LCP 6330 材料说明：泽尼特«6330注塑30%的矿物增强液晶聚合物。它具有优异的耐冲击性、优异的热变形温度，适合各种要求的应用。
LCP 6330 加工方法：注塑成型
LCP 6330 参数详情：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.000 cm/cm | 0.000 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00650 cm/cm | 0.00650 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 5.00 % | 5.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 10.0 GPa | 1450 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | ISO 179/1eU |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.40 @Frequency 1.00e+6 Hz |
3.40 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.80 @Frequency 100 Hz |
3.80 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0140 @Frequency 100 Hz |
0.0140 @Frequency 100 Hz |
IEC 60250 |
| 0.0310 @Frequency 1.00e+6 Hz |
0.0310 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 8.00 µm/m-°C | 4.44 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-2 |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 275 °C | 527 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1, -2 |
| Glass Transition Temp, Tg | 120 °C | 248 °F | ISO 11357-1,-2,-3 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 @Thickness 0.850 mm |
V-0 @Thickness 0.0335 in |
||
| Oxygen Index | 47.0 % | 47.0 % | ISO 4589 |