PBT/美国杜邦/SK612SF NC010增强级,高流动

PBT/美国杜邦/SK612SF NC010增强级,高流动
 参考图片：

颗粒图片：
10-03-30-95-421529.jpg.middle_副本

包装图片：

成品图片：
19-44-36-87-342874.jpg.middle

 

 

 

Physical Properties Metric English Comments
Density  1.22 g/cc 0.0441 lb/in³  
  1.42 g/cc 0.0513 lb/in³ ISO 1183
Water Absorption  0.40 %
@Thickness 2.00 mm		 0.40 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.150 %
@Thickness 2.00 mm		 0.150 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   54480 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 54480 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  65970 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 65970 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  81200 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 81200 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  152700 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 152700 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  187800 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 187800 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  234000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 234000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.0040 cm/cm 0.0040 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.011 cm/cm 0.011 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  110 MPa 16000 psi ISO 527-1/-2
Tensile Stress   9.443 MPa
@Strain 0.546765 %,
Temperature 160 °C		 1370 psi
@Strain 0.546765 %,
Temperature 320 °F		 ISO 11403-1 -2
  10.44 MPa
@Strain 0.543915 %,
Temperature 140 °C		 1514 psi
@Strain 0.543915 %,
Temperature 284 °F		 ISO 11403-1 -2
  13.88 MPa
@Strain 0.298656 %,
Temperature 40.0 °C		 2013 psi
@Strain 0.298656 %,
Temperature 104 °F		 ISO 11403-1 -2
  15.16 MPa
@Strain 0.239814 %,
Temperature -40.0 °C		 2198 psi
@Strain 0.239814 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  15.89 MPa
@Strain 0.268361 %,
Temperature 23.0 °C		 2304 psi
@Strain 0.268361 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  16.44 MPa
@Strain 0.263749 %,
Temperature -20.0 °C		 2384 psi
@Strain 0.263749 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  19.57 MPa
@Strain 1.3907 %,
Temperature 160 °C		 2839 psi
@Strain 1.3907 %,
Temperature 320 °F		 ISO 11403-1 -2
  20.30 MPa
@Strain 0.332444 %,
Temperature 0.000 °C		 2945 psi
@Strain 0.332444 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  20.39 MPa
@Strain 1.23103 %,
Temperature 140 °C		 2957 psi
@Strain 1.23103 %,
Temperature 284 °F		 ISO 11403-1 -2
  25.94 MPa
@Strain 2.21207 %,
Temperature 160 °C		 3762 psi
@Strain 2.21207 %,
Temperature 320 °F		 ISO 11403-1 -2
  28.35 MPa
@Strain 2.01089 %,
Temperature 140 °C		 4111 psi
@Strain 2.01089 %,
Temperature 284 °F		 ISO 11403-1 -2
  30.25 MPa
@Strain 0.682024 %,
Temperature 40.0 °C		 4387 psi
@Strain 0.682024 %,
Temperature 104 °F		 ISO 11403-1 -2
  30.59 MPa
@Strain 3.09033 %,
Temperature 160 °C		 4437 psi
@Strain 3.09033 %,
Temperature 320 °F		 ISO 11403-1 -2
  32.37 MPa
@Strain 0.525841 %,
Temperature -20.0 °C		 4695 psi
@Strain 0.525841 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  32.91 MPa
@Strain 0.527955 %,
Temperature -40.0 °C		 4774 psi
@Strain 0.527955 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  34.51 MPa
@Strain 2.90782 %,
Temperature 140 °C		 5006 psi
@Strain 2.90782 %,
Temperature 284 °F		 ISO 11403-1 -2
  34.73 MPa
@Strain 0.597341 %,
Temperature 23.0 °C		 5037 psi
@Strain 0.597341 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  35.17 MPa
@Strain 0.579891 %,
Temperature 0.000 °C		 5101 psi
@Strain 0.579891 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  46.94 MPa
@Strain 1.13289 %,
Temperature 40.0 °C		 6808 psi
@Strain 1.13289 %,
Temperature 104 °F		 ISO 11403-1 -2
  47.47 MPa
@Strain 0.779352 %,
Temperature -20.0 °C		 6886 psi
@Strain 0.779352 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  49.06 MPa
@Strain 0.795618 %,
Temperature -40.0 °C		 7116 psi
@Strain 0.795618 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  51.90 MPa
@Strain 0.872047 %,
Temperature 0.000 °C		 7527 psi
@Strain 0.872047 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  54.34 MPa
@Strain 0.971766 %,
Temperature 23.0 °C		 7881 psi
@Strain 0.971766 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  62.24 MPa
@Strain 1.66228 %,
Temperature 40.0 °C		 9027 psi
@Strain 1.66228 %,
Temperature 104 °F		 ISO 11403-1 -2
  63.03 MPa
@Strain 1.05428 %,
Temperature -20.0 °C		 9142 psi
@Strain 1.05428 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  64.96 MPa
@Strain 1.07013 %,
Temperature -40.0 °C		 9422 psi
@Strain 1.07013 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  69.141 MPa
@Strain 1.20176 %,
Temperature 0.000 °C		 10028 psi
@Strain 1.20176 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  73.73 MPa
@Strain 1.40132 %,
Temperature 23.0 °C		 10690 psi
@Strain 1.40132 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  107.5 MPa
@Strain 2.00763 %,
Temperature -20.0 °C		 15590 psi
@Strain 2.00763 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  110.99 MPa
@Strain 2.0059 %,
Temperature -40.0 °C		 16098 psi
@Strain 2.0059 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Elongation at Break  3.3 % 3.3 % ISO 527-1/-2
Tensile Modulus  6.00 GPa 870 ksi ISO 527-1/-2
Secant Modulus  1.23 GPa
@Strain 4.12508 %,
Temperature 100 °C		 179 ksi
@Strain 4.12508 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.2757 GPa
@Strain 4.5039 %,
Temperature 80.0 °C		 185.03 ksi
@Strain 4.5039 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.78 GPa
@Strain 2.20401 %,
Temperature 100 °C		 258 ksi
@Strain 2.20401 %,
Temperature 212 °F		 ISO 11403-1 -2
  2.06 GPa
@Strain 2.00926 %,
Temperature 80.0 °C		 298 ksi
@Strain 2.00926 %,
Temperature 176 °F		 ISO 11403-1 -2
  2.20 GPa
@Strain 1.02372 %,
Temperature 100 °C		 319 ksi
@Strain 1.02372 %,
Temperature 212 °F		 ISO 11403-1 -2
  2.3886 GPa
@Strain 1.11375 %,
Temperature 80.0 °C		 346.44 ksi
@Strain 1.11375 %,
Temperature 176 °F		 ISO 11403-1 -2
  2.45 GPa
@Strain 0.411103 %,
Temperature 100 °C		 355 ksi
@Strain 0.411103 %,
Temperature 212 °F		 ISO 11403-1 -2
  2.68 GPa
@Strain 0.437002 %,
Temperature 80.0 °C		 388 ksi
@Strain 0.437002 %,
Temperature 176 °F		 ISO 11403-1 -2
  2.7596 GPa
@Strain 3.00056 %,
Temperature 40.0 °C		 400.25 ksi
@Strain 3.00056 %,
Temperature 104 °F		 ISO 11403-1 -2
  3.43 GPa
@Strain 2.06534 %,
Temperature 40.0 °C		 497 ksi
@Strain 2.06534 %,
Temperature 104 °F		 ISO 11403-1 -2
  4.0227 GPa
@Strain 1.30015 %,
Temperature 40.0 °C		 583.45 ksi
@Strain 1.30015 %,
Temperature 104 °F		 ISO 11403-1 -2
  4.10 GPa
@Strain 2.5045 %,
Temperature 23.0 °C		 595 ksi
@Strain 2.5045 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  4.44 GPa
@Strain 0.682024 %,
Temperature 40.0 °C		 643 ksi
@Strain 0.682024 %,
Temperature 104 °F		 ISO 11403-1 -2
  4.65 GPa
@Strain 0.298656 %,
Temperature 40.0 °C		 674 ksi
@Strain 0.298656 %,
Temperature 104 °F		 ISO 11403-1 -2
  4.97 GPa
@Strain 1.72197 %,
Temperature 23.0 °C		 721 ksi
@Strain 1.72197 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  5.14 GPa
@Strain 1.96921 %,
Temperature 0.000 °C		 745 ksi
@Strain 1.96921 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  5.49 GPa
@Strain 1.11022 %,
Temperature 23.0 °C		 796 ksi
@Strain 1.11022 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  5.59 GPa
@Strain 1.44095 %,
Temperature 0.000 °C		 810 ksi
@Strain 1.44095 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  5.61 GPa
@Strain 1.66598 %,
Temperature -20.0 °C		 814 ksi
@Strain 1.66598 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  5.75 GPa
@Strain 1.67592 %,
Temperature -40.0 °C		 833 ksi
@Strain 1.67592 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  5.81 GPa
@Strain 0.597341 %,
Temperature 23.0 °C		 843 ksi
@Strain 0.597341 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  5.88 GPa
@Strain 1.24902 %,
Temperature -20.0 °C		 852 ksi
@Strain 1.24902 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  5.89 GPa
@Strain 0.97819 %,
Temperature 0.000 °C		 855 ksi
@Strain 0.97819 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  5.92 GPa
@Strain 0.268361 %,
Temperature 23.0 °C		 859 ksi
@Strain 0.268361 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  5.98 GPa
@Strain 1.26366 %,
Temperature -40.0 °C		 867 ksi
@Strain 1.26366 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  6.06 GPa
@Strain 0.869061 %,
Temperature -20.0 °C		 879 ksi
@Strain 0.869061 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  6.07 GPa
@Strain 0.579891 %,
Temperature 0.000 °C		 880 ksi
@Strain 0.579891 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  6.11 GPa
@Strain 0.332444 %,
Temperature 0.000 °C		 886 ksi
@Strain 0.332444 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  6.14 GPa
@Strain 0.884826 %,
Temperature -40.0 °C		 891 ksi
@Strain 0.884826 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  6.16 GPa
@Strain 0.525841 %,
Temperature -20.0 °C		 893 ksi
@Strain 0.525841 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  6.23 GPa
@Strain 0.263749 %,
Temperature -20.0 °C		 904 ksi
@Strain 0.263749 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  6.23 GPa
@Strain 0.527955 %,
Temperature -40.0 °C		 904 ksi
@Strain 0.527955 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  6.32 GPa
@Strain 0.239814 %,
Temperature -40.0 °C		 917 ksi
@Strain 0.239814 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Charpy Impact Unnotched  3.00 J/cm² 14.3 ft-lb/in² ISO 179/1eU
  3.00 J/cm²
@Temperature -30.0 °C		 14.3 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.550 J/cm² 2.62 ft-lb/in² ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+15 ohm 1.00e+15 ohm IEC 60093
Dielectric Constant   3.5
@Frequency 1.00e+6 Hz		 3.5
@Frequency 1.00e+6 Hz		 IEC 60250
  4.1
@Frequency 100 Hz		 4.1
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  27.0 kV/mm 686 kV/in IEC 60243-1
Dissipation Factor   0.0020
@Frequency 100 Hz		 0.0020
@Frequency 100 Hz		 IEC 60250
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  350 V 350 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  50.0 µm/m-°C 27.8 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  95.0 µm/m-°C 52.8 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  1.90 J/g-°C 0.454 BTU/lb-°F  
Thermal Conductivity  0.240 W/m-K 1.67 BTU-in/hr-ft²-°F of melt
Melting Point  224 °C 435 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)  200 °C 392 °F ISO 75-1/-2
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 3.00 mm		 HB
@Thickness 0.118 in		 IEC 60695-11-10
Oxygen Index  19 % 19 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT-GF15< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT-GF15  
UL recognition UL  

聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(TPA)或者对苯二甲酸酯(DMT)聚缩合而成，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。

⒈优良的机械性能，机械强度高，耐疲劳性和尺寸稳定好。蠕变也小，这些性能在高温条件下也极少有变化。

⒉生产PBT所消耗的能量是工程塑料中最低的的，这对于世界范围内能源紧缺的情况下，具有十分重要的意义。

⒊耐热老化性优异，增强后的UL温度指数达到120~140℃，此外，户外长期老化性也很好。

⒋耐溶剂好，无应力开裂。

⒌PBT易于阻燃，可达UL94V-0级，由于与阻燃剂亲和性能好，所以容易开发反应型或添加型的阻燃品级。阻燃产品在电子电器工业中获得广泛应用。

⒍PBT遇水易分解，在高温、高湿环境下使用需谨慎。

⒎优良的电气性能，体积电阻率及介电强度高，耐电弧性优良，吸湿性极小，在潮湿及高温环境下，也能保持电性能稳定，是制造电子、电器零件的理想材料。

⒏易成型加工和二次加工，易用普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程材料要求低，在加工薄壁制件时仅需几秒钟，对大部件也只需40-60s即可。

PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。

优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；

3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。

用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；

2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；

3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。

特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40456.html

免责声明: 本文 PBT/美国杜邦/SK612SF NC010增强级,高流动 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4