杜邦高性能聚合物S620F20 NC010/中粘度

杜邦高性能聚合物Crastin®S620F20 NC010聚对苯二甲酸丁二醇酯（PBT） 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT） 材料说明：无筋中粘度聚对苯二甲酸乙二醇酯 Crastin S620F20 NC010是一种无筋核润滑介质粘度聚对苯二甲酸乙二醇酯的快速注塑成型树脂。
 物性表：

 
Physical Properties Metric English Comments
Density  1.11 g/cc 0.0401 lb/in³  
  1.31 g/cc 0.0473 lb/in³ ISO 1183
Water Absorption  0.40 %
@Thickness 2.00 mm		 0.40 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.200 %
@Thickness 2.00 mm		 0.200 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   92000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 92000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  105000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 105000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  121000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 121000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  207000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 207000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  244000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 244000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  289000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 289000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Viscosity Test  130 cm³/g 130 cm³/g ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.017 cm/cm 0.017 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.016 cm/cm 0.016 in/in ISO 294-4 2577
Melt Flow  19.1 g/10 min
@Load 2.16 kg,
Temperature 250 °C		 19.1 g/10 min
@Load 4.76 lb,
Temperature 482 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Stress   8.62 MPa
@Strain 0.320 %,
Temperature 23.0 °C		 1250 psi
@Strain 0.320 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  10.61 MPa
@Strain 2.43 %,
Temperature 90.0 °C		 1539 psi
@Strain 2.43 %,
Temperature 194 °F		 ISO 11403-1 -2
  20.07 MPa
@Strain 1.69 %,
Temperature 40.0 °C		 2911 psi
@Strain 1.69 %,
Temperature 104 °F		 ISO 11403-1 -2
  22.69 MPa
@Strain 9.30 %,
Temperature 90.0 °C		 3291 psi
@Strain 9.30 %,
Temperature 194 °F		 ISO 11403-1 -2
  25.75 MPa
@Strain 15.89 %,
Temperature 90.0 °C		 3735 psi
@Strain 15.89 %,
Temperature 194 °F		 ISO 11403-1 -2
  26.61 MPa
@Strain 22.76 %,
Temperature 90.0 °C		 3859 psi
@Strain 22.76 %,
Temperature 194 °F		 ISO 11403-1 -2
  36.67 MPa
@Strain 6.70 %,
Temperature 40.0 °C		 5319 psi
@Strain 6.70 %,
Temperature 104 °F		 ISO 11403-1 -2
  39.4 MPa
@Strain 1.59 %,
Temperature 23.0 °C		 5710 psi
@Strain 1.59 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  41.23 MPa
@Strain 11.68 %,
Temperature 40.0 °C		 5980 psi
@Strain 11.68 %,
Temperature 104 °F		 ISO 11403-1 -2
  42.19 MPa
@Strain 16.69 %,
Temperature 40.0 °C		 6119 psi
@Strain 16.69 %,
Temperature 104 °F		 ISO 11403-1 -2
  53.5 MPa
@Strain 2.50 %,
Temperature 23.0 °C		 7760 psi
@Strain 2.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
Tensile Strength, Yield  59.0 MPa 8560 psi ISO 527-1/-2
Elongation at Break  30 % 30 % Nominal; ISO 527-1/-2
Elongation at Yield  8.0 % 8.0 % ISO 527-1/-2
Tensile Modulus  2.60 GPa 377 ksi ISO 527-1/-2
Flexural Strength  88.0 MPa 12800 psi ISO 178
Shear Modulus   0.0640 GPa
@Temperature 160 °C		 9.28 ksi
@Temperature 320 °F		 Dynamic; ISO 11403-1 -2
  0.0900 GPa
@Temperature 120 °C		 13.1 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.187 GPa
@Temperature 70.0 °C		 27.1 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  0.869 GPa
@Temperature 20.0 °C		 126 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  0.959 GPa
@Temperature -20.0 °C		 139 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.07 GPa
@Temperature -50.0 °C		 155 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   0.313 GPa
@Strain 13.35 %,
Temperature 40.0 °C		 45.4 ksi
@Strain 13.35 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.547 GPa
@Strain 6.70 %,
Temperature 40.0 °C		 79.4 ksi
@Strain 6.70 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.19 GPa
@Strain 1.69 %,
Temperature 40.0 °C		 172 ksi
@Strain 1.69 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.93 GPa
@Strain 2.86 %,
Temperature 23.0 °C		 279 ksi
@Strain 2.86 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.48 GPa
@Strain 1.59 %,
Temperature 23.0 °C		 359 ksi
@Strain 1.59 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.69 GPa
@Strain 0.320 %,
Temperature 23.0 °C		 391 ksi
@Strain 0.320 %,
Temperature 73.4 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  4.00 kJ/m² 1.90 ft-lb/in² ISO 180/1A
  5.00 kJ/m²
@Temperature -30.0 °C		 2.38 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  142 kJ/m² 67.6 ft-lb/in² ISO 180/1U
  70.0 kJ/m²
@Temperature -30.0 °C		 33.3 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1U
Charpy Impact Unnotched  NB NB ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.450 J/cm² 2.14 ft-lb/in² ISO 179/1eA
  0.350 J/cm²
@Temperature -30.0 °C		 1.67 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour  2600 MPa
@Time 3600 sec		 377000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours  1800 MPa
@Time 3.60e+6 sec		 261000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Dielectric Constant   3.2
@Frequency 1.00e+6 Hz		 3.2
@Frequency 1.00e+6 Hz		 IEC 60250
  3.8
@Frequency 100 Hz		 3.8
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  26.0 kV/mm 660 kV/in IEC 60243-1
Dissipation Factor   0.0020
@Frequency 100 Hz		 0.0020
@Frequency 100 Hz		 IEC 60250
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  130 µm/m-°C 72.2 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  130 µm/m-°C 72.2 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  2.10 J/g-°C 0.502 BTU/lb-°F  
Thermal Conductivity  0.210 W/m-K 1.46 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  145 °C 293 °F ISO 75-1/-2
  180 °C 356 °F annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  60.0 °C 140 °F ISO 75-1/-2
  60.0 °C 140 °F annealed; ISO 75-1/-2
Vicat Softening Point  175 °C 347 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Oxygen Index  22 % 22 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT  
UL recognition UL

图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40897.html

免责声明: 本文 杜邦高性能聚合物S620F20 NC010/中粘度 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4