杜邦bm6450xd bk560/非常高的挤出和吹塑应用粘度

杜邦高性能聚合物Crastin®bm6450xd bk560聚对苯二甲酸丁二醇酯（PBT） 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT） 材料说明：吹塑发达增强聚对苯二甲酸丁二醇酯 Crastin bm6450xd bk560是一个无筋超韧聚对苯二甲酸丁二醇酯树脂具有非常高的挤出和吹塑应用粘度。
 物性表：

 
Physical Properties Metric English Comments
Density  1.03 g/cc 0.0372 lb/in³  
  1.21 g/cc 0.0437 lb/in³ ISO 1183
Viscosity   169000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 169000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  226000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 226000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  312000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 312000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  608000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 608000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  816000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 816000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  1.13e+6 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 1.13e+6 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.015 cm/cm 0.015 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.017 cm/cm 0.017 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Stress   0.590 MPa
@Strain 0.160 %,
Temperature 90.0 °C		 85.6 psi
@Strain 0.160 %,
Temperature 194 °F		 ISO 11403-1 -2
  1.20 MPa
@Strain 0.600 %,
Temperature 150 °C		 174 psi
@Strain 0.600 %,
Temperature 302 °F		 ISO 11403-1 -2
  1.69 MPa
@Strain 0.150 %,
Temperature 40.0 °C		 245 psi
@Strain 0.150 %,
Temperature 104 °F		 ISO 11403-1 -2
  3.29 MPa
@Strain 2.81 %,
Temperature 150 °C		 477 psi
@Strain 2.81 %,
Temperature 302 °F		 ISO 11403-1 -2
  4.02 MPa
@Strain 1.78 %,
Temperature 90.0 °C		 583 psi
@Strain 1.78 %,
Temperature 194 °F		 ISO 11403-1 -2
  4.24 MPa
@Strain 0.240 %,
Temperature 23.0 °C		 615 psi
@Strain 0.240 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  4.26 MPa
@Strain 0.190 %,
Temperature -20.0 °C		 618 psi
@Strain 0.190 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  4.72 MPa
@Strain 0.230 %,
Temperature 0.000 °C		 685 psi
@Strain 0.230 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  4.73 MPa
@Strain 5.10 %,
Temperature 150 °C		 686 psi
@Strain 5.10 %,
Temperature 302 °F		 ISO 11403-1 -2
  5.81 MPa
@Strain 7.64 %,
Temperature 150 °C		 843 psi
@Strain 7.64 %,
Temperature 302 °F		 ISO 11403-1 -2
  7.01 MPa
@Strain 3.88 %,
Temperature 90.0 °C		 1020 psi
@Strain 3.88 %,
Temperature 194 °F		 ISO 11403-1 -2
  8.09 MPa
@Strain 20.0 %,
Temperature 150 °C		 1170 psi
@Strain 20.0 %,
Temperature 302 °F		 ISO 11403-1 -2
  9.18 MPa
@Strain 6.32 %,
Temperature 90.0 °C		 1330 psi
@Strain 6.32 %,
Temperature 194 °F		 ISO 11403-1 -2
  10.02 MPa
@Strain 1.38 %,
Temperature 40.0 °C		 1453 psi
@Strain 1.38 %,
Temperature 104 °F		 ISO 11403-1 -2
  15.74 MPa
@Strain 3.66 %,
Temperature 40.0 °C		 2283 psi
@Strain 3.66 %,
Temperature 104 °F		 ISO 11403-1 -2
  17.25 MPa
@Strain 0.950 %,
Temperature 0.000 °C		 2502 psi
@Strain 0.950 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  19.01 MPa
@Strain 7.19 %,
Temperature 40.0 °C		 2757 psi
@Strain 7.19 %,
Temperature 104 °F		 ISO 11403-1 -2
  20.65 MPa
@Strain 1.38 %,
Temperature 23.0 °C		 2995 psi
@Strain 1.38 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  21.31 MPa
@Strain 1.13 %,
Temperature -20.0 °C		 3091 psi
@Strain 1.13 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  29.53 MPa
@Strain 3.85 %,
Temperature 23.0 °C		 4283 psi
@Strain 3.85 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  32.79 MPa
@Strain 2.14 %,
Temperature 0.000 °C		 4756 psi
@Strain 2.14 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  39.61 MPa
@Strain 4.14 %,
Temperature 0.000 °C		 5745 psi
@Strain 4.14 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  40.28 MPa
@Strain 2.57 %,
Temperature -20.0 °C		 5842 psi
@Strain 2.57 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  48.39 MPa
@Strain 4.80 %,
Temperature -20.0 °C		 7018 psi
@Strain 4.80 %,
Temperature -4.00 °F		 ISO 11403-1 -2
Tensile Strength, Yield  34.0 MPa 4930 psi ISO 527-1/-2
Elongation at Break  >= 50 % >= 50 % Nominal; ISO 527-1/-2
Elongation at Yield  9.0 % 9.0 % ISO 527-1/-2
Tensile Modulus  1.60 GPa 232 ksi ISO 527-1/-2
  0.115 GPa
@Temperature 150 °C		 16.7 ksi
@Temperature 302 °F		 ISO 11403-1 -2
  0.322 GPa
@Temperature 60.0 °C		 46.7 ksi
@Temperature 140 °F		 ISO 11403-1 -2
  1.983 GPa
@Temperature -20.0 °C		 287.6 ksi
@Temperature -4.00 °F		 ISO 11403-1 -2
Flexural Strength  50.0 MPa 7250 psi ISO 178
Flexural Modulus  1.60 GPa 232 ksi ISO 178
Shear Strength   0.09893 MPa
@Shear Rate 50.0 1/s,
Temperature 260 °C		 14.35 psi
@Shear Rate 50.0 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  0.13975 MPa
@Shear Rate 50.0 1/s,
Temperature 250 °C		 20.269 psi
@Shear Rate 50.0 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  0.2001 MPa
@Shear Rate 50.0 1/s,
Temperature 240 °C		 29.02 psi
@Shear Rate 50.0 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  0.3038 MPa
@Shear Rate 500 1/s,
Temperature 260 °C		 44.06 psi
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  0.4082 MPa
@Shear Rate 500 1/s,
Temperature 250 °C		 59.20 psi
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  0.5666 MPa
@Shear Rate 500 1/s,
Temperature 240 °C		 82.17 psi
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  0.84519 MPa
@Shear Rate 5000 1/s,
Temperature 260 °C		 122.58 psi
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  1.129 MPa
@Shear Rate 5000 1/s,
Temperature 250 °C		 163.7 psi
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  1.562 MPa
@Shear Rate 5000 1/s,
Temperature 240 °C		 226.5 psi
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Secant Modulus   0.187 GPa
@Strain 11.06 %,
Temperature 40.0 °C		 27.1 ksi
@Strain 11.06 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.373 GPa
@Strain 4.50 %,
Temperature 40.0 °C		 54.1 ksi
@Strain 4.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.726 GPa
@Strain 1.38 %,
Temperature 40.0 °C		 105 ksi
@Strain 1.38 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.13 GPa
@Strain 0.150 %,
Temperature 40.0 °C		 163 ksi
@Strain 0.150 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.36 GPa
@Strain 2.68 %,
Temperature 0.000 °C		 197 ksi
@Strain 2.68 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  1.38 GPa
@Strain 3.23 %,
Temperature -20.0 °C		 200 ksi
@Strain 3.23 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  1.50 GPa
@Strain 1.38 %,
Temperature 23.0 °C		 217 ksi
@Strain 1.38 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  1.77 GPa
@Strain 0.240 %,
Temperature 23.0 °C		 256 ksi
@Strain 0.240 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  1.82 GPa
@Strain 0.950 %,
Temperature 0.000 °C		 263 ksi
@Strain 0.950 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  1.89 GPa
@Strain 1.13 %,
Temperature -20.0 °C		 274 ksi
@Strain 1.13 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.05 GPa
@Strain 0.230 %,
Temperature 0.000 °C		 298 ksi
@Strain 0.230 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.24 GPa
@Strain 0.190 %,
Temperature -20.0 °C		 325 ksi
@Strain 0.190 %,
Temperature -4.00 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  90.0 kJ/m² 42.8 ft-lb/in² ISO 180/1A
Charpy Impact Unnotched  NB NB ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  12.0 J/cm² 57.1 ft-lb/in² ISO 179/1eA
  1.00 J/cm²
@Temperature -30.0 °C		 4.76 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  >= 1.00e+15 ohm >= 1.00e+15 ohm IEC 60093
Dielectric Strength  31.0 kV/mm 787 kV/in IEC 60243-1
Dissipation Factor   0.0070
@Frequency 100 Hz		 0.0070
@Frequency 100 Hz		 IEC 60250
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 IEC 60250
 
Thermal Properties Metric English Comments
Specific Heat Capacity  2.21 J/g-°C 0.528 BTU/lb-°F  
Thermal Conductivity  0.150 W/m-K 1.04 BTU-in/hr-ft²-°F of melt
Melting Point  220 °C 428 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  80.0 °C 176 °F ISO 75-1/-2
  130 °C 266 °F annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  50.0 °C 122 °F ISO 75-1/-2
Flame Spread  40 mm/min
@Thickness 1.00 mm		 1.6 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT-F< ISO 11469
Processing Blow Moulding  
  Casting  
  Coatable  
  Film Extrusion  
  Other Extrusion  
  Profile Extrusion  
  Sheet Extrusion  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT-F
图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40833.html

免责声明: 本文 杜邦bm6450xd bk560/非常高的挤出和吹塑应用粘度 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4