特种LCP XYDAR®G-930，30%玻璃纤维

LCP G-930 类别：聚合物；热塑性；液晶聚合物（LCP）
LCP G-930 材料说明：®g-930 XYDAR液晶聚合物（LCP）是一种玻璃纤维增强注塑级专门为电气/电子应用表面贴装技术的应用。
LCP G-930 特点：阻燃剂；耐化学性好；成型性好；耐候性好；高刚度；高强度；低翘曲；耐辐射（γ）
LCP G-930 用途：汽车上的应用；汽车电子；纱管；电器；电气/电子应用；工业应用；工业零件 
LCP G-930 成型性：XYDAR®g-930可以填补墙壁非常薄在很少或没有闪光长的流动长度，即使在模具温度低于200°F（93°C）。此外，它在成型产品和特殊的焊缝强度低翘曲。
LCP G-930 的物性表：

Physical Properties	Metric	English	Comments
Density	1.60 g/cc	0.0578 lb/in³	ASTM D792
Filler Content	30 %	30 %	Glass Fiber
Water Absorption	<= 0.10 % @Time 86400 sec	<= 0.10 % @Time 24.0 hour	ISO 62
Mechanical Properties	Metric	English	Comments
Tensile Strength	135 MPa	19600 psi	ASTM D638
Elongation at Break	1.6 %	1.6 %	ASTM D638
Tensile Modulus	15.9 GPa	2310 ksi	ASTM D638
Flexural Strength	172 MPa	24900 psi	ASTM D790
Flexural Modulus	13.4 GPa	1940 ksi	ASTM D790
Izod Impact, Notched	0.960 J/cm	1.80 ft-lb/in	ASTM D256
Izod Impact, Unnotched	4.30 J/cm	8.06 ft-lb/in	ASTM D256
Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Dielectric Constant	3.9 @Frequency 1.00e+6 Hz	3.9 @Frequency 1.00e+6 Hz	ASTM D150
	4.2 @Frequency 60.0 Hz	4.2 @Frequency 60.0 Hz	ASTM D150
Dielectric Strength	39.0 kV/mm @Thickness 1.57 mm	991 kV/in @Thickness 0.0618 in	ASTM D149
Arc Resistance	>= 300 sec	>= 300 sec	ASTM D495
Comparative Tracking Index	185 V	185 V	ASTM D3638
Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	3.60 - 7.20 µm/m-°C	2.00 - 4.00 µin/in-°F
CTE, linear, Transverse to Flow	40.0 - 79.0 µm/m-°C	22.2 - 43.9 µin/in-°F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	271 °C	520 °F	Unannealed; ASTM D648
UL RTI, Electrical	220 °C @Thickness 0.750 mm	428 °F @Thickness 0.0295 in
UL RTI, Mechanical with Impact	200 °C @Thickness 0.750 mm	392 °F @Thickness 0.0295 in
UL RTI, Mechanical without Impact	220 °C @Thickness 0.750 mm	428 °F @Thickness 0.0295 in
Flammability, UL94	V-0 @Thickness 0.400 mm	V-0 @Thickness 0.0157 in
Processing Properties	Metric	English	Comments
Melt Temperature	321 - 360 °C	610 - 680 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	149 °C @Time 21600 - 28800 sec	300 °F @Time 6.00 - 8.00 hour