LCP J540 说明：40%的矿物填充料、高耐热性。
LCP J540 加工方法：注塑成型
LCP J540 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.000700 cm/cm | 0.000700 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00370 cm/cm | 0.00370 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 105 MPa | 15200 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.30 % | 3.30 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 9.00 GPa | 1310 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 350 °C | 662 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1, -2 |