| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.50 % | 0.50 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 107 cm³/g | 107 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | |||
| 0.016 cm/cm | 0.016 in/in | 60x60x2mm; ISO 294 | |||
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | |||
| 0.019 cm/cm | 0.019 in/in | 60x60x2mm; ISO 294 | |||
| Melt Flow | 52 g/10 min @Load 2.16 kg, Temperature 250 °C |
52 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 130 MPa | 18900 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 57.0 MPa | 8270 psi | 5mm/min; ISO 527-2 | ||
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 35 % | 35 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 3.7 % | 3.7 % | 50mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 2.50 GPa | 363 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 25.0 J/cm² | 119 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA | ||
| Dart Drop, Total Energy | 100 J | 73.8 ft-lb | ISO 6603-1 | ||
| Tensile Creep Modulus, 1000 hours | 1100 MPa | 160000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 93 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 93 | ||
| Dielectric Constant | 3.3 @Frequency 100 Hz |
3.3 @Frequency 100 Hz |
IEC 250 | ||
| 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 250 | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.0013 @Frequency 100 Hz |
0.0013 @Frequency 100 Hz |
IEC 250 | ||
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 250 | |||
| Comparative Tracking Index | 450 V | 450 V | Test Liquid B; IEC 112 | ||
| 500 V | 500 V | Test liquid A; IEC 112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 13.0 - 16.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
7.22 - 8.89 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | Melt; IEC 1006 | ||
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | Melt; DIN 52612 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | ISO 11357-3 | ||
| Maximum Service Temperature, Air | 120 °C | 248 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 140 °C | 284 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |||
| 200 °C | 392 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 245 - 270 °C | 473 - 518 °F | Injection molding | ||
| 230 - 290 °C | 446 - 554 °F | Coating | |||
| 260 °C | 500 °F | for shrinkage test | |||
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Ejection temperature | ||
| 60.0 °C | 140 °F | for shrinkage test | |||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| FDA | 21 CFR 177.1660 | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding and Coating | ||||
| Processing | Coating | ||||
| Film Extrusion | |||||
| Injection Molding | |||||
| Other Extrusion | |||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| U.V. stabilized or stable to weather | |||||
| UL.UL-C | Yes | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com