| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH | ||
| Viscosity Measurement | 139 | 139 | [ml/g]; Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | Sheet | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | Sheet | ||
| Melt Flow | 14.19 g/10 min @Load 2.16 kg, Temperature 275 °C |
14.19 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Break | 3.8 % | 3.8 % | 50mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 4.00 GPa | 580 ksi | ISO 527-2 | ||
| Flexural Strength | 104 MPa | 15100 psi | ISO 178 | ||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | DSC; ISO 11357-3 | ||
| Maximum Service Temperature, Air | 170 °C | 338 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection-molding | ||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | Europe | ||||
| Primary Processing Technique | Injection Molding | ||||
图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com