  4. 杜邦高性能聚合物6129 NC010/用于挤出和注塑成型

杜邦高性能聚合物6129 NC010/用于挤出和注塑成型

杜邦高性能聚合物Crastin®6129 NC010聚对苯二甲酸丁二醇酯（PBT） 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT） 材料说明：无筋高粘度聚对苯二甲酸乙二醇酯用于挤出和注塑成型
 物性表：

 
Physical Properties Metric English Comments
Density  1.12 g/cc 0.0405 lb/in³  
  1.32 g/cc 0.0477 lb/in³ ISO 1183
Water Absorption  0.40 %
@Thickness 2.00 mm		 0.40 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.200 %
@Thickness 2.00 mm		 0.200 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   123300 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 123300 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  142200 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 142200 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  165000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 165000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  396400 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 396400 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  505900 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 505900 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  626100 cP
@Shear Rate 10.0 1/s,
Temperature 260 °C		 626100 cP
@Shear Rate 10.0 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  641900 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 641900 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  918900 cP
@Shear Rate 10.0 1/s,
Temperature 250 °C		 918900 cP
@Shear Rate 10.0 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  1.3929e+6 cP
@Shear Rate 10.0 1/s,
Temperature 240 °C		 1.3929e+6 cP
@Shear Rate 10.0 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Viscosity Test  150 cm³/g 150 cm³/g ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.017 cm/cm 0.017 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.015 cm/cm 0.015 in/in ISO 294-4 2577
Melt Flow  10 g/10 min
@Load 2.16 kg,
Temperature 250 °C		 10 g/10 min
@Load 4.76 lb,
Temperature 482 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Stress   0.410 MPa
@Strain 0.170 %,
Temperature 150 °C		 59.5 psi
@Strain 0.170 %,
Temperature 302 °F		 ISO 11403-1 -2
  0.680 MPa
@Strain 0.170 %,
Temperature 90.0 °C		 98.6 psi
@Strain 0.170 %,
Temperature 194 °F		 ISO 11403-1 -2
  4.10 MPa
@Strain 2.28 %,
Temperature 150 °C		 595 psi
@Strain 2.28 %,
Temperature 302 °F		 ISO 11403-1 -2
  6.67 MPa
@Strain 4.80 %,
Temperature 150 °C		 967 psi
@Strain 4.80 %,
Temperature 302 °F		 ISO 11403-1 -2
  7.25 MPa
@Strain 2.25 %,
Temperature 90.0 °C		 1050 psi
@Strain 2.25 %,
Temperature 194 °F		 ISO 11403-1 -2
  8.25 MPa
@Strain 7.41 %,
Temperature 150 °C		 1200 psi
@Strain 7.41 %,
Temperature 302 °F		 ISO 11403-1 -2
  12.07 MPa
@Strain 4.64 %,
Temperature 90.0 °C		 1751 psi
@Strain 4.64 %,
Temperature 194 °F		 ISO 11403-1 -2
  13.63 MPa
@Strain 0.430 %,
Temperature -40.0 °C		 1977 psi
@Strain 0.430 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  14.34 MPa
@Strain 1.27 %,
Temperature 40.0 °C		 2080 psi
@Strain 1.27 %,
Temperature 104 °F		 ISO 11403-1 -2
  15.07 MPa
@Strain 7.13 %,
Temperature 90.0 °C		 2186 psi
@Strain 7.13 %,
Temperature 194 °F		 ISO 11403-1 -2
  16.61 MPa
@Strain 0.700 %,
Temperature 23.0 °C		 2409 psi
@Strain 0.700 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  22.95 MPa
@Strain 0.820 %,
Temperature -20.0 °C		 3329 psi
@Strain 0.820 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  24.96 MPa
@Strain 3.64 %,
Temperature 40.0 °C		 3620 psi
@Strain 3.64 %,
Temperature 104 °F		 ISO 11403-1 -2
  27.2 MPa
@Strain 1.04 %,
Temperature 0.000 °C		 3950 psi
@Strain 1.04 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  29.39 MPa
@Strain 6.18 %,
Temperature 40.0 °C		 4263 psi
@Strain 6.18 %,
Temperature 104 °F		 ISO 11403-1 -2
  32.22 MPa
@Strain 8.75 %,
Temperature 40.0 °C		 4673 psi
@Strain 8.75 %,
Temperature 104 °F		 ISO 11403-1 -2
  45.2 MPa
@Strain 2.17 %,
Temperature 23.0 °C		 6560 psi
@Strain 2.17 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  48.4 MPa
@Strain 1.69 %,
Temperature -40.0 °C		 7020 psi
@Strain 1.69 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  51.39 MPa
@Strain 2.00 %,
Temperature -20.0 °C		 7454 psi
@Strain 2.00 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  54.78 MPa
@Strain 2.40 %,
Temperature 0.000 °C		 7945 psi
@Strain 2.40 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  65.05 MPa
@Strain 4.22 %,
Temperature 0.000 °C		 9435 psi
@Strain 4.22 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  70.55 MPa
@Strain 3.31 %,
Temperature -20.0 °C		 10230 psi
@Strain 3.31 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  71.25 MPa
@Strain 2.81 %,
Temperature -40.0 °C		 10330 psi
@Strain 2.81 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  77.04 MPa
@Strain 5.18 %,
Temperature -20.0 °C		 11170 psi
@Strain 5.18 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  87.67 MPa
@Strain 4.16 %,
Temperature -40.0 °C		 12720 psi
@Strain 4.16 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  95.86 MPa
@Strain 5.77 %,
Temperature -40.0 °C		 13900 psi
@Strain 5.77 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  58.0 MPa 8410 psi ISO 527-1/-2
Elongation at Break  >= 50 % >= 50 % Nominal; ISO 527-1/-2
Elongation at Yield  5.0 % 5.0 % ISO 527-1/-2
Tensile Modulus  2.60 GPa 377 ksi ISO 527-1/-2
  0.251 GPa
@Temperature 120 °C		 36.4 ksi
@Temperature 248 °F		 ISO 11403-1 -2
  1.162 GPa
@Temperature 40.0 °C		 168.5 ksi
@Temperature 104 °F		 ISO 11403-1 -2
  3.024 GPa
@Temperature -40.0 °C		 438.6 ksi
@Temperature -40.0 °F		 ISO 11403-1 -2
Flexural Modulus  2.40 GPa 348 ksi ISO 178
Shear Strength   0.006261 MPa
@Shear Rate 10.0 1/s,
Temperature 260 °C		 0.9081 psi
@Shear Rate 10.0 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  0.009189 MPa
@Shear Rate 10.0 1/s,
Temperature 250 °C		 1.333 psi
@Shear Rate 10.0 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  0.013929 MPa
@Shear Rate 10.0 1/s,
Temperature 240 °C		 2.0202 psi
@Shear Rate 10.0 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  0.1982 MPa
@Shear Rate 500 1/s,
Temperature 260 °C		 28.74 psi
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  0.2530 MPa
@Shear Rate 500 1/s,
Temperature 250 °C		 36.69 psi
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  0.3209 MPa
@Shear Rate 500 1/s,
Temperature 240 °C		 46.55 psi
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  0.6165 MPa
@Shear Rate 5000 1/s,
Temperature 260 °C		 89.42 psi
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  0.7110 MPa
@Shear Rate 5000 1/s,
Temperature 250 °C		 103.1 psi
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  0.8248 MPa
@Shear Rate 5000 1/s,
Temperature 240 °C		 119.6 psi
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Secant Modulus   0.43495 GPa
@Strain 7.01 %,
Temperature 40.0 °C		 63.085 ksi
@Strain 7.01 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.686 GPa
@Strain 3.64 %,
Temperature 40.0 °C		 99.5 ksi
@Strain 3.64 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.13 GPa
@Strain 1.27 %,
Temperature 40.0 °C		 164 ksi
@Strain 1.27 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.81 GPa
@Strain 5.21 %,
Temperature -40.0 °C		 262 ksi
@Strain 5.21 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  1.95 GPa
@Strain 3.80 %,
Temperature -20.0 °C		 282 ksi
@Strain 3.80 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.08 GPa
@Strain 2.17 %,
Temperature 23.0 °C		 302 ksi
@Strain 2.17 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.2825 GPa
@Strain 2.40 %,
Temperature 0.000 °C		 331.05 ksi
@Strain 2.40 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.37 GPa
@Strain 0.700 %,
Temperature 23.0 °C		 344 ksi
@Strain 0.700 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.4175 GPa
@Strain 3.20 %,
Temperature -40.0 °C		 350.63 ksi
@Strain 3.20 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.5695 GPa
@Strain 2.00 %,
Temperature -20.0 °C		 372.68 ksi
@Strain 2.00 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.62 GPa
@Strain 1.04 %,
Temperature 0.000 °C		 379 ksi
@Strain 1.04 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.80 GPa
@Strain 0.820 %,
Temperature -20.0 °C		 406 ksi
@Strain 0.820 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.86 GPa
@Strain 1.69 %,
Temperature -40.0 °C		 415 ksi
@Strain 1.69 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  3.17 GPa
@Strain 0.430 %,
Temperature -40.0 °C		 460 ksi
@Strain 0.430 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Charpy Impact Unnotched  NB NB ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.550 J/cm² 2.62 ft-lb/in² ISO 179/1eA
  0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour  2500 MPa
@Time 3600 sec		 363000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours  1800 MPa
@Time 3.60e+6 sec		 261000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+12 ohm 1.00e+12 ohm IEC 60093
Dielectric Strength  26.0 kV/mm 660 kV/in IEC 60243-1
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  130 µm/m-°C 72.2 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  130 µm/m-°C 72.2 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  2.09 J/g-°C 0.500 BTU/lb-°F  
Thermal Conductivity  0.250 W/m-K 1.74 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  115 °C 239 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  50.0 °C 122 °F ISO 75-1/-2
Vicat Softening Point  175 °C 347 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.900 mm		 HB
@Thickness 0.0354 in		 IEC 60695-11-10
Flame Spread  21 mm/min
@Thickness 1.00 mm		 0.83 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
Oxygen Index  22 % 22 % ISO 4589-1/-2
 
Descriptive Properties
Delivery form Pellets  
Part Marking Code >PBT< ISO 11469
Processing Coatable  
  Injection Moulding  
  Other Extrusion  
  Profile Extrusion  
  Sheet Extrusion  
Regional Availability Europe  
  Near East/Africa  
UL recognition UL


图：





上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40825.html

免责声明: 本文 杜邦高性能聚合物6129 NC010/用于挤出和注塑成型 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4