| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH | ||
| Viscosity Measurement | 115 | 115 | [ml/g]; Viscosity number; ISO 1628 | ||
| 70 @Temperature 290 °C |
70 @Temperature 554 °F |
20 mins plasticating | |||
| 75 @Temperature 300 °C |
75 @Temperature 572 °F |
10 mins plasticating | |||
| 75 @Temperature 280 °C |
75 @Temperature 536 °F |
30 mins plasticating | |||
| 90 @Temperature 270 °C |
90 @Temperature 518 °F |
30 mins plasticating | |||
| 95 @Temperature 290 °C |
95 @Temperature 554 °F |
10 mins plasticating | |||
| 100 @Temperature 260 °C |
100 @Temperature 500 °F |
30 mins plasticating | |||
| 100 @Temperature 300 °C |
100 @Temperature 572 °F |
5 mins plasticating | |||
| 105 @Temperature 280 °C |
105 @Temperature 536 °F |
10 mins plasticating | |||
| 106 @Temperature 250 °C |
106 @Temperature 482 °F |
30 mins plasticating | |||
| 110 @Temperature 270 °C |
110 @Temperature 518 °F |
10 mins plasticating | |||
| 115 @Temperature 260 °C |
115 @Temperature 500 °F |
10 mins plasticating | |||
| 115 @Temperature 240 °C |
115 @Temperature 464 °F |
30 mins plasticating | |||
| 117 @Temperature 250 °C |
117 @Temperature 482 °F |
10 mins plasticating | |||
| 120 @Temperature 240 °C |
120 @Temperature 464 °F |
10 mins plasticating | |||
| Linear Mold Shrinkage, Flow | 0.017 cm/cm | 0.017 in/in | Sheet | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | Sheet | ||
| Melt Flow | 24.65 g/10 min @Load 2.16 kg, Temperature 250 °C |
24.65 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 150 MPa | 21800 psi | ISO 2039-1 | ||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Break | 5.0 % | 5.0 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 2.8 % | 2.8 % | 50 mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 3.50 GPa | 508 ksi | ISO 527-2 | ||
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 | ||
| Charpy Impact Unnotched | 2.60 J/cm² @Temperature -30.0 °C |
12.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | ||
| Dart Drop, Total Energy | <= 5.00 J | <= 3.69 ft-lb | W501 housing; ISO 6603-1 | ||
| Tensile Creep Modulus, 1000 hours | 1300 MPa @Strain <=0.500 % |
189000 psi @Strain <=0.500 % |
ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 93 | ||
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 93 | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 250 | ||
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 250 | |||
| Dielectric Strength | 100 kV/mm | 2540 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.012 @Frequency 100 Hz |
0.012 @Frequency 100 Hz |
IEC 250 | ||
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
IEC 250 | |||
| Comparative Tracking Index | 125 V | 125 V | Test solution B; IEC 112 | ||
| 250 V | 250 V | Test solution A; IEC 112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 80.0 - 90.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
44.4 - 50.0 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.60 J/g-°C | 0.382 BTU/lb-°F | IEC 1006 | ||
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | DSC; ISO 11357-3 | ||
| Maximum Service Temperature, Air | 120 °C | 248 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 130 °C | 266 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |||
| 200 °C | 392 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-2 | ||
| Decomposition Temperature | >= 290 °C | >= 554 °F | |||
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
|||
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
||||
| Flame Spread | <= 100 mm/min | <= 3.94 in/min | DIN 75200 | ||
| Glow Wire Test | <= 750 °C @Thickness 3.00 mm |
<= 1380 °F @Thickness 0.118 in |
IEC 695 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 240 °C | 464 °F | Feeding zone | ||
| Zone 2 | 245 °C | 473 °F | Compression | ||
| Zone 3 | 250 °C | 482 °F | Metering-zone | ||
| Zone 4 | 250 °C | 482 °F | Nozzle | ||
| Melt Temperature | 250 °C | 482 °F | Optimal | ||
| 260 °C | 500 °F | for shrinkage test | |||
| 250 - 275 °C | 482 - 527 °F | Injection-molding | |||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| 60.0 °C | 140 °F | for shrinkage test, Optimal | |||
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| De |
|||||
| Color | Natural, Colored, Black and Special Colors | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 350°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.25 m/s | ||||
| Primary Processing Technique | Injection Molding | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com