  4. PBT 美国杜邦 SK615SF NC010 低粘度 高流动

PBT 美国杜邦 SK615SF NC010 低粘度 高流动

PBT美国杜邦 SK615SF NC010 低粘度 高流动
 参考图片：

颗粒图片：

100013567048_14032739394852

包装图片：

成品图片：

 

 

 
Physical Properties Metric English Comments
Density  1.36 g/cc 0.0491 lb/in³  
  1.54 g/cc 0.0556 lb/in³ ISO 1183
Water Absorption  0.35 %
@Thickness 2.00 mm		 0.35 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.150 %
@Thickness 2.00 mm		 0.150 %
@Thickness 0.0787 in		 Sim. to ISO 62
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.011 cm/cm 0.011 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  150 MPa 21800 psi ISO 527-1/-2
Tensile Stress   6.288 MPa
@Strain 0.152378 %,
Temperature 140 °C		 911.9 psi
@Strain 0.152378 %,
Temperature 284 °F		 ISO 11403-1 -2
  8.422 MPa
@Strain 0.240189 %,
Temperature 160 °C		 1222 psi
@Strain 0.240189 %,
Temperature 320 °F		 ISO 11403-1 -2
  15.15 MPa
@Strain 0.386488 %,
Temperature 140 °C		 2197 psi
@Strain 0.386488 %,
Temperature 284 °F		 ISO 11403-1 -2
  15.45 MPa
@Strain 0.143435 %,
Temperature -20.0 °C		 2240 psi
@Strain 0.143435 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  15.51 MPa
@Strain 0.141174 %,
Temperature -40.0 °C		 2249 psi
@Strain 0.141174 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  16.86 MPa
@Strain 0.210062 %,
Temperature 40.0 °C		 2445 psi
@Strain 0.210062 %,
Temperature 104 °F		 ISO 11403-1 -2
  22.62 MPa
@Strain 0.215233 %,
Temperature 23.0 °C		 3281 psi
@Strain 0.215233 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  23.28 MPa
@Strain 0.231655 %,
Temperature 0.000 °C		 3377 psi
@Strain 0.231655 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  24.29 MPa
@Strain 0.690557 %,
Temperature 140 °C		 3522 psi
@Strain 0.690557 %,
Temperature 284 °F		 ISO 11403-1 -2
  30.06 MPa
@Strain 1.37862 %,
Temperature 160 °C		 4360 psi
@Strain 1.37862 %,
Temperature 320 °F		 ISO 11403-1 -2
  32.585 MPa
@Strain 1.0723 %,
Temperature 140 °C		 4726.1 psi
@Strain 1.0723 %,
Temperature 284 °F		 ISO 11403-1 -2
  34.518 MPa
@Strain 0.453157 %,
Temperature 40.0 °C		 5006.4 psi
@Strain 0.453157 %,
Temperature 104 °F		 ISO 11403-1 -2
  36.42 MPa
@Strain 2.02599 %,
Temperature 160 °C		 5282 psi
@Strain 2.02599 %,
Temperature 320 °F		 ISO 11403-1 -2
  39.23 MPa
@Strain 2.53541 %,
Temperature 160 °C		 5690 psi
@Strain 2.53541 %,
Temperature 320 °F		 ISO 11403-1 -2
  41.66 MPa
@Strain 0.412778 %,
Temperature 23.0 °C		 6043 psi
@Strain 0.412778 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  43.48 MPa
@Strain 0.410528 %,
Temperature -20.0 °C		 6307 psi
@Strain 0.410528 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  45.36 MPa
@Strain 0.453926 %,
Temperature 0.000 °C		 6579 psi
@Strain 0.453926 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  48.77 MPa
@Strain 2.68009 %,
Temperature 140 °C		 7073 psi
@Strain 2.68009 %,
Temperature 284 °F		 ISO 11403-1 -2
  52.96 MPa
@Strain 0.746328 %,
Temperature 40.0 °C		 7681 psi
@Strain 0.746328 %,
Temperature 104 °F		 ISO 11403-1 -2
  62.36 MPa
@Strain 0.591272 %,
Temperature -40.0 °C		 9045 psi
@Strain 0.591272 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  64.57 MPa
@Strain 0.683319 %,
Temperature 23.0 °C		 9365 psi
@Strain 0.683319 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  69.31 MPa
@Strain 0.710966 %,
Temperature 0.000 °C		 10050 psi
@Strain 0.710966 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  71.131 MPa
@Strain 1.0997 %,
Temperature 40.0 °C		 10317 psi
@Strain 1.0997 %,
Temperature 104 °F		 ISO 11403-1 -2
  72.09 MPa
@Strain 0.700638 %,
Temperature -20.0 °C		 10460 psi
@Strain 0.700638 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  87.83 MPa
@Strain 1.00996 %,
Temperature 23.0 °C		 12740 psi
@Strain 1.00996 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  91.14 MPa
@Strain 0.87993 %,
Temperature -40.0 °C		 13220 psi
@Strain 0.87993 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  93.89 MPa
@Strain 1.01022 %,
Temperature 0.000 °C		 13620 psi
@Strain 1.01022 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  100.4 MPa
@Strain 1.02518 %,
Temperature -20.0 °C		 14560 psi
@Strain 1.02518 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  108.7 MPa
@Strain 2.58789 %,
Temperature 40.0 °C		 15770 psi
@Strain 2.58789 %,
Temperature 104 °F		 ISO 11403-1 -2
  121.5 MPa
@Strain 1.21618 %,
Temperature -40.0 °C		 17620 psi
@Strain 1.21618 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  174.0 MPa
@Strain 2.41732 %,
Temperature -20.0 °C		 25240 psi
@Strain 2.41732 %,
Temperature -4.00 °F		 ISO 11403-1 -2
Elongation at Break  2.5 % 2.5 % ISO 527-1/-2
Tensile Modulus  10.0 GPa 1450 ksi ISO 527-1/-2
Secant Modulus   2.71 GPa
@Strain 2.64148 %,
Temperature 80.0 °C		 393 ksi
@Strain 2.64148 %,
Temperature 176 °F		 ISO 11403-1 -2
  2.79 GPa
@Strain 2.08034 %,
Temperature 100 °C		 405 ksi
@Strain 2.08034 %,
Temperature 212 °F		 ISO 11403-1 -2
  4.06 GPa
@Strain 1.2473 %,
Temperature 80.0 °C		 589 ksi
@Strain 1.2473 %,
Temperature 176 °F		 ISO 11403-1 -2
  4.46 GPa
@Strain 0.591579 %,
Temperature 100 °C		 647 ksi
@Strain 0.591579 %,
Temperature 212 °F		 ISO 11403-1 -2
  4.93 GPa
@Strain 0.600598 %,
Temperature 80.0 °C		 715 ksi
@Strain 0.600598 %,
Temperature 176 °F		 ISO 11403-1 -2
  5.02 GPa
@Strain 0.229987 %,
Temperature 100 °C		 728 ksi
@Strain 0.229987 %,
Temperature 212 °F		 ISO 11403-1 -2
  5.04 GPa
@Strain 1.99815 %,
Temperature 40.0 °C		 731 ksi
@Strain 1.99815 %,
Temperature 104 °F		 ISO 11403-1 -2
  5.46 GPa
@Strain 0.294996 %,
Temperature 80.0 °C		 793 ksi
@Strain 0.294996 %,
Temperature 176 °F		 ISO 11403-1 -2
  6.01 GPa
@Strain 1.36981 %,
Temperature 40.0 °C		 872 ksi
@Strain 1.36981 %,
Temperature 104 °F		 ISO 11403-1 -2
  6.72 GPa
@Strain 1.87532 %,
Temperature 23.0 °C		 974 ksi
@Strain 1.87532 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  6.8964 GPa
@Strain 0.857481 %,
Temperature 40.0 °C		 1000.3 ksi
@Strain 0.857481 %,
Temperature 104 °F		 ISO 11403-1 -2
  7.62 GPa
@Strain 0.453157 %,
Temperature 40.0 °C		 1100 ksi
@Strain 0.453157 %,
Temperature 104 °F		 ISO 11403-1 -2
  7.88 GPa
@Strain 1.75077 %,
Temperature 0.000 °C		 1140 ksi
@Strain 1.75077 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  8.02 GPa
@Strain 0.210062 %,
Temperature 40.0 °C		 1160 ksi
@Strain 0.210062 %,
Temperature 104 °F		 ISO 11403-1 -2
  8.11 GPa
@Strain 1.26111 %,
Temperature 23.0 °C		 1180 ksi
@Strain 1.26111 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  8.32 GPa
@Strain 1.822 %,
Temperature -20.0 °C		 1210 ksi
@Strain 1.822 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  8.55 GPa
@Strain 2.01539 %,
Temperature -40.0 °C		 1240 ksi
@Strain 2.01539 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  8.90 GPa
@Strain 1.23431 %,
Temperature 0.000 °C		 1290 ksi
@Strain 1.23431 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  9.21 GPa
@Strain 0.786074 %,
Temperature 23.0 °C		 1340 ksi
@Strain 0.786074 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  9.36 GPa
@Strain 1.26922 %,
Temperature -20.0 °C		 1360 ksi
@Strain 1.26922 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  9.54 GPa
@Strain 1.4648 %,
Temperature -40.0 °C		 1380 ksi
@Strain 1.4648 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  9.62 GPa
@Strain 0.806055 %,
Temperature 0.000 °C		 1400 ksi
@Strain 0.806055 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  9.99 GPa
@Strain 0.453926 %,
Temperature 0.000 °C		 1450 ksi
@Strain 0.453926 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  10.1 GPa
@Strain 0.231655 %,
Temperature 0.000 °C		 1460 ksi
@Strain 0.231655 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  10.1 GPa
@Strain 0.412778 %,
Temperature 23.0 °C		 1460 ksi
@Strain 0.412778 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  10.1 GPa
@Strain 0.803431 %,
Temperature -20.0 °C		 1470 ksi
@Strain 0.803431 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  10.3 GPa
@Strain 0.986916 %,
Temperature -40.0 °C		 1490 ksi
@Strain 0.986916 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  10.511 GPa
@Strain 0.215233 %,
Temperature 23.0 °C		 1524.5 ksi
@Strain 0.215233 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  10.5 GPa
@Strain 0.591272 %,
Temperature -40.0 °C		 1530 ksi
@Strain 0.591272 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  10.6 GPa
@Strain 0.410528 %,
Temperature -20.0 °C		 1540 ksi
@Strain 0.410528 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  10.8 GPa
@Strain 0.143435 %,
Temperature -20.0 °C		 1560 ksi
@Strain 0.143435 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  11.0 GPa
@Strain 0.141174 %,
Temperature -40.0 °C		 1590 ksi
@Strain 0.141174 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Charpy Impact Unnotched  6.00 J/cm² 28.6 ft-lb/in² ISO 179/1eU
  3.00 J/cm²
@Temperature -30.0 °C		 14.3 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.900 J/cm² 4.28 ft-lb/in² ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  >= 1.00e+15 ohm >= 1.00e+15 ohm IEC 60093
Dielectric Constant   3.8
@Frequency 1.00e+6 Hz		 3.8
@Frequency 1.00e+6 Hz		 IEC 60250
  4.4
@Frequency 100 Hz		 4.4
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  31.0 kV/mm 787 kV/in IEC 60243-1
Dissipation Factor   0.0025
@Frequency 100 Hz		 0.0025
@Frequency 100 Hz		 IEC 60250
  0.018
@Frequency 1.00e+6 Hz		 0.018
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  370 V 370 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  30.0 µm/m-°C 16.7 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  80.0 µm/m-°C 44.4 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  1.73 J/g-°C 0.413 BTU/lb-°F  
Thermal Conductivity  0.280 W/m-K 1.94 BTU-in/hr-ft²-°F of melt
Melting Point  223 °C 433 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)  210 °C 410 °F ISO 75-1/-2
Flammability, UL94  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 3.00 mm		 HB
@Thickness 0.118 in		 IEC 60695-11-10
Oxygen Index  19 % 19 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT-GF30< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT-GF30  

聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(TPA)或者对苯二甲酸酯(DMT)聚缩合而成，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。

⒈优良的机械性能，机械强度高，耐疲劳性和尺寸稳定好。蠕变也小，这些性能在高温条件下也极少有变化。

⒉生产PBT所消耗的能量是工程塑料中最低的的，这对于世界范围内能源紧缺的情况下，具有十分重要的意义。

⒊耐热老化性优异，增强后的UL温度指数达到120~140℃，此外，户外长期老化性也很好。

⒋耐溶剂好，无应力开裂。

⒌PBT易于阻燃，可达UL94V-0级，由于与阻燃剂亲和性能好，所以容易开发反应型或添加型的阻燃品级。阻燃产品在电子电器工业中获得广泛应用。

⒍PBT遇水易分解，在高温、高湿环境下使用需谨慎。

⒎优良的电气性能，体积电阻率及介电强度高，耐电弧性优良，吸湿性极小，在潮湿及高温环境下，也能保持电性能稳定，是制造电子、电器零件的理想材料。

⒏易成型加工和二次加工，易用普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程材料要求低，在加工薄壁制件时仅需几秒钟，对大部件也只需40-60s即可。

PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。

优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；

3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。

用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；

2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；

3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。

特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40458.html

免责声明: 本文 PBT 美国杜邦 SK615SF NC010 低粘度 高流动 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4