类别：聚合物；热塑性；液晶聚合物（LCP）；液晶聚合物（LCP），20%的玻璃纤维填充
LCP MT1305 材料说明：提供流量比mt1310容易。稍微强硬，但可经略多于部分mt1310。15%玻璃增强。
LCP MT1305 加工方法：注塑成型
LCP MT1305 的物性表：
LCP MT1305 材料说明：提供流量比mt1310容易。稍微强硬，但可经略多于部分mt1310。15%玻璃增强。
LCP MT1305 加工方法：注塑成型
LCP MT1305 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00400 cm/cm | 0.00400 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80.0 | 80.0 | ISO 2039-2 |
| Tensile Strength at Break | 200 MPa | 29000 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.10 % | 3.10 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 12.0 GPa | 1740 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| Flexural Modulus | 12.4 GPa | 1800 ksi | ISO 178 |
| Compressive Strength | 85.0 MPa @Strain 1.00 % |
12300 psi @Strain 1.00 % |
ISO 604 |
| Compressive Modulus | 10.0 GPa | 1450 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | ISO 180/1A |
| 61.0 kJ/m² @Temperature 23.0 °C |
29.0 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 4.80 J/cm² | 22.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 4.20 J/cm² | 20.0 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.00 @Frequency 1.00e+6 Hz |
3.00 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.50 @Frequency 100 Hz |
3.50 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0180 @Frequency 1.00e+6 Hz |
0.0180 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.0200 @Frequency 100 Hz |
0.0200 @Frequency 100 Hz |
IEC 60250 | |
| Arc Resistance | 135 sec | 135 sec | Internal |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 18.0 µm/m-°C | 10.0 µin/in-°F | ISO 11359-2 |
| Melting Point | 280 °C | 536 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 157 °C | 315 °F | ISO 75-1, -2 |
| Vicat Softening Point | 162 °C | 324 °F | ISO 306 |
| Flammability, UL94 | V-0 | V-0 | |