISO 178
Shear Modulus  0.7794 GPa
@Temperature 100 °C		 113.0 ksi
@Temperature 212 °F		 Dynamic; ISO 11403-1 -2
  1.256 GPa
@Temperature 60.0 °C		 182.2 ksi
@Temperature 140 °F		 Dynamic; ISO 11403-1 -2
  1.966 GPa
@Temperature 10.0 °C		 285.1 ksi
@Temperature 50.0 °F		 Dynamic; ISO 11403-1 -2
  2.137 GPa
@Temperature -40.0 °C		 310.0 ksi
@Temperature -40.0 °F		 Dynamic; ISO 11403-1 -2
  2.331 GPa
@Temperature -70.0 °C		 338.1 ksi
@Temperature -94.0 °F		 Dynamic; ISO 11403-1 -2
  2.501 GPa
@Temperature -100 °C		 362.7 ksi
@Temperature -148 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   2.95 GPa
@Strain 3.47 %,
Temperature 40.0 °C		 428 ksi
@Strain 3.47 %,
Temperature 104 °F		 ISO 11403-1 -2
  3.97 GPa
@Strain 2.41 %,
Temperature 40.0 °C		 575 ksi
@Strain 2.41 %,
Temperature 104 °F		 ISO 11403-1 -2
  4.95 GPa
@Strain 1.62 %,
Temperature 40.0 °C		 717 ksi
@Strain 1.62 %,
Temperature 104 °F		 ISO 11403-1 -2
  5.47 GPa
@Strain 2.90 %,
Temperature 0.000 °C		 794 ksi
@Strain 2.90 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  5.71 GPa
@Strain 2.05 %,
Temperature 23.0 °C		 828 ksi
@Strain 2.05 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  6.0413 GPa
@Strain 0.920 %,
Temperature 40.0 °C		 876.23 ksi
@Strain 0.920 %,
Temperature 104 °F		 ISO 11403-1 -2
  6.74 GPa
@Strain 0.360 %,
Temperature 40.0 °C		 978 ksi
@Strain 0.360 %,
Temperature 104 °F		 ISO 11403-1 -2
  6.8305 GPa
@Strain 1.41 %,
Temperature 23.0 °C		 990.70 ksi
@Strain 1.41 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  6.95 GPa
@Strain 2.08 %,
Temperature 0.000 °C		 1010 ksi
@Strain 2.08 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  7.00 GPa
@Strain 2.60 %,
Temperature -20.0 °C		 1020 ksi
@Strain 2.60 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  7.65 GPa
@Strain 2.85 %,
Temperature -40.0 °C		 1110 ksi
@Strain 2.85 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  7.74 GPa
@Strain 0.880 %,
Temperature 23.0 °C		 1120 ksi
@Strain 0.880 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  8.06 GPa
@Strain 1.46 %,
Temperature 0.000 °C		 1170 ksi
@Strain 1.46 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  8.0974 GPa
@Strain 1.92 %,
Temperature -20.0 °C		 1174.4 ksi
@Strain 1.92 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  8.12 GPa
@Strain 0.440 %,
Temperature 23.0 °C		 1180 ksi
@Strain 0.440 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  8.70 GPa
@Strain 2.07 %,
Temperature -40.0 °C		 1260 ksi
@Strain 2.07 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  8.7875 GPa
@Strain 0.960 %,
Temperature 0.000 °C		 1274.5 ksi
@Strain 0.960 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  9.08 GPa
@Strain 0.420 %,
Temperature 0.000 °C		 1320 ksi
@Strain 0.420 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  9.08 GPa
@Strain 1.23 %,
Temperature -20.0 °C		 1320 ksi
@Strain 1.23 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  9.44 GPa
@Strain 1.49 %,
Temperature -40.0 °C		 1370 ksi
@Strain 1.49 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  9.52 GPa
@Strain 0.660 %,
Temperature -20.0 °C		 1380 ksi
@Strain 0.660 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  9.81 GPa
@Strain 1.01 %,
Temperature -40.0 °C		 1420 ksi
@Strain 1.01 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  14.0 kJ/m² 6.66 ft-lb/in² ISO 180/1A
  11.0 kJ/m²
@Temperature -40.0 °C		 5.23 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  65.0 kJ/m² 30.9 ft-lb/in² ISO 180/1U
Charpy Impact Unnotched  7.00 J/cm² 33.3 ft-lb/in² ISO 179/1eU
Charpy Impact, Notched  1.30 J/cm² 6.19 ft-lb/in² ISO 179/1eA
  1.15 J/cm²
@Temperature -30.0 °C		 5.47 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  >= 1.00e+15 ohm >= 1.00e+15 ohm IEC 60093
Dielectric Constant  4.4
@Frequency 100 Hz		 4.4
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  31.0 kV/mm 787 kV/in IEC 60243-1
  31.0 kV/mm
@Thickness 1.00 mm		 787 kV/in
@Thickness 0.0394 in		 Short Time; IEC 60243-1
Dissipation Factor  0.0025
@Frequency 100 Hz		 0.0025
@Frequency 100 Hz		 IEC 60250
  0.0025
@Frequency 100 Hz		 0.0025
@Frequency 100 Hz		 ASTM D150
  0.0070
@Frequency 1000 Hz		 0.0070
@Frequency 1000 Hz		 ASTM D150
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 IEC 60250
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 ASTM D150
Comparative Tracking Index  375 V 375 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  30.0 µm/m-°C 16.7 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  85.0 µm/m-°C 47.2 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  1.73 J/g-°C 0.413 BTU/lb-°F  
Thermal Conductivity  0.280 W/m-K 1.94 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  221 °C 430 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  207 °C 405 °F ISO 75-1/-2
Vicat Softening Point  215 °C 419 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Flame Spread  30 mm/min
@Thickness 1.00 mm		 1.2 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
Oxygen Index  19 % 19 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT-IGF30< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT-IGF30  
UL recognition UL  

聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(TPA)或者对苯二甲酸酯(DMT)聚缩合而成，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。

⒈优良的机械性能，机械强度高，耐疲劳性和尺寸稳定好。蠕变也小，这些性能在高温条件下也极少有变化。

⒉生产PBT所消耗的能量是工程塑料中最低的的，这对于世界范围内能源紧缺的情况下，具有十分重要的意义。

⒊耐热老化性优异，增强后的UL温度指数达到120~140℃，此外，户外长期老化性也很好。

⒋耐溶剂好，无应力开裂。

⒌PBT易于阻燃，可达UL94V-0级，由于与阻燃剂亲和性能好，所以容易开发反应型或添加型的阻燃品级。阻燃产品在电子电器工业中获得广泛应用。

⒍PBT遇水易分解，在高温、高湿环境下使用需谨慎。

⒎优良的电气性能，体积电阻率及介电强度高，耐电弧性优良，吸湿性极小，在潮湿及高温环境下，也能保持电性能稳定，是制造电子、电器零件的理想材料。

⒏易成型加工和二次加工，易用普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程材料要求低，在加工薄壁制件时仅需几秒钟，对大部件也只需40-60s即可。

PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。

优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；

3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。

用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；

2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；

3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。

特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40422.html

免责声明: 本文 PBT/美国杜邦/HR5330HF NC010 耐磨 耐高温 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4