LCP MLX4243 材料说明：高耐热，矿物填充LCP材料具有高流动。金属材料在美学金属效应应用中具有银金属外观。
LCP MLX4243 加工方法：注塑成型
LCP MLX4243 的物性表：
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.50 % | 2.50 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 12.5 GPa | 1810 ksi | 50mm/min; ISO 527-2/1A | ||
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 | ||
| Flexural Modulus | 13.2 GPa | 1910 ksi | ISO 178 | ||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 332 °C | 630 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 - 130 °C | 176 - 266 °F | cavity | ||
| Zone 1 | 315 - 325 °C | 599 - 617 °F | |||
| Zone 2 | 325 - 335 °C | 617 - 635 °F | |||
| Zone 3 | 330 - 345 °C | 626 - 653 °F | |||
| Zone 4 | 335 - 350 °C | 635 - 662 °F | |||
| Die Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Melt Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Drying Temperature | >= 150 °C | >= 302 °F | |||
| Dry Time | 6.00 hour | 6.00 hour | |||
| Moisture Content | <= 0.0100 % | <= 0.0100 % | |||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| De |
|||||
| Injection speed | very fast | ||||