LCP 5145L 它有改进的韧性,50%的玻璃纤维填充

LCP 5145L 类别:聚合物;热塑性;液晶聚合物(LCP);液晶聚合物(LCP),50%的玻璃纤维填充 LCP 5145L 材料说明:泽尼特«5145l是45%玻璃纤维增强增韧液晶聚合物注射成型。它有改进的韧性。 联系人: 夏先生 手 机: 13501802636 QQ :205730283 邮 箱 :205730283@qq.com
LCP 5145L 类别:聚合物;热塑性;液晶聚合物(LCP);液晶聚合物(LCP),50%的玻璃纤维填充 
LCP 5145L 材料说明:
泽尼特«5145l是45%玻璃纤维增强增韧液晶聚合物注射成型。它有改进的韧性。 
LCP 5145L 加工方法:
注塑成型 
LCP 5145L 的物性表:
 
Physical Properties Metric English Comments
Density  1.75 g/cc 0.0632 lb/in³ ISO 1183
Density of Compound  1.48 g/cc 0.0535 lb/in³  
Linear Mold Shrinkage, Flow  0.000900 cm/cm 0.000900 in/in ISO 294-4
Linear Mold Shrinkage, Transverse  0.00500 cm/cm 0.00500 in/in ISO 294-4
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  115 MPa 16700 psi 5mm/min; ISO 527-2/1A
Elongation at Break  3.10 % 3.10 % 5mm/min; ISO 527-2/1A
Tensile Modulus  15.0 GPa 2180 ksi 50mm/min; ISO 527-2/1A
Flexural Strength  190 MPa 27600 psi ISO 178
Flexural Modulus  11.0 GPa 1600 ksi ISO 178
Compressive Strength  71.0 MPa 10300 psi ISO 604
  21.3 MPa
@Strain 1.00 %
3090 psi
@Strain 1.00 %
ISO 604
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+15 ohm-cm 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+15 ohm 1.00e+15 ohm IEC 60093
Dielectric Constant  3.90
@Frequency 1.00e+6 Hz
3.90
@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength  45.0 kV/mm 1140 kV/in IEC 60243-1
Dissipation Factor  0.0180
@Frequency 1.00e+6 Hz
0.0180
@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index  175 V 175 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  7.00 µm/m-°C 3.89 µin/in-°F ISO 11359-2
CTE, linear, Transverse to Flow  60.0 µm/m-°C 33.3 µin/in-°F ISO 11359-2
Specific Heat Capacity  1.50 J/g-°C 0.359 BTU/lb-°F  
Thermal Conductivity  0.350 W/m-K 2.43 BTU-in/hr-ft²-°F  
Melting Point  319 °C 606 °F 10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi)  290 °C 554 °F ISO 75-1, -2
Flammability, UL94   V-0
@Thickness 1.50 mm
V-0
@Thickness 0.0591 in
 
  V-0
@Thickness 0.800 mm
V-0
@Thickness 0.0315 in
 
Oxygen Index  33.0 % 33.0 %

如有需求欢迎各位来电咨询:
联系人: 夏先生  
手  机:13501802636  
QQ    :205730283  
邮 箱 :205730283@qq.com 

原料图:(兹图非实物图)
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40884.html

免责声明: 本文 LCP 5145L 它有改进的韧性,50%的玻璃纤维填充 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4