LCP S135 材料说明：具有非常低的气体增强威达35%级玻璃，很高的热变形温度（335¦C）和刚度。典型的应用是lampsockets，lensholders为投影仪，电气和电子部件的连接器，继电器，开关，线圈和发动机罩下的应用。
LCP S135 加工方法：注塑成型
LCP S135 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.00700 % | 0.00700 % | 23°C/50%RH; ISO 62 |
| Water Absorption at Saturation | 0.00400 % | 0.00400 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00400 cm/cm | 0.00400 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 140 MPa | 20300 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.30 % | 1.30 % | 5mm/min; ISO 527-2/1A |
| 2.00 % | 2.00 % | flexural; ISO 178 | |
| Tensile Modulus | 15.5 GPa | 2250 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 230 MPa | 33400 psi | ISO 178 |
| Flexural Modulus | 14.5 GPa | 2100 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/1A |
| 14.0 kJ/m² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Dielectric Constant | 3.50 @Frequency 1.00e+6 Hz |
3.50 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.00900 @Frequency 1.00e+6 Hz |
0.00900 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 1.00 µm/m-°C | 0.556 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 23.0 µm/m-°C | 12.8 µin/in-°F | ISO 11359-2 |
| Melting Point | 350 °C | 662 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 340 °C | 644 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 267 °C | 513 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 | V-0 | |