LCP MT4310 材质说明：最高的温度能力，最易流动。适用于非常薄的墙壁是必需的。用于SMT应用范围广泛，以最小的尺寸变化。30%玻璃填充。
LCP MT4310 形式：粒子
LCP MT4310 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 71.0 | 71.0 | ISO 2039-2 |
| Tensile Strength at Break | 150 MPa | 21800 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.60 % | 1.60 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 225 MPa | 32600 psi | ISO 178 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 |
| Compressive Strength | 93.0 MPa @Strain 1.00 % |
13500 psi @Strain 1.00 % |
ISO 604 |
| Compressive Modulus | 14.0 GPa | 2030 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180/1A |
| 31.0 kJ/m² @Temperature 23.0 °C |
14.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 4.30 J/cm² | 20.5 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.30 @Frequency 1.00e+6 Hz |
3.30 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.00 @Frequency 100 Hz |
4.00 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0100 @Frequency 100 Hz |
0.0100 @Frequency 100 Hz |
IEC 60250 |
| 0.0250 @Frequency 1.00e+6 Hz |
0.0250 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Arc Resistance | 140 sec | 140 sec | Internal |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 7.00 µm/m-°C | 3.89 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-2 |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 276 °C | 529 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 216 °C | 421 °F | ISO 75-1, -2 |
| Vicat Softening Point | 195 °C | 383 °F | ISO 306 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 45.0 % | 45.0 % | ISO 4589 |