LCP E820iPd 材料说明：e820i催化改性
LCP E820iPd 填料/增强材料：矿物填料, 40% 填料按重量
LCP E820iPd 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.79 g/cc | 0.0647 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00400 cm/cm | 0.00400 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0120 cm/cm | 0.0120 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 89.0 MPa | 12900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.20 % | 3.20 % | flexural; ISO 178 |
| 3.60 % | 3.60 % | 5mm/min; ISO 527-2/1A | |
| Tensile Modulus | 8.00 GPa | 1160 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Flexural Modulus | 8.80 GPa | 1280 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 180/1A |
| 28.0 kJ/m² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dissipation Factor | 0.0163 @Frequency 1.00e+6 Hz |
0.0163 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C | 12.8 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 49.0 µm/m-°C | 27.2 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 119 °C | 246 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 | V-0 | |