  4. 杜邦6130 NC010/挤出和注塑成型。

杜邦6130 NC010/挤出和注塑成型。

杜邦高性能聚合物Crastin®6130 NC010聚对苯二甲酸丁二醇酯（PBT） 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT） 材料说明：无筋高粘度聚对苯二甲酸乙二醇酯用于挤出和注塑成型 03 6130 NC010是一种无筋中高粘度聚对苯二甲酸丁二醇酯树脂的挤出和注塑成型。
 物性表：

 
Physical Properties Metric English Comments
Density  1.11 g/cc 0.0401 lb/in³  
  1.30 g/cc 0.0470 lb/in³ ISO 1183
Water Absorption  0.40 %
@Thickness 2.00 mm		 0.40 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.200 %
@Thickness 2.00 mm		 0.200 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   68390 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 68390 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  79240 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 79240 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  91390 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 91390 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  130000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 130000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  169100 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 169100 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  222100 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 222100 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Viscosity Test  110 cm³/g 110 cm³/g ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.017 cm/cm 0.017 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.016 cm/cm 0.016 in/in ISO 294-4 2577
Melt Flow  48 g/10 min
@Load 2.16 kg,
Temperature 250 °C		 48 g/10 min
@Load 4.76 lb,
Temperature 482 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Stress   10.0 MPa
@Strain 0.380 %,
Time 3600 sec		 1450 psi
@Strain 0.380 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.550 %,
Time 36000 sec		 1450 psi
@Strain 0.550 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.770 %,
Time 360000 sec		 1450 psi
@Strain 0.770 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 1.10 %,
Time 3.60e+6 sec		 1450 psi
@Strain 1.10 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 1.45 %,
Time 3.60e+7 sec		 1450 psi
@Strain 1.45 %,
Time 10000 hour		 isochronous; ISO 11403-1 -2
Tensile Strength, Yield  59.0 MPa 8560 psi ISO 527-1/-2
Elongation at Break  30 % 30 % Nominal; ISO 527-1/-2
Elongation at Yield  6.0 % 6.0 % ISO 527-1/-2
Tensile Modulus  2.60 GPa 377 ksi ISO 527-1/-2
Flexural Strength  85.0 MPa 12300 psi ISO 178
Shear Modulus   0.110 GPa
@Temperature 150 °C		 16.0 ksi
@Temperature 302 °F		 Dynamic; ISO 11403-1 -2
  0.160 GPa
@Temperature 110 °C		 23.2 ksi
@Temperature 230 °F		 Dynamic; ISO 11403-1 -2
  0.340 GPa
@Temperature 60.0 °C		 49.3 ksi
@Temperature 140 °F		 Dynamic; ISO 11403-1 -2
  1.06 GPa
@Temperature 10.0 °C		 154 ksi
@Temperature 50.0 °F		 Dynamic; ISO 11403-1 -2
  1.12 GPa
@Temperature -20.0 °C		 162 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.20 GPa
@Temperature -50.0 °C		 174 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Izod Impact, Notched (ISO)  3.50 kJ/m² 1.67 ft-lb/in² ISO 180/1A
Charpy Impact Unnotched  NB NB ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm² 1.90 ft-lb/in² ISO 179/1eA
  0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour   909 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 132000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  975.61 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 141500 psi
@Pressure 725 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1170 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 170000 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1670 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 242000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2270 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 329000 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2630 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 382000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2810 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 407000 psi
@Pressure 725 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
Tensile Creep Modulus, 1000 hours   455 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 65900 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  606 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 87900 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  789 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 115000 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  909 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 132000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+12 ohm 1.00e+12 ohm IEC 60093
Dielectric Strength  26.0 kV/mm 660 kV/in IEC 60243-1
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  108 µm/m-°C 60.0 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  144 µm/m-°C 80.0 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  2.05 J/g-°C 0.490 BTU/lb-°F  
Thermal Conductivity  0.250 W/m-K 1.74 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  115 °C 239 °F ISO 75-1/-2
  180 °C 356 °F annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  50.0 °C 122 °F ISO 75-1/-2
  60.0 °C 140 °F annealed; ISO 75-1/-2
Vicat Softening Point  175 °C 347 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.900 mm		 HB
@Thickness 0.0354 in		 IEC 60695-11-10
Oxygen Index  22 % 22 % ISO 4589-1/-2
 
Descriptive Properties
Delivery form Pellets  
Part Marking Code >PBT< ISO 11469
Processing Casting  
  Coatable  
  Film Extrusion  
  Injection Moulding  
  Other Extrusion  
  Profile Extrusion  
  Sheet Extrusion  
Regional Availability Europe  
  Near East/Africa  
Resin Identification PBT  
UL recognition UL
图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40831.html

免责声明: 本文 杜邦6130 NC010/挤出和注塑成型。 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4